Bone mineral density in postmenopausal women with and without breast cancer

OBJECTIVE: The values of bone mineral density (BMD) were compared in postmenopausal women with and without breast cancer. METHODS: A cross-sectional study was conducted, including 51 breast cancer survivors (BCS) and 71 women without breast cancer, who were non-users of hormone therapy, tamoxifen, or aromatase inhibitors. BMD T-scores and measurements in grams per centimeter squared (g/cm²) were obtained at the femoral neck, trochanter, Ward's triangle, and lumbar spine. Osteopenia and osteoporosis were grouped and categorized as abnormal BMD. Unconditional logistic regression analysis was used to estimate the odds ratios (OR) of abnormal BMD values as measures of association, with 95% confidence intervals (CIs), adjusting for age, years since menopause, parity, and body mass index (BMI). RESULTS: The mean age of the women with and without breast cancer was 54.7 ± 5.8 years and 58.2 ± 4.8 years (p < 0.01), respectively. After adjusting for age, parity and BMI, abnormal BMD at the femoral neck (adjusted OR: 4.8; 95% CI: 1.5-15.4), trochanter (adjusted OR: 4.6; 95% CI: 1.4-15.5), and Ward's triangle (adjusted OR: 4.5; 95% CI: 1.5-12.9) were significantly more frequent in postmenopausal BCS than in women without breast cancer. Postmenopausal BCS had a significantly lower mean BMD at the trochanter (0.719 vs. 0.809 g/cm², p < 0.01) and at the Ward's triangle (0.751 vs. 0.805 g/cm², p = 0.03). CONCLUSION: The prevalence of abnormal BMD was higher in postmenopausal BCS than in postmenopausal women without breast cancer. Bone health requires special vigilance and the adoption of interventions should be instituted early to minimize bone loss in BCS.

Theoretical and experimental study of the excitonic binding energy in GaAs/AlGaAs single and coupled double quantum wells

This paper discusses the theoretical and experimental results obtained for the excitonic binding energy (Eb) in a set of single and coupled double quantum wells (SQWs and CDQWs) of GaAs/AlGaAs with different Al concentrations (Al%) and inter-well barrier thicknesses. To obtain the theoretical Eb the method proposed by Mathieu, Lefebvre and Christol (MLC) was used, which is based on the idea of fractional-dimension space, together with the approach proposed by Zhao et al., which extends the MLC method for application in CDQWs. Through magnetophotoluminescence (MPL) measurements performed at 4 K with magnetic fields ranging from 0 T to 12 T, the diamagnetic shift curves were plotted and adjusted using two expressions: one appropriate to fit the curve in the range of low intensity fields and another for the range of high intensity fields, providing the experimental Eb values. The effects of increasing the Al% and the inter-well barrier thickness on Eb are discussed. The Eb reduction when going from the SQW to the CDQW with 5 Å inter-well barrier is clearly observed experimentally for 35% Al concentration and this trend can be noticed even for concentrations as low as 25% and 15%, although the Eb variations in these latter cases are within the error bars. As the Zhao's approach is unable to describe this effect, the wave functions and the probability densities for electrons and holes were calculated, allowing us to explain this effect as being due to a decrease in the spatial superposition of the wave functions caused by the thin inter-well barrier.

Effects of specimen geometry and loading mode on crack growth resistance curves of a high-strength pipeline girth weld

This work presents an investigation of the ductile tearing properties for a girth weld made of an API 5L X80 pipeline steel using experimentally measured crack growth resistance curves. Use of these materials is motivated by the increasing demand in the number of applications for manufacturing high strength pipes for the oil and gas industry including marine applications and steel catenary risers. Testing of the pipeline girth welds employed side-grooved, clamped SE(T) specimens and shallow crack bend SE(B) specimens with a weld centerline notch to determine the crack growth resistance curves based upon the unloading compliance (UC) method using the single specimen technique. Recently developed compliance functions and η-factors applicable for SE(T) and SE(B) fracture specimens with homogeneous material and overmatched welds are introduced to determine crack growth resistance data from laboratory measurements of load-displacement records.