Eroded dentin does not jeopardize the bond strength of adhesive restorative materials

This in vitro study evaluated the bond strength of adhesive restorative materials to sound and eroded dentin. Thirty-six bovine incisors were embedded in acrylic resin and ground to obtain flat buccal dentin surfaces. Specimens were randomly allocated in 2 groups: sound dentin (immersion in artificial saliva) and eroded dentin (pH cycling model - 3x / cola drink for 7 days). Specimens were then reassigned according to restorative material: glass ionomer cement (Ketac (TM) Molar Easy Mix), resin-modified glass ionomer cement (Vitremer (TM)) or adhesive system with resin composite (Adper Single Bond 2 + Filtek Z250). Polyethylene tubes with an internal diameter of 0.76 mm were placed over the dentin and filled with the material. The microshear bond test was performed after 24 h of water storage at 37 degrees C. The failure mode was evaluated using a stereomicroscope (400x). Bond strength data were analyzed with two-way ANOVA and Tukey's post hoc tests (alpha = 0.05). Eroded dentin showed bond strength values similar to those for sound dentin for all materials. The adhesive system showed the highest bond strength values, regardless of the substrate (p < 0.0001). For all groups, the adhesive/mixed failure prevailed. In conclusion, adhesive materials may be used in eroded dentin without jeopardizing the bonding quality. It is preferable to use an etch-and-rinse adhesive system because it shows the highest bond strength values compared with the glass ionomer cements tested.

Particulate composite based on coconut fiber and castor oil polyurethane adhesive: An eco-efficient product

This paper presents a study on the potential use of coconut fiber as material to produce particleboards, with two different densities (0.8 g/cm(3) and 1.0 g/cm3), using castor oil-based polyurethane adhesive and urea-formaldehyde. The quality of the product that can be produced by industry was evaluated according to the normative NBR 14.810:2006, where density, thickness swell (TS), absorption, modulus of elasticity (MOE), modulus of rupture (MOR) in static bending and internal bond (IB) were determined. From the results, there was a decrease in TS and increase in MOR of coconut fiber panels with polyurethane resin panels compared with coconut fiber and resin urea-formaldehyde. Scanning microscopy electronic images (SEM) indicated that castor oil-based polyurethane adhesive occupies the gaps between the particles, a factor that contributes to improved physical and mechanical properties of the panels. The assessment of durability through accelerated aging tests shows that panels protected with waterproofing material can be used in environments that have contact with moisture. (C) 2012 Elsevier B.V. All rights reserved.

Effect of surface area and air-drying distance on shear bond strength of etch-and-rinse adhesive

We evaluated the effects of air-drying distance and bond surface area on the shear bond strength of a 2-step etch-and-rinse adhesive. A total of 120 bovine anterior teeth were equally divided into 6 main groups based on bonding surface area. The main groups were divided into sub-groups (n = 5) according to air-drying distance. The shear strength was determined using a universal testing machine at a crosshead speed of 0.5 mm/min. The averaged results were subjected to two-way ANOVA and Tukey's test (alpha = 0.05). Two-way ANOVA testing identified no significant cross-product interactions (p > 0.05), but the main factors of area (p < 0.0001) and air-drying distance (p < 0.00001) significantly affected the mean bond strength. Shorter air-drying distances improved bond strength, and increased surface area decreased the bond strength.

In vitro enterococcus faecalis biofilm formation on five adhesive systems

Objective: To determine the E. faecalis biofilm formation on the surface of five adhesive systems (AS) and its relationship with roughness. Study Design: The formation of E. faecalis biofilms was tested on the surface of four dual-cure AS: AdheSE DC, Clearfil DC Bond, Futurabond DC and Excite DSC and one light-cure antimicrobial AS, Clearfil Protect Bond, after 24 hours of incubation, using the MBEC high-throughput device. Results: E. faecalis biofilms grew on all the adhesives. The least growth of biofilm was on Excite DSC, Clearfil Protect Bond, and the control. Futurabond DC resulted in the greatest roughness and biofilm amount. There was a close relationship between the quantity of biofilm and roughness, except for Clearfil Protect Bond, which showed little biofilm but high roughness. Conclusion: None of the tested AS prevented E. faecalis biofilm formation, although the least quantity was found on the surface of Clearfil Protect Bond.

