Influence of the Sol-Gel pH Process and Compact Film on the Efficiency of TiO2-Based Dye-Sensitized Solar Cells

The influence of pH during hydrolysis of titanium(IV) isopropoxide on the morphological and electronic properties of TiO2 nanoparticles prepared by the sol-gel method is investigated and correlated to the photoelectrochemical parameters of dye-sensitized solar cells (DSCs) based on TiO2 films. Nanoparticles prepared under acid pH exhibit smaller particle size and higher surface area, which result in higher dye loadings and better short-circuit current densities than DSCs based on alkaline TiO2-processed films. On the other hand, the product of charge collection and separation quantum yields in films with TiO2 obtained by alkaline hydrolysis is c. a. 27% higher than for the acid TiO2 films. The combination of acid and alkaline TiO2 nanoparticles as mesoporous layer in DSCs results in a synergic effect with overall efficiencies up to 6.3%, which is better than the results found for devices employing one of the nanoparticles separately. These distinct nanoparticles can be also combined by using the layer-by-layer technique (LbL) to prepare compact TiO2 films applied before the mesoporous layer. DSCs employing photoanodes with 30 TiO2 bilayers have shown efficiencies up to 12% higher than the nontreated photoanode ones. These results can be conveniently used to develop optimized synthetic procedures of TiO2 nanoparticles for several dye-sensitized solar cell applications.

Mechanical Measurements Of Two Exogenous Surfactants Using A Langmuir Film Balance:A Comparative Study

Rationale: The primary function of surfactant is to reduce the surface tension at air-liquid interface. In this study, the surface tension behavior of two commercial surfactants, poractant alfa (ChiesiFarmaceuticals,ltaly) and beractant (Abbott Laboratories,USA), were evaluated,using new parameters. Methods: We used a Langmuir film balance (Minitrough,KSV lnstruments,Finland) to measure of surface tension of both poractant alfa and beractant samples. For both samples,we prepared a solution of 1 mg/mdl dissolved in chloroform. The solution (1uL) was applied over a subphase of milli-Q water (175 ml) in the chamber of the balance. The chamber has two moving barriers that can change its surface area between a maximum value of 112.5 cm2 anda minimum value of 22.5 cm2, defining a balance cycle.lhree sample's films were evaluated for each sample, during 20 balance cycles. Here quantify two new variables, which is the mean hysteresis area of the measured curve surface tension of the last 16 balance cycles,defined here as Mean Work Cycle (MWC), and the moment that the surfactant is active in the surface, this measure is defined here as Active Surface Area Critical in the compression (ASACC) and the expansion (ASACE). The test was applied to compare the statistical significance of the results.