Mass loss and wear mechanisms of HVOF-sprayed multi-component white cast iron coatings

In this work, multi-component white cast iron was applied by HVOF thermal spray process as alternative to other manufacture processes. Effects of substrate type, substrate pre-heating and heat treatment of coating on mass loss have been determined by rubber wheel apparatus in accordance with ASTM G-65. Furthermore, influence of heat treatment of coating on wear mechanisms was also determined by scanning electron microscopy analysis. Heat-treated coatings presented mass loss three times lower than as-sprayed coatings. Furthermore, wear mechanisms of as-sprayed coating are micro-cutting associated with cracks close to unmelted particles and pores. In heat-treated coating, lesser mass loss is due to sintering. (C) 2011 Elsevier B.V. All rights reserved.

Minimal alterations on the enamel surface by micro-abrasion: in vitro roughness and wear assessments

Objective: To evaluate the in vitro changes on the enamel surface after a micro-abrasion treatment promoted by different products. Material and Methods: Fifty (50) fragments of bovine enamel (15 mm × 5 mm) were randomly assigned to five groups (n=10) according to the product utilized: G1 (control)= silicone polisher (TDV), G2= 37% phosphoric acid (3M/ESPE) + pumice stone (SS White), G3= Micropol (DMC Equipment), G4= Opalustre (Ultradent) and G5= Whiteness RM (FGM Dental Products). Roughness and wear were the responsible variables used to analyze these surfaces in four stages: baseline, 60 s and 120 s after the micro-abrasion and after polishing, using a Hommel Tester T1000 device. After the tests, a normal distribution of data was verified, with repeated ANOVA analyses (p?0.05) which were used to compare each product in different stages. One-way ANOVA and Tukey tests were applied for individual comparisons between the products in each stage (p?0.05). Results: Means and standard deviations of roughness and wear (µm) after all the promoted stages were: G1=7.26(1.81)/13.16(2.67), G2=2.02(0.62)/37.44(3.33), G3=1.81(0.91)/34.93(6.92), G4=1.92(0.29)/38.42(0.65) and G5=1.98(0.53)/33.45(2.66). At 60 seconds, all products tended to produce less surface roughness with a variable gradual decrease over time. After polishing, there were no statistically significant differences between the groups, except for G1. Independent of the product utilized, the enamel wear occurred after the micro-abrasion. Conclusions: In this in vitro study, enamel micro-abrasion presented itself as a conservative approach, regardless of the type of the paste compound utilized. These products promoted minor roughness alterations and minimal wear. The use of phosphoric acid and pumice stone showed similar results to commercial products for the micro-abrasion with regard to the surface roughness and wear.

An epidemiological scoring system for tooth wear and dental erosive wear

Background: The prevalence and severity of tooth wear and dental erosion is rising in children and there is no consensus about an index to be employed. Aim: To assess the reliability of an epidemiological scoring system dental wear index (DWI) to measure tooth wear and dental erosive wear. Design: An epidemiological cross-sectional survey was conducted to evaluate and compare tooth wear and dental erosion using the dental wear index and erosion wear index (EWI). The study was conducted with randomised samples of 2,371 children aged between 4 years and 12 years selected from the State of São Paulo, Brazil. Records were used for calculating tooth wear and dental erosion; the incisal edge and canine cusp were excluded. Results: As the schoolchildren's ages increased the severity of primary tooth wear increased in canines (P = 0.0001, OR = 0.34) and molars (P = 0.0001, OR = 2.47) and erosion wear increased in incisal/occlusal (P = 0.0001, OR = 5.18) and molars (P = 0.0001, OR = 2.47). There was an increased prevalence of wear in the permanent teeth of older schoolchildren, particularly on the incisal/occlusal surfaces (P = 0.0001, OR = 7.03). Conclusion: The prevalence of tooth wear and dental erosion increased as age increased in children. The epidemiological scoring system Dental Wear Index is able to measure both tooth wear and dental erosive wear. This index should be used to monitor the progression of non-carious lesions and to evaluate the levels of disease in the population.

Availability of heavy metals in contaminated soil evidenced by chemical extractants

Heavy metals have been accumulating in Brazilian soils, due to natural processes, such as atmospheric deposition, or human industrial activities. For certain heavy metals, when in high concentrations in the soil, there is no specific extractant to determine the availability of these elements in the soil. The objective of the present study was to evaluate the availability of Cd, Cu, Fe, Mn, Pb and Zn for rice and soybeans, using different chemical extractants. In this study we used seven soil samples with different levels of contamination, in completely randomized experimental design with four replications. We determined the available concentrations of Cd, Cu, Fe, Mn, Pb and Zn extracted by Mehlich-1, HCl 0.1 mol L-1, DTPA, and organic acid extractants and the contents in rice and soybeans, which extracts were analyzed by ICP-OES. It was observed that Mehlich-1, HCl 0.1 mol L-1 and DTPA extractants were effective to assess the availability of Cd, Cu, Pb and Zn for rice and soybeans. However, the same was not observed for the organic acid extractant.