Qualitative SEM/EDS analysis of microleakage and apical gap formation of adhesive root-filling materials

Objective: The aim of this study was to compare the correspondence between gap formation and apical microleakage in root canals filled with epoxy resin-based (AH Plus) combined or not with resinous primer or with a dimethacrylate-based root canal sealer (Epiphany). Material and Methods: Thirty-nine lower single-rooted human premolars were filled by the lateral condensation technique (LC) and immersed in a 50-wt% aqueous silver nitrate solution at 37 degrees C (24 h). After longitudinal sectioning, epoxy resin replicas were made from the tooth specimens. Both the replicas and the specimens were prepared for scanning electron microscopy (SEM). The gaps were observed in the replicas. Apical microleakage was detected in the specimens by SEM/energy dispersive spectroscopy (SEM/EDS). The data were analyzed statistically using an Ordinal Logistic Regression model and Analysis of Correspondence (alpha=0.05). Results: Epiphany presented more regions containing gaps between dentin and sealer (p<0.05). There was correspondence between the presence of gaps and microleakage (p<0.05). Microleakage was similar among the root-filling materials (p>0.05). Conclusions: The resinous primer did not improve the sealing ability of AH Plus sealer and the presence of gaps had an effect on apical microleakage for all materials.

Complete denture wear during sleep in elderly sleep apnea patients-a preliminary study

There is no consensus in the literature about the impact of complete denture wear on obstructive sleep apnea (OSA). The goal of this randomized clinical study was to assess if complete denture wear during sleep interferes with the quality of sleep. Elderly edentulous OSA patients from a complete denture clinic were enrolled and received new complete dentures. An objective sleep analysis was determined with polysomnography performed at the sleep laboratory for all patients who slept either with or without their dentures. Twenty-three patients (74% females) completed the study with a mean age of 69.6 years and a mean body mass index of 26.7 kg/m(2). The apnea and hypopnea index (AHI) was significantly higher when patients slept with dentures compared to without (25.9 +/- 14.8/h vs. 19.9 +/- 10.2/h; p > 0.005). In the mild OSA group, the AHI was significantly higher when patients slept with the dentures (16.6 +/- 6.9 vs. 8.9 +/- 2.4; p < 0.05), while in moderate to severe OSA patients, the AHI was not significantly different when sleeping with dentures (.30.8 +/- 15.6 vs. 25.7 +/- 7.5; p = 0.2). The supine AHI in mild patients was related to a higher increase in AHI while wearing dentures (12.7 +/- 8.4/h vs. 51.9 +/- 28.6/h; p < 0.001). A limitation of the study is that the mild OSA patients had a higher BMI when compared to the moderate to severe OSA patients. Ten out of 14 patients who preferred to sleep with their upper and lower dentures showed an increase in their AHI while wearing dentures to sleep. Contrary to previous studies, we found that OSA patients may experience more apneic events if they sleep with their dentures in place. Specifically, in mild OSAS patients, the use of dentures substantially increases the AHI especially when in the supine position.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS). Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM). Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM. Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Migrant labor and wear-out in manual sugarcane harvesting in Sao Paulo, Brazil

The scope of this paper is to describe the work of manual sugarcane harvesters, assessing the nutritional behavior and body composition between the beginning and the end of the harvest. A descriptive longitudinal study was made of harvesters in Piracicaba, Sao Paulo, Brazil, who answered a socio-demographic questionnaire and authorized measurement of Body Mass Index, Body Fat Percentage and Arm Muscle Circumference at three stages. Creatine kinase on the skeletal isoform, C-reactive protein and plasma urea were measured at the end of the harvest. Thirty male migrant harvesters with ages ranging from 18 to 44 from the Northeast (Ceara) were assessed over a nine-month period. The workers suffered significant body fat and weight loss in the first half of the harvest. Eighteen workers had abnormal levels of creatine kinase and four - out of 24 who had donated blood - had altered urea levels. Sugarcane harvesting work causes weight and body fat loss and gains in the lean body mass index, which suffers wear-out when working on consecutive harvests. It can also cause changes in biochemical markers of chronic systemic inflammation. Further studies will make it possible to comprehend the relationships between stress, wear-out, labor longevity and health in sugarcane harvesting.

