Magnetic and optical investigation of 40SiO(2)center dot 30Na(2)O center dot 1Al(2)O(3)center dot(29-x) B2O3 center dot xFe(2)O(3) glass matrix

Samples of 40SiO(2)center dot 30Na(2)O center dot 1Al(2)O(3)center dot(29 - x)B2O3 center dot xFe(2)O(3) (mol%), with 0.0 <= x <= 17.5, were prepared by the fusion method and investigated by electron paramagnetic resonance (EPR), optical absorption (OA) and Mossbauer spectroscopy (MS). The EPR spectra of the as-synthesized samples exhibit two well-defined EPR signals around g = 4.27 and g = 2.01 and a visible EPR shoulder around g = 6.4, assigned to isolated Fe3+ ion complexes (g = 4.27 and g = 6.4) and Fe3+-based clusters (g = 2.01). Analyses of both EPR line intensity and line width support the model picture of Fe3+-based clusters built in from two sources of isolated ions, namely Fe2+ and Fe3+; the ferrous ion being used to build in iron-based clusters at lower x-content (below about x = 2.5%) whereas the ferric ion is used to build in iron-based clusters at higher x-content (above about x = 2.5%). The presence of Fe2+ ions incorporated within the glass template is supported by OA data with a strong band around 1100 nm due to the spin-allowed E-5(g)-T-5(2g) transition in an octahedral coordination with oxygen. Additionally, Mossbauer data (isomer shift and quadrupole splitting) confirm incorporation of both Fe2+ and Fe3+ ions within the template, more likely in tetrahedral-like environments. We hypothesize that ferrous ions are incorporated within the glass template as FeO4 complex resulting from replacing silicon in non-bridging oxygen (SiO3O-) sites whereas ferric ions are incorporated as FeO4 complex resulting from replacing silicon in bridging-like oxygen silicate groups (SiO4). (C) 2012 Elsevier Masson SAS. All rights reserved.

Incorporation of PbF2 into Heavy Metal Oxide Borate Glasses. Structural Studies by Solid State NMR

A series of heavy metal oxide (HMO) glasses with composition 26.66B(2)O(3)-16GeO(2)-4 Bi2O3-(53.33-x)PbO-xPbF2 (0 <= x <= 40) were prepared and characterized with respect to their bulk (glass transition and crystallization temperatures, densities, molar volumes) and spectroscopic properties. Homogeneous glasses are formed up to x = 30, while crystallization of beta-PbF2 takes place at higher contents. Substitution of PbO by PbF2 shifts the optical band gap toward higher energies, thereby extending the UV transmission window significantly toward higher frequencies. Raman and infrared absorption spectra can be interpreted in conjunction with published reference data. Using B-11 and F-19 high-resolution solid state NMR as well as B-11/F-19 double resonance methodologies, we develop a quantitative structural description of this material. The fraction of four-coordinate boron is found to be moderately higher compared to that in glasses with the same PbO/B2O3 ratios, suggesting some participation of PbF2 in the network transformation process. This suggestion is confirmed by the F-19 NMR spectra. While the majority of the fluoride ions is present as ionic fluoride, similar to 20% of the fluorine inventory acts as a network modifier, resulting in the formation of four-coordinate BO3/2F- units. These units can be identified by F-19{B-11} rotational echo double resonance and B-11{F-19} cross-polarization magic angle spinning (CPMAS) data. These results provide the first unambiguous evidence of B-F bonding in a PbF2-modified glass system. The majority of the fluoride ions are found in a lead-dominated environment. F-19-F-19 homonuclear dipolar second moments measured by spin echo decay spectroscopy are quantitatively consistent with a model in which these ions are randomly distributed within the network modifier subdomain consisting of PbO, Bi2O3, and PbF2. This model, which implies both the features of atomic scale mixing with the network former borate species and some degree of fluoride ion clustering is consistent with all of the experimental data obtained on these glasses.

Structure and Ionic Conductivity in the Mixed-Network Former Chalcogenide Glass System [Na2S](2/3)[(B2S3)(x)(P2S5)(1-x)](1/3)

Glasses in the system [Na2S](2/3)[(B2S3)(x)(P2S5)(1-x)](1/3) (0.0 <= x <= 1.0) were prepared by the melt quenching technique, and their properties were characterized by thermal analysis and impedance spectroscopy. Their atomic-level structures were comprehensively characterized by Raman spectroscopy and B-11, P-31, and Na-23 high resolution solid state magic-angle spinning (MAS) NMR techniques. P-31 MAS NMR peak assignments were made by the presence or absence of homonuclear indirect P-31-P-31 spin-spin interactions as detected using homonuclear J-resolved and refocused INADEQUATE techniques. The extent of B-S-P connectivity in the glassy network was quantified by P-31{B-11} and B-11{P-31} rotational echo double resonance spectroscopy. The results clearly illustrate that the network modifier alkali sulfide, Na2S, is not proportionally shared between the two network former components, B and P. Rather, the thiophosphate (P) component tends to attract a larger concentration of network modifier species than predicted by the bulk composition, and this results in the conversion of P2S74-, pyrothiophosphate, Na/P = 2:1, units into PS43-, orthothiophosphate, Na/P = 3:1, groups. Charge balance is maintained by increasing the net degree of polymerization of the thioborate (B) units through the formation of covalent bridging sulfur (BS) units, B S B. Detailed inspection of the B-11 MAS NMR spectra reveals that multiple thioborate units are formed, ranging from neutral BS3/2 groups all the way to the fully depolymerized orthothioborate (BS33-) species. On the basis of these results, a comprehensive and quantitative structural model is developed for these glasses, on the basis of which the compositional trends in the glass transition temperatures (T-g) and ionic conductivities can be rationalized. Up to x = 0.4, the dominant process can be described in a simplified way by the net reaction equation P-1 + B-1 reversible arrow P-0 + B-4, where the superscripts denote the number of BS atoms for the respective network former species. Above x = 0.4, all of the thiophosphate units are of the P-0 type and both pyro-(B-1) and orthothioborate (B-0) species make increasing contributions to the network structure with increasing x. In sharp contrast to the situation in sodium borophosphate glasses, four-coordinated thioborate species are generally less abundant and heteroatomic B-S-P linkages appear to not exist. On the basis of this structural information, compositional trends in the ionic conductivities are discussed in relation to the nature of the charge-compensating anionic species and the spatial distribution of the charge carriers.