Boron site preference in ternary Ta and Nb boron suicides

X-ray single crystal (XSC) and neutron powder diffraction data (NPD) were used to elucidate boron site preference for five ternary phases. Ta3Si1-xBx (x=0.112(4)) crystallizes with the Ti3P-type (space group P4(2)/n) with B-atoms sharing the 8g site with Si atoms. Ta5Si3-x (x=0.03(1); Cr5B3- type) crystallizes with space group 14/mcm, exhibiting a small amount of vacancies on the 4 alpha site. Both, Ta-5(Si1-xBx)(3), X=0.568(3), and Nb-5(Si1-xBx)(3), x=0.59(2), are part of solid solutions of M5Si3 with Cr5B3-type into the ternary M-Si-B systems (M=Nb or Ta) with B replacing Si on the 8h site. The D8(8)-phase in the Nb-Si-B system crystallizes with the Ti5Ga4-type revealing the formula Nb5Si3B1-x (x=0.292(3)) with B partially filling the voids in the 2b site of the Mn5Si3 parent type. (C) 2012 Elsevier Inc. All rights reserved.

On Ti-18Si-6B and Ti-7.5Si-22.5B powder alloys prepared by high-energy ball milling and sintering

Recently, a new ternary phase was discovered in the Ti-Si-B system, located near the Ti6Si2B composition. The present study concerns the preparation of titanium alloys that contain such phase mixed with α-titanium and other intermetallic phases. High-purity powders were initially processed in a planetary ball-mill under argon atmosphere with Ti-18Si-6B and Ti-7.5Si-22.5B at. (%) initial compositions. Variation of parameters such as rotary speed, time, and ball diameters were adopted. The as-milled powders were pressureless sintered and hot pressed. Both the as-milled and sintered materials were characterized by X-ray diffraction, scanning electron microscopy and energy-dispersive spectrometry. Sintered samples have presented equilibrium structures formed mainly by the α-Ti+Ti6Si2B+Ti5Si3+TiB phases. Silicon and boron peaks disappear throughout the milling processes, as observed in the powder diffraction data. Furthermore, an iron contamination of up to 10 at. (%) is measured by X-ray spectroscopy analysis on some regions of the sintered samples. Density, hardness and tribological results for these two compositions are also presented here.