Impact of filler size and distribution on roughness and wear of composite resin after simulated toothbrushing

Objectives: Nanofilled composite resins are claimed to provide superior mechanical properties compared with microhybrid resins. Thus, the aim of this study was to compare nanofilled with microhybrid composite resins. The null hypothesis was that the size and the distribution of fillers do not influence the mechanical properties of surface roughness and wear after simulated toothbrushing test. Material and methods: Ten rectangular specimens (15 mm x 5 mm x 4 mm) of Filtek Z250 (FZ2), Admira (A), TPH3 (T), Esthet-X (EX), Estelite Sigma (ES), Concept Advanced (C), Grandio (G) and Filtek Z350 (F) were prepared according to manufacturer's instructions. Half of each top surface was protected with nail polish as control surface (not brushed) while the other half was assessed with five random readings using a roughness tester (Ra). Following, the specimens were abraded by simulated toothbrushing with soft toothbrushes and slurry comprised of 2: 1 water and dentifrice (w/w). 100,000 strokes were performed and the brushed surfaces were re-analyzed. Nail polish layers were removed from the specimens so that the roughness (Ra) and the wear could be assessed with three random readings (mu m). Data were analyzed by ANOVA and Tukey's multiple-comparison test (alpha = 0.05). Results: Overall outcomes indicated that composite resins showed a significant increase in roughness after simulated toothbrushing, except for Grandio, which presented a smoother surface. Generally, wear of nanofilled resins was significantly lower compared with microhybrid resins. Conclusions: As restorative materials suffer alterations under mechanical challenges, such as toothbrushing, the use of nanofilled materials seem to be more resistant than microhybrid composite resins, being less prone to be rougher and worn.

Wear and corrosion resistance of pack chromised carbon steel

Pack chromising treatment is an environmentally friendly alternative to hard chromium to form wear and corrosion resistant surface layers. In this work, samples of AISI 1060 steel were pack chromised for 6 and 9 h at 1000 and 1050 degrees C using different activator concentrations. Wear tests were performed in dry conditions and corrosion tests in natural sea water for the pack chromised samples and hard chromium. Pack chromising yielded the formation of layers with high chromium concentrations, high hardness and wear resistance. Increasing activator concentration causes no significant change on the morphology and thickness of the layers. The layers produced at 1050 degrees C yielded only a (Cr,Fe)(2)N1-x phase, and those obtained at 1000 degrees C are composed of a carbide mixture with (Cr,Fe)(2)N1-x. The sample treated at 1050 degrees C for 9 h resulted in an optimum condition by means of better wear resistance and corrosion properties, which were close to that exhibited by the hard chrome, indicating that pack chromising is a promising alternative.

WEAR OF MATRIX OVERDENTURE ATTACHMENTS AFTER ONE TO EIGHT YEARS OF CLINICAL USE

Statement of problem. Matrices of unsplinted attachment systems are generally reported to be the weak component of implant overdentures, often requiring frequent maintenance. Clinical wear results in reduced retention of the prosthesis, requiring activation or renewal of the matrix to restore the initial level of retention. Purpose. The purpose of this retrospective study was to measure the wear of the matrix of a ball attachment after various periods of clinical wear. Material and methods. Seventy specimens of 3 groups of matrices of ball attachments that had been in use for mean periods of 12.3 months (1Y group, n=26), 39.0 months (3Y group, n=28) and 95.6 months (8Y group, n=16) were retrieved from 35 patients (2 specimens per patient) and measured on a coordinate measuring machine equipped with a touch trigger probe. Ten unused matrices were used as controls (CTRL group). The external and internal matrix diameters and deviations from circularity were measured. For the various time periods, the decreases in matrix thickness were calculated and compared with controls. Kruskal-Wallis 1-way ANOVA by ranks, followed by the Mann-Whitney post hoc tests, were conducted to test for differences in median values among groups (alpha=.05). Results. For the internal upper diameter of the matrices tested, the Kruskal-Wallis and Mann-Whitney tests revealed significant differences for the 3 groups compared to the controls. For group 1Y, a significant difference (P<.001) of the internal upper diameter was found compared to the CTRL group. Compared to the controls, the nonparametric analyses for groups 3Y and 8Y showed significant differences for the internal upper diameter (P<.001) and deviations from circularity (P<.001). For groups 1Y, 3Y and 8Y, matrix thickness losses were 07, 47 and 70 pm, respectively. Conclusions. Within the limitations of this study, it was observed that one year of clinical wear had limited effect on the ball attachment matrices. Three to 8 years of clinical use resulted in a significant decrease of matrix thickness, especially at the tip of the retentive lamellae. (J Prosthet Dent 2012;107:191-198)

Degradation of resin-dentin bonds of etch-and-rinse adhesive system to primary and permanent teeth

