Magnetic Tuning of All-Organic Binary Alloys between Two Stable Radicals

Mixtures of 2-(4,5,6,7-tetrafluorobenzimidazol-2-yl)-4,4,5,5-tetramethyl-4,5-dihydro-1H-imidazole-3-oxide-1-oxyl (F4BImNN) and 2-(benzi-midazol-2-yl)-4,4,5,5-tetramethyl-4,5-dihydro-1H-imidazole-3-oxide-1-oxyl (BImNN.) crystallize as solid solutions (alloys) across a wide range of binary compositions. (F4BImNN)(x)(BImNN)((1-x)) with x < 0.8 gives orthorhombic unit cells, while x >= 0.9 gives monoclinic unit cells. In all crystalline samples, the dominant intermolecular packing is controlled by one-dimensional (1D) hydrogen-bonded chains that lead to quasi-1D ferromagnetic behavior. Magnetic analysis over 0.4-300 K indicates ordering with strong 1D ferromagnetic exchange along the chains (J/k = 12-22 K). Interchain exchange is estimated to be 33- to 150-fold weaker, based on antiferromagnetic ordered phase formation below Neel temperatures in the 0.4-1.2 K range for the various compositions. The ordering temperatures of the orthorhombic samples increase linearly as (1 - x) increases from 0.25 to 1.00. The variation is attributed to increased interchain distance corresponding to decreased interchain exchange, when more F4BImNN is added into the orthorhombic lattice. The monoclinic samples are not part of the same trend, due to the different interchain arrangement associated with the phase change.

Complex mixed state of the Pauli-limited superconductor CeCoIn5

Magnetization measurements were performed on CeCoIn5 at temperatures down to 20 mK and magnetic fields up to 17 T applied along different crystallographic orientations. For field configurations nearly parallel to the ab plane (theta less than or similar to 40 degrees and T <= 50 mK), we have found an intriguing vortex dynamics regime revealed by a hysteretic and metastable anomalous peak effect (APE), which gives evidence of surface barrier effects enhanced by antiferromagnetic fluctuations in the mixed state of CeCoIn5. Furthermore, we have observed crossover features in the torque and magnetization traces at fields below H-c2, which are consistent with vortices lattice phase transitions and with the anomalies speculated to be the Fulde-Ferrel-Larkin-Ovchinnikov (FFLO) superconducting state in CeCoIn5. All of the above features were found to be dramatically perturbed in Ce0.98Gd0.02CoIn5.

Structural and magnetic characterization of colloidal CdMnS

This paper reports on the synthesis (chemical co-precipitation reaction) and characterization (X-ray diffraction, magnetization, and electron paramagnetic resonance) of nanosized Cd1-xMnxS particles with manganese concentration up to x = 0.73. Though the literature reports that nanosized (bulk) CdS can incorporate as much as 30% (50%) of manganese ion within its crystal structure we found manganese segregation at the nanoparticle surface at doping levels as low as 14%. We found that both XRD and magnetization data support the presence of the Mn3O4 phase (observed spin-glass transition around 43 K) at the high manganese doping levels whereas the EPR data strongly suggest preferential incorporation of manganese at the nanoparticle's surface, even at low manganese doping levels. Analyses of the experimental data strongly suggest the preparation of well-defined core/shell (Cd1-xMnxS/Mn3O4) structures at higher levels of manganese doping.

Magnetic susceptibility study of Ce3+ in PbCeA (A=Te, Se, S)

The magnetic susceptibility of Pb(1-x)Ce(x)A (A=S, Se and Te) crystals with Ce3+ concentrations 0.006 <= x <= 0.036 was investigated in the temperature range from 2 K to 300 K. The magnetic susceptibility data was found to be consistent with a E-2(5/2) lowest manifold for Ce3+ ions with a crystal-field splitting Delta=E(Gamma(8))-E(Gamma(7)) of about 340 K, 440 K and 540 K for Pb1-xCexTe, Pb1-xCexSe, and Pb1-xCexS, respectively. For all the three compounds the doublet Gamma(7) lies below the Gamma(8) quadruplet which confirms the substitution of Pb2+ by Ce3+ ions in the host crystals. The observed values for the crystal-field splitting are in good agreement with the calculated ones based on the point-charge model. Moreover, the effective Lande factors were determined by X-band (similar to 9.5 GHz), electron paramagnetic measurements (EPR) to be g=1.333, 1.364, and 1.402 for Ce ions in PbA, A = S. Se and Te, respectively. The small difference with the predicted Lande factor g of 10/7 for the Gamma(7) (J=5/2) ground state was attributed to crystal-field admixture. (C) 2012 Elsevier B.V. All rights reserved.