Influence of titanium and lutetium on the persistent luminescence of ZrO2

Non-doped as well as titanium and lutetium doped zirconia (ZrO2) materials were synthesized via the sol-gel method and structurally characterized with X-ray powder diffraction. The addition of Ti in the zirconia lattice does not change the crystalline structure whilst the Lu doping introduces a small fraction of the tetragonal phase. The UV excitation results in a bright white-blue luminescence at ca. 500 nm for all the materials which emission could be assigned to the Ti3+ e(g) -> t(2g) transition. The persistent luminescence originates from the same Ti3+ center. The thermoluminescence data shows a well-defined though rather similar defect structures for all the zirconia materials. The kinetics of persistent luminescence was probed with the isothermal decay curve analyses which indicated significant retrapping. The short duration of persistent luminescence was attributed to the quasi-continuum distribution of the traps and to the possibility of shallow traps even below the room temperature. (C) 2012 Optical Society of America

Synthesis, characterisation, luminescence and defect centres in solution combustion synthesised CaZrO3:Tb3+ phosphor

Tb3+ doped CaZrO3 has been prepared by an easy solution combustion synthesis method. The combustion derived powder was investigated by X-ray diffraction, Fourier-transform infrared spectrometry and scanning electron microscopy techniques. A room temperature photoluminescence study showed that the phosphors can be efficiently excited by 251 nm light with a weak emission in the blue and orange region and a strong emission in green light region. CaZrO3:Tb3+ exhibits three thermoluminescence (TL) glow peaks at 126 degrees C, 200 degrees C and 480 degrees C. Electron Spin Resonance (ESR) studies were carried out to study the defect centres induced in the phosphor by gamma irradiation and also to identify the centres responsible for the TL peaks. The room temperature ESR spectrum of irradiated phosphor appears to be a superposition of two distinct centres. One of the centres (centre I) with principal g-value 2.0233 is identified as an O- ion. Centre II with an axial symmetric g-tensor with principal values g(parallel to) = 1.9986 and g(perpendicular to) = 2.0023 is assigned to an F+ centre (singly ionised oxygen vacancy). An additional defect centre is observed during thermal annealing experiments and this centre (assigned to F+ centre) seems to originate from an F centre (oxygen vacancy with two electrons). The F centre and also the F+ centre appear to correlate with the observed high temperature TL peak in CaZrO3:Tb3+ phosphor. (c) 2012 Elsevier B.V. All rights reserved.

Black hole formation with an interacting vacuum energy density

We discuss the gravitational collapse of a spherically symmetric massive core of a star in which the fluid component is interacting with a growing vacuum energy density. The influence of the variable vacuum in the collapsing core is quantified by a phenomenological beta parameter as predicted by dimensional arguments and the renormalization group approach. For all reasonable values of this free parameter, we find that the vacuum energy density increases the collapsing time, but it cannot prevent the formation of a singular point. However, the nature of the singularity depends on the value of beta. In the radiation case, a trapped surface is formed for beta <= 1/2, whereas for beta >= 1/2, a naked singularity is developed. In general, the critical value is beta = 1-2/3(1 + omega) where omega is the parameter describing the equation of state of the fluid component.

Discovery of the Persistent Luminescence Mechanism of CdSiO3:Tb3+

The persistent luminescence of CdSiO3:Tb3+ was investigated with photoluminescence, thermoluminescence (TL), synchrotron radiation X-ray absorption (XANES and EXAFS) and UV-VUV spectroscopies. Only the typical intraconfigurational 4f(8)-4f(8) transitions of the Tb3+ ion were observed with no traces of band emission in either the conventional UV excited or persistent luminescence spectra. The trap structure from TL with three traps from 0.65 to 0.85 eV is ideal for room-temperature persistent luminescence similar to, e.g., Sr2MgSi2O7:Eu2+,R3+. Despite the rather low band gap energy, 5.28 eV, the persistent luminescence from Tb3+ is produced only under UV irradiation due to the inauspicious position of the F-7(6) ground level deep in the band gap of CdSiO3. This confirms the role of electrons as the charge carriers in the mechanism of Tb3+ persistent luminescence. The XANES spectra indicated the presence of only the trivalent Tb3+ species, thus excluding the direct Tb3+ -> Tb-IV oxidation during the charging process of persistent luminescence. Eventually, a unique persistent luminescence mechanism for Tb3+ in CdSiO3 was constructed based on the comprehensive experimental data.

Luminescence quantum efficiency at 1.5 µm of Er3+- doped tellurite glass determined by thermal lens spectroscopy

Erbium doped tellurite glasses (TeO2 + Li2O + TiO2) were prepared by conventional melt-quenching method to study the influence of the Er3+ concentration on the luminescence quantum efficiency (η) at 1.5 µm. Absorption and luminescence data were used to characterize the samples, and the η parameter was measured using the well-known thermal lens spectroscopy. For low Er3+ concentration, the measured values are around 76%, and the concentration behavior of η shows Er-Er and Er-OH- interactions, which agreed with the measured lifetime values.

Concentration quenching and thermal activation of the luminescence from terbium-doped a-SiC:H and c-AlN thin films

The effect of terbium (Tb) doping on the photoluminescence (PL) of crystalline aluminum nitride (c-AlN) and amorphous hydrogenated silicon carbide (a-SiC:H) thin films has been investigated for different Tb atomic concentrations. The samples were prepared by DC and RF magnetron reactive sputtering techniques covering the concentration range of Tb from 0.5 to 11 at.%. The Tb-related light emission versus the Tb concentration is reported for annealing temperatures of 450 °C, 750 °C and 1000 °C. In the low concentration region the intensity exhibits a linear increase and its slope is enhanced with the annealing temperature giving an activation energy of 0.106 eV in an Arrhenius plot. In the high concentration region an exponential decay is recorded which is almost independent on the host material, its structure and the annealing process.