The aim of this in vitro study was to compare the degradation of resin-dentin bonds of an etch-and-rinse adhesive system to primary and permanent teeth. Flat superficial coronal dentin surfaces from 5 primary second molars and 5 permanent third molars were etched with phosphoric acid and bonded with an adhesive system (Adper Single Bond 2, 3M ESPE). Blocks of resin composite (Z250, 3M ESPE) were built up and the teeth sectioned to produce bonded sticks with a 0.8 mm(2) cross-sectional area. The sticks of each tooth were randomly divided and assigned to be subjected to microtensile testing immediately (24 h) or after aging by water storage (6 months). Data were analyzed by two-way repeated measures ANOVA and Tukey post hoc test (alpha = 0.05). Failure mode was evaluated using a stereomicroscope (400x). Microtensile values significantly decreased after the 6 months aging, independent of the dentin substrate. In 24 h, the values obtained to primary dentin were lower compared with permanent dentin. This difference was not maintained after aging. Adhesive/mixed failure was predominant in all experimental groups. In conclusion, degradation of resin-dentin bonds of the etch-and-rinse adhesive system occurred after 6 months of water storage; however, the reduction in bond strength values was higher for permanent teeth.

A SIMPLIFIED MODEL FOR EVALUATING TIRE WEAR DURING CONCEPTUAL DESIGN

In the field of vehicle dynamics, commercial software can aid the designer during the conceptual and detailed design phases. Simulations using these tools can quickly provide specific design metrics, such as yaw and lateral velocity, for standard maneuvers. However, it remains challenging to correlate these metrics with empirical quantities that depend on many external parameters and design specifications. This scenario is the case with tire wear, which depends on the frictional work developed by the tire-road contact. In this study, an approach is proposed to estimate the tire-road friction during steady-state longitudinal and cornering maneuvers. Using this approach, a qualitative formula for tire wear evaluation is developed, and conceptual design analyses of cornering maneuvers are performed using simplified vehicle models. The influence of some design parameters such as cornering stiffness, the distance between the axles, and the steer angle ratio between the steering axles for vehicles with two steering axles is evaluated. The proposed methodology allows the designer to predict tire wear using simplified vehicle models during the conceptual design phase.

Mass loss and wear mechanisms of HVOF-sprayed multi-component white cast iron coatings

In this work, multi-component white cast iron was applied by HVOF thermal spray process as alternative to other manufacture processes. Effects of substrate type, substrate pre-heating and heat treatment of coating on mass loss have been determined by rubber wheel apparatus in accordance with ASTM G-65. Furthermore, influence of heat treatment of coating on wear mechanisms was also determined by scanning electron microscopy analysis. Heat-treated coatings presented mass loss three times lower than as-sprayed coatings. Furthermore, wear mechanisms of as-sprayed coating are micro-cutting associated with cracks close to unmelted particles and pores. In heat-treated coating, lesser mass loss is due to sintering. (C) 2011 Elsevier B.V. All rights reserved.

Minimal alterations on the enamel surface by micro-abrasion: in vitro roughness and wear assessments

Objective: To evaluate the in vitro changes on the enamel surface after a micro-abrasion treatment promoted by different products. Material and Methods: Fifty (50) fragments of bovine enamel (15 mm × 5 mm) were randomly assigned to five groups (n=10) according to the product utilized: G1 (control)= silicone polisher (TDV), G2= 37% phosphoric acid (3M/ESPE) + pumice stone (SS White), G3= Micropol (DMC Equipment), G4= Opalustre (Ultradent) and G5= Whiteness RM (FGM Dental Products). Roughness and wear were the responsible variables used to analyze these surfaces in four stages: baseline, 60 s and 120 s after the micro-abrasion and after polishing, using a Hommel Tester T1000 device. After the tests, a normal distribution of data was verified, with repeated ANOVA analyses (p?0.05) which were used to compare each product in different stages. One-way ANOVA and Tukey tests were applied for individual comparisons between the products in each stage (p?0.05). Results: Means and standard deviations of roughness and wear (µm) after all the promoted stages were: G1=7.26(1.81)/13.16(2.67), G2=2.02(0.62)/37.44(3.33), G3=1.81(0.91)/34.93(6.92), G4=1.92(0.29)/38.42(0.65) and G5=1.98(0.53)/33.45(2.66). At 60 seconds, all products tended to produce less surface roughness with a variable gradual decrease over time. After polishing, there were no statistically significant differences between the groups, except for G1. Independent of the product utilized, the enamel wear occurred after the micro-abrasion. Conclusions: In this in vitro study, enamel micro-abrasion presented itself as a conservative approach, regardless of the type of the paste compound utilized. These products promoted minor roughness alterations and minimal wear. The use of phosphoric acid and pumice stone showed similar results to commercial products for the micro-abrasion with regard to the surface roughness and wear.