Migrant labor and wear-out in manual sugarcane harvesting in São Paulo, Brazil

The scope of this paper is to describe the work of manual sugarcane harvesters, assessing the nutritional behavior and body composition between the beginning and the end of the harvest. A descriptive longitudinal study was made of harvesters in Piracicaba, São Paulo, Brazil, who answered a socio-demographic questionnaire and authorized measurement of Body Mass Index, Body Fat Percentage and Arm Muscle Circumference at three stages. Creatine kinase on the skeletal isoform, C-reactive protein and plasma urea were measured at the end of the harvest. Thirty male migrant harvesters with ages ranging from 18 to 44 from the Northeast (Ceará) were assessed over a nine-month period. The workers suffered significant body fat and weight loss in the first half of the harvest. Eighteen workers had abnormal levels of creatine kinase and four - out of 24 who had donated blood - had altered urea levels. Sugarcane harvesting work causes weight and body fat loss and gains in the lean body mass index, which suffers wear-out when working on consecutive harvests. It can also cause changes in biochemical markers of chronic systemic inflammation. Further studies will make it possible to comprehend the relationships between stress, wear-out, labor longevity and health in sugarcane harvesting.

Tool wear evaluations in friction stir processing of commercial titanium Ti–6Al–4V

This research addresses the application of friction stir welding (FWS) of titanium alloy Ti–6Al–4V. Friction stir welding is a recent process, developed in the 1990s for aluminum joining; this joining process is being increasingly applied in many industries from basic materials, such as steel alloys, to high performance alloys, such as titanium. It is a process in great development and has its economic advantages when compared to conventional welding. For high performance alloys such as titanium, a major problem to overcome is the construction of tools that can withstand the extreme process environment. In the literature, the possibilities approached are only few tungsten alloys. Early experiments with tools made of cemented carbide (WC) showed optimistic results consistent with the literature. It was initially thought that WC tools may be an option to the FSW process since it is possible to improve the wear resistance of the tool. The metallographic analysis of the welds did not show primary defects of voids (tunneling) or similar internal defects due to processing, only defects related to tool wear which can cause loss of weld quality. The severe tool wear caused loss of surface quality and inclusions of fragments inside the joining, which should be corrected or mitigated by means of coating techniques on tool, or the replacement of cemented carbide with tungsten alloys, as found in the literature.

Friction and wear of performance of MoDTC and ester-containing lubrificants over steel surfaces under reciprocating conditions

Since the earliest developments of human history, friction has been a major issue. From the invention of the wheel and the use of the first lubricants to the studiesof coated and microtexturized surfaces, significant effort has been put on improvements that couldovercome the resistance to motion. Areview by Holmberg, Andersson and Erdemir[1] shows that, in an average passenger car, about one third of the total energy consumptionis due to friction losses. Of these, another one third is consumed in the engine system. The optimization of the lubricating oil formulation used ininternal combustion enginesis an important way to reduce friction, therefore improving energeticefficiencyand controllingemissions.Lubrication is also a way to assure the required protection to the system by maintaining wear rates in an adequate level, which helps to minimize maintenance costs.

Femtosecond laser processing of glassy and polymeric matrices containing metals and semiconductor nanostructures

Tailoring properties of materials by femtosecond laser processing has been proposed in the last decade as a powerful approach for technological applications, ranging from optics to biology. Although most of the research output in this field is related to femtosecond laser processing of single either organic or inorganic materials, more recently a similar approach has been proposed to develop advanced hybrid nanomaterials. Here, we report results on the use of femtosecond lasers to process hybrid nanomaterials, composed of polymeric and glassy matrices containing metal or semiconductor nanostructures. We present results on the use of femtosecond pulses to induce Cu and Ag nanoparticles in the bulk of borate and borosilicate glasses, which can be applied for a new generation of waveguides. We also report on 3D polymeric structures, fabricated by two-photon polymerization, containing Au and ZnO nanostructures, with intense two-photon fluorescent properties. The approach based on femtosecond laser processing to fabricate hybrid materials containing metal or semiconductor nanostructures is promising to be exploited for optical sensors and photonics devices.