Time-dependent effects of chitosan on dentin structures

Complete debridement with smear layer removal are essential measures for achieving a successful outcome of root canal treatment. The aim of this study was to evaluate the effects of chitosan at different concentrations on the removal of the smear layer and on dentin structure after 3 and 5 min of application. Twelve recently extracted maxillary canine teeth were instrumented using the crown-down technique and irrigated with 1% sodium hypochlorite. The specimens were distributed according to the time and concentration of the final irrigating solution: G1: 0.1% chitosan for 3 min; G2: 0.2% chitosan for 3 min; G3: 0.37% chitosan for 3 min; G4: 0.1% chitosan for 5 min; G5: 0.2% chitosan for 5 min; G6: 0.37% chitosan for 5 min. All samples were prepared for SEM analysis. G1 exhibited removal of the smear layer, but not the smear plugs. G2 showed visible and open tubules with slight erosion of the peritubular dentin. Cleaning in G3 was similar to that in G2, however, the erosive effect was greater. There was expansion of the diameter of the tubules in G4; and in G5 and G6, there was severe erosion with deterioration of dentin surface. In conclusion, 0.2% chitosan for 3 min appeared to be efficient for removing the smear layer, causing little erosion of dentin.

Chlorhexidine does not increase immediate bond strength of etch-and-rinse adhesive to caries-affected dentin of primary and permanent teeth

The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on immediate bond strength of etch-and-rinse adhesive to sound (SD) and caries-affected (CAD) primary dentin compared with permanent dentin. Flat dentin surfaces from 20 primary molars (Pri) and 20 permanent molars (Perm) were assigned to 8 experimental groups (n=5) according to tooth type (Pri or Perm), dentin condition (SD or CAD - pH-cycling for 14 days) and treatment (control - C or 60 s application of 2% CHX solution after acid etching - CHX). The bonding system (Adper Single Bond 2) was applied according to manufacturer's instructions followed by resin composite application (Filtek Z250). After 24 h water storage, specimens with cross-section area of 0.8 mm² were prepared for being tested under microtensile test (1 mm/min). Data were submitted to ANOVA and Tukey's post hoc test (α=0.05). Failure mode was evaluated using a stereomicroscope at ×400. Treatment with CHX did not result in higher bond strength values than no pre-treatment (C groups), independently of tooth type. Primary teeth and caries-affected dentin showed significantly lower (p<0.05) bond strength means compared with permanent teeth and sound dentin, respectively. Predominance of adhesive/mixed failure was observed for all groups. CHX did not influence the immediate bond strength to sound or caries-affected dentin of primary and permanent teeth.

Effect of sodium hypochlorite and edta irrigation, individually and in alternation, on dentin microhardness at the furcation area of mandibular molars

The aim of this study was to evaluate the effect of irrigation regimens on dentin microhardness at the furcation area of mandibular molars, using sodium hypochlorite and ethylenediaminetetraacetic acid (EDTA), individually and in alternation. The occlusal surface and the roots of 20 non-carious extracted human permanent mandibular molars were cut transversally and discarded. The tooth blocks were embedded in acrylic resin and randomly assigned to 4 groups (n=5) according to the irrigating regimens: 1% NaOCl solution, 17% EDTA solution, 1% NaOCl and 17% EDTA and distilled water (control). Knoop microhardness of dentin at the furcation area was evaluated. Data were analyzed using one-way ANOVA and Tukey's multiple comparison tests (α=0.05). The results of this study indicated that all irrigation solutions, except for distilled water (control), decreased dentin microhardness. EDTA did not show a significant difference with NaOCl/EDTA (p>0.05), but showed a significant difference with NaOCl (p<0.01). EDTA and NaOCl/EDTA showed a maximum decrease in microhardness. The 17% EDTA solution, either alone or in combination with 1% NaOCl reduced significantly dentin microhardness at the furcation area of mandibular molars.

Dental pulp vascular permeability changes induced by dental bleaching

Aiming to compare the effect of different light sources for dental bleaching on vascular permeability of dental pulps, forty-eight incisors were used. The bleaching agent (35 % hydrogen peroxide) was activated by halogen light; LED (Light Emitting Diode) or LED, followed by laser phototherapy (LPT) (λ = 780 nm; 3 J/cm²). After the bleaching procedures, the animals received an intra-arterial dye injection and one hour later were sacrificed. The teeth were diaphanized and photographed. The amount of blue stain content of each dental pulp was quantified using a computer imaging program. The data was statistically compared (p < 0.05). The results showed a significant higher (p < 0.01) dye content in the groups bleached with halogen light, compared with the control, LED and LED plus LPT groups. Thus, tooth bleaching activated by LED or LED plus LPT induces lesser resulted in increased vascular permeability than halogen light.