Evaluation of epoxy resin sealer after three root canal filling techniques by confocal laser scanning microscopy

The aim of this study was to evaluate the penetration of endodontic sealer into the dentin tubules, the integrity of the sealer layer perimeter, and the sealer area at the apical third after different filling techniques by confocal laser scanning microscopy (CLSM). Forty-five mandibular premolars were mechanically prepared with ProTaper files, until F5 file. Thereafter, they were filled with an epoxy-resin sealer (AH Plus) mixed with Rhodamine B dye (0.1% proportion) and allocated in three groups: Group 1, single master cone; Group 2, cold lateral compaction; and Group 3, Thermafil. For confocal laser scanning microscopy analysis, the specimens were transversely sectioned at 4 mm from the apex. The images at x10 and x40 were analyzed by Imagetool 3.0 software. Significant differences were not found among the three experimental groups according the dentin-impregnate area by the sealer (P = 0.68) and between the sealer and root canal perimeter (P = 0.18). However, root canal filling techniques were significantly different when apical sealer areas were compared (P = 0.001). Thermafil group showed smaller sealer areas (8.09%) while cold lateral compaction and gutta-percha master cone showed similar areas (17.37 and 21.18%, respectively). The dentin-impregnated area was not dependent on the root canal filling technique. Single master cone, cold lateral condensation and Thermafil techniques presented integrity of the sealer perimeter close to 100% and Thermafil resulted in a significantly thinner sealer layer. Microsc. Res. Tech. 75:12771280, 2012. (C) 2012 Wiley Periodicals, Inc.

Chitosan: effect of a new chelating agent on the microhardness of root dentin

The effect of solutions of 0.2% chitosan, 15% EDTA and 10% citric acid on the microhardness of root dentin was evaluated comparatively in this study. Thirteen sound human maxillary central incisors were selected and decoronated at the cementoenamel junction. Ten roots were set into rapid polymerization acrylic resin and the root/resin block was fitted to the cutting machine to obtain slices from the cervical third. The first slice was discarded and the second slice was divided into four quadrants. Each quadrant was used to construct a sample, so that 4 specimens were obtained from each root slice, being one for each chelating solution to be tested: 15% EDTA, 10% citric acid, 0.2% chitosan and distilled water (control). The specimens were exposed to 50 μL of the solution for 5 min, and then washed in distilled water. A microhardness tester (Knoop hardness) with a 10 g load was used for 15 s. Data were analyzed statistically by one-way ANOVA and Tukey-Kramer test (α=0.05). The other 3 roots had the canals instrumented and irrigated at the end of the biomechanical preparation with the test solutions, and then examined by scanning electron microscopy (SEM) for qualitative analysis. All solutions reduced the microhardness of root dentin in a way that was statistically similar to each other (p>0.05) but significantly different from the control (p>0.05). The SEM micrographs showed that the three solutions removed smear layer from the middle third of the root canal. In conclusion, 0.2% chitosan, 15% EDTA and 10% citric acid showed similar effects in reducing dentin microhardness.

Chlorhexidine does not increase immediate bond strength of etch-and-rinse adhesive to caries-affected dentin of primary and permanent teeth

The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on immediate bond strength of etch-and-rinse adhesive to sound (SD) and caries-affected (CAD) primary dentin compared with permanent dentin. Flat dentin surfaces from 20 primary molars (Pri) and 20 permanent molars (Perm) were assigned to 8 experimental groups (n=5) according to tooth type (Pri or Perm), dentin condition (SD or CAD - pH-cycling for 14 days) and treatment (control - C or 60 s application of 2% CHX solution after acid etching - CHX). The bonding system (Adper Single Bond 2) was applied according to manufacturer's instructions followed by resin composite application (Filtek Z250). After 24 h water storage, specimens with cross-section area of 0.8 mm² were prepared for being tested under microtensile test (1 mm/min). Data were submitted to ANOVA and Tukey's post hoc test (α=0.05). Failure mode was evaluated using a stereomicroscope at ×400. Treatment with CHX did not result in higher bond strength values than no pre-treatment (C groups), independently of tooth type. Primary teeth and caries-affected dentin showed significantly lower (p<0.05) bond strength means compared with permanent teeth and sound dentin, respectively. Predominance of adhesive/mixed failure was observed for all groups. CHX did not influence the immediate bond strength to sound or caries-affected dentin of primary and permanent teeth.

Effect of sodium hypochlorite and edta irrigation, individually and in alternation, on dentin microhardness at the furcation area of mandibular molars

The aim of this study was to evaluate the effect of irrigation regimens on dentin microhardness at the furcation area of mandibular molars, using sodium hypochlorite and ethylenediaminetetraacetic acid (EDTA), individually and in alternation. The occlusal surface and the roots of 20 non-carious extracted human permanent mandibular molars were cut transversally and discarded. The tooth blocks were embedded in acrylic resin and randomly assigned to 4 groups (n=5) according to the irrigating regimens: 1% NaOCl solution, 17% EDTA solution, 1% NaOCl and 17% EDTA and distilled water (control). Knoop microhardness of dentin at the furcation area was evaluated. Data were analyzed using one-way ANOVA and Tukey's multiple comparison tests (α=0.05). The results of this study indicated that all irrigation solutions, except for distilled water (control), decreased dentin microhardness. EDTA did not show a significant difference with NaOCl/EDTA (p>0.05), but showed a significant difference with NaOCl (p<0.01). EDTA and NaOCl/EDTA showed a maximum decrease in microhardness. The 17% EDTA solution, either alone or in combination with 1% NaOCl reduced significantly dentin microhardness at the furcation area of mandibular molars.