Low liquid-solid ratio (LSR) hot water pretreatment of sugarcane bagasse

Low liquid-solid ratio (LSR) can be used to obtain high-content xylo-oligosaccharide (XOS) spend liquor by hot water pretreatment. Developing a technology based on low LSR results in more efficient water usage in the system and thus in lower capital and operating costs. Xylans from xylan rich agro-industrial waste are abundant hemicellulosic polymers with enormous potential for industrial applications. Currently, freeze-dried xylo-oligosaccharides are used as bio-based polymers and hydrolysates containing high xylose contents are converted to several chemical products. In this study, sugarcane bagasse was treated with water at low LSRs and mild temperatures in order to assess the effects of varying the pretreatment conditions on the xylo-oligosaccharide and xylose concentrations, and use a central composite experimental design to optimize the process parameters. The pretreatments were performed in the ranges temperature: 143.3-176.7 degrees C, time: 20-70 min and LSR: 1 : 1 to 11 : 1 (g g(-1)). The maximum concentrations of xylose and xylan were 13.76 and 36.18 g L-1 (equivalent to 48.29 g L-1 of xylan), respectively, which were achieved by treating bagasse at 170 degrees C for 60 min, with LSR of 3 g g(-1). The amount of xylan removed under these conditions was almost 57%. The soluble xylan consisted mainly of xylo-oligosaccharides (74 wt% of the identified compound in the spent liquor).

Effect of partial preferential orientation and distortions in octahedral clusters on the photoluminescence properties of FeWO4 nanocrystals

This communication is a report of our initial research to obtain iron tungstate (FeWO4) nanocrystals by the microwave-hydrothermal method at 170 degrees C for 45 min. X-ray diffraction patterns showed that the FeWO4 nanocrystals prepared with polyethylene glycol-200 have a partial preferential orientation in the (011) plane in relation to other nanocrystals prepared with sodium bis(2-ethylhexyl) sulfosuccinate and water. Rietveld refinement data indicates that all nanocrystals are monophasic with wolframite-type monoclinic structures and exhibit different distortions on octahedral [FeO6]/[WO6] clusters. High resolution transmission electron microcopy revealed an oriented attachment mechanism for the growth of aggregated FeWO4 nanocrystals. Finally, we observed that the photoluminescence properties of these nanocrystals are affected by partial preferential orientation in the (011) plane and distortions on [FeO6]/[WO6] clusters.