Comparative study on structure and magnetic properties of polycrystalline PrxY1-xBa2Cu3O7-delta prepared in oxygen and argon atmosphere

We report a systematic study on the influence of the synthesis routes on the structural and magnetic properties of polycrystalline PrxY1-xBa2Cu3O7-delta. We have prepared high-quality samples of this material by following a sol-gel method based on heat treatment in both inert argon and oxygen atmospheres in order to compare their effect on the formation of the superconducting phase using X-ray powder diffraction. Magnetic measurements (DC and AC susceptibility) clearly demonstrate that, for the same concentration of Pr, the superconducting transition temperature markedly increases in all samples prepared in argon atmosphere, including pure Pr-123. (C) 2012 Elsevier B.V. All rights reserved.

Argon and Nd:YAG Lasers for Caries Prevention in Enamel

Objective: The aim of this study was to investigate the effect of Nd:YAG and argon laser irradiations on enamel demineralization after two different models to induce artificial caries. Background data: It is believed that the use of the high-intensity laser on the dental structure can lead to a more acid-resistant surface. Materials and methods: Twenty-one extracted human third molars were sectioned into tooth quarters. The quarters were distributed in three groups: Group I (control), untreated; Group II, Nd:YAG laser (60 mJ, 15 pps, 47.77 J/cm(2), 30 sec); and Group III, argon laser (250mW, 12 J/cm(2), 48 sec). Tooth quarters from each group were subjected to two different demineralization models: cycle 1, a 14 day demineralization (pH 4.5; 6 h) and remineralization (pH 7.0; 18 h) solutions, 37 degrees C and cycle 2, 48 h in demineralization solution (pH 4.5). Samples were prepared in slices (60-100 mu m thick) to be evaluated under polarized light microscopy. Demineralization areas were measured (mm(2)) (n = 11). Data were analyzed by ANOVA and Tukey's test (p < 0.05). Results: Means followed by different letters are significantly different: 0.25 A (control, cycle 48 h); 0.18 AB (control, cycle 14 days); 0.17 AB (Nd:YAG, cycle 14 days); 0.14 BC (argon, cycle 48 h); 0.09 BC (Nd:YAG, cycle 48 h), and 0.06 C (argon, cycle 14 days). Conclusions: The argon laser was more effective for caries preventive treatment than Nd: YAG laser, showing a smaller demineralization area in enamel.

Distribution of major elements in Atlantic surface sediments (36 degrees N-49 degrees S): Imprint of terrigenous input and continental weathering

Numerous studies use major element concentrations measured on continental margin sediments to reconstruct terrestrial climate variations. The choice and interpretation of climate proxies however differ from site to site. Here we map the concentrations of major elements (Ca, Fe, Al, Si, Ti, K) in Atlantic surface sediments (36 degrees N-49 degrees S) to assess the factors influencing the geochemistry of Atlantic hemipelagic sediments and the potential of elemental ratios to reconstruct different terrestrial climate regimes. High concentrations of terrigenous elements and low Ca concentrations along the African and South American margins reflect the dominance of terrigenous input in these regions. Single element concentrations and elemental ratios including Ca (e. g., Fe/Ca) are too sensitive to dilution effects (enhanced biological productivity, carbonate dissolution) to allow reliable reconstructions of terrestrial climate. Other elemental ratios reflect the composition of terrigenous material and mirror the climatic conditions within the continental catchment areas. The Atlantic distribution of Ti/Al supports its use as a proxy for eolian versus fluvial input in regions of dust deposition that are not affected by the input of mafic rock material. The spatial distributions of Al/Si and Fe/K reflect the relative input of intensively weathered material from humid regions versus slightly weathered particles from drier areas. High biogenic opal input however influences the Al/Si ratio. Fe/K is sensitive to the input of mafic material and the topography of Andean river drainage basins. Both ratios are suitable to reconstruct African and South American climatic zones characterized by different intensities of chemical weathering in well-understood environmental settings.

Microhardness of a dental restorative composite resin containing nanoparticles polymerized with argon ion laser

The objective of this study was to compare the microhardness of two resin composites (microhybrid and nanoparticles). Light activation was performed with argon ion laser 1.56J (L) and halogen light 2.6J (H) was used as control. Measurements were taken on the irradiated surfaces and those opposite them, at thicknesses of 1, 2 and 3 mm. To evaluate the quality of polymerization, the percentages of maximum hardness were calculated (PMH). For statistical analysis the ANOVA and Tukey tests were used (p <= 0.05). To microhybrid was shown that the hardness with laser was inferior to the hardness achieved with halogen light, for both the 1 mm and 2 mm. The nanoparticles polymerized with laser, presented lower hardness even on the irradiated surface, than the same surface light activated with halogen light. The microhybrid attained a minimum PMH of 80% up to the thickness of 2 mm with halogen light, and with laser, only up to 1 mm. The nanoparticles attained a minimum PMH of 80% up to 3 mm thickness with halogen light and with laser this minimum was not obtained at any thickness. Based on these results, it could be concluded that light activation with argon ion laser is contra-indicated for the studied nanoparticles. Published by Elsevier GmbH.

Importância dos vírus respiratórios na febre sem sinais localizatórios em crianças menores de 36 meses

INTRODUÇÃO Cerca de 20% das crianças menores de 36 meses trazidas ao setor de emergência por febre apresentam febre sem sinais localizatórios (FSSL). Nos últimos anos, vários estudos estabeleceram critérios para a identificação dos pacientes com risco de infecção bacteriana grave (IBG), além de demonstrarem a aplicabilidade da pesquisa de vírus respiratórios (PVR) na avaliação destes pacientes. Entretanto, não existem estudos abordando a identificação de vírus respiratórios em crianças menores de 36 meses com FSSL no nosso meio. OBJETIVOS Descrever a frequência dos vírus respiratórios na febre sem sinais localizatórios (FSSL) em crianças menores de 36 meses de idade CASUÍSTICA E MÉTODOS Estudo prospectivo e observacional de crianças menores de 36 meses no setor de emergência pediátrico, durante o período de abril de 2011 a abril de 2013, com diagnóstico de FSSL. Foram excluídas crianças portadoras de doenças de base que implicavam em alteração da imunidade e uso de antibiótico até 14 dias antes da consulta. Os pacientes foram avaliados laboratorialmente de acordo com o protocolo institucional para avaliação de FSSL. Além de hemograma completo, análise do sedimento urinário e culturas de sangue e urina, foi coletada amostra de secreção de nasofaringe para pesquisa de vírus respiratórios por imunoflourescência indireta. Resultados Foram estudados 232 crianças menores de 36 meses com diagnóstico de FSSL, sendo 53% do sexo masculino, com idade mediana de 10,7 meses (5,4 - 16,1). Em 57 (24,6%) destes pacientes, foi identificado vírus respiratórios, sendo o adenovírus (33 casos - 57,9%) o agente mais identificado, seguido do parainfluenza 3 (17,5%) e do influenza A (12,3%). CONCLUSÃO Em torno de 25% dos casos de FSSL do nosso meio foram identificados vírus respiratórios, mostrando que a PVR é uma ferramenta útil na avaliação do paciente com FSSL, possibilitando a redução do número de retornos hospitalares e uso de antibioticoterapia empírica.