Effect of pH-induced nanopowder deagglomeration on sintering, microstructure and dielectric properties of Ba0.77Ca0.23TiO3 ceramics

Ba0.77Ca0.23TiO3 ceramics were produced in this work starting from nanopowders synthesized via a polymeric precursor method. By adjusting the pH values of the precursor solutions above 7, it was possible to prepare powders weakly aggregated and with a smaller particle size, both facts which traduced into an enhanced nanopowders' sintering process at comparatively lower temperatures. Irrespective of the initial pH value, highly-dense and second phase-free ceramics were obtained following optimal sintering parameters (temperature and time) extracted from dilatometric and density measurements. By considering these and other sintering conditions, moreover, polycrystalline materials with an average grain size varying from 0.35 to 8 mm were produced, the grain growth process involving liquid phase-assisted sintering for heat treatments achieved at 1320 °C. The study of grain size effects on the ferroelectric properties of these materials was conducted, the results being discussed in the light of previous debates, including grain size-dependent degree of tetragonal distortion in such materials, as verified in this work.

Gold ion implantation into alumina using an “inverted ion source” configuration.

We describe an approach to ion implantation in which the plasma and its electronics are held at ground potential and the ion beam is injected into a space held at high negative potential, allowing considerable savings both economically and technologically. We used an “inverted ion implanter” of this kind to carry out implantation of gold into alumina, with Au ion energy 40 keV and dose (3–9) × 1016 cm−2. Resistivity was measured in situ as a function of dose and compared with predictions of a model based on percolation theory, in which electron transport in the composite is explained by conduction through a random resistor network formed by Au nanoparticles. Excellent agreement is found between the experimental results and the theory.

Effects of synthesis conditions on the nanostructre of CexZr1-xO2 mesoporous ceramics.

CexZr1-xO2 (0.5 ≤ x ≤ 0.9) were synthesized with Zr and Ce chloride precursors, using the triblock copolymer Pluronic P123 and HCl (2 mol/L). The pH adjustment was performed in two ways: synthesis A used 11.4 mL of a NH4OH solution added at once to the initial mixture, composed by metal precursors and template in HCl; synthesis B was done by dripping slowly until the change of pH value (between 3 and 6). In this work, CexZr1-xO2 samples synthesized by these two processes are compared. The effects of pH values in materials characteristics were also evaluated. These samples were analysed by X-Ray Diffraction (XRD) with Rietveld refinement, and Nitrogen Adsorption/Desorption. In both processes, the studied materials presented two crystalline phases of CexZr1-xO2 solid solution: cubic and tetragonal. The synthesis A also presented a tetragonal phase of ZrO2. The average crystallite size and the Brunauer- Emmett-Teller (BET) surface area are bigger in process A. Both processes give samples with a mesoporous structure.

Photoluminescence of core-shell nanoparticles made from yttrium stabilized zirconia powder grain coated with alumina

A YSZ@Al2O3 nanocomposite was obtained by Al2O3 coating on the surface of yttrium stabilized zirconia via a polymeric precursor method. The resulting core–shell structures were characterized by X-ray diffraction, scanning electron microscopy, transmission electronic microscopy and PL spectra. The TEM micrographs clearly show a homogeneous Al2O3 shell around the ZrO2 core. The observed PL is related to surface–interface defects. Such novel technologies can, in principle, explore materials which are not available in the bulk single crystal form but their figure-of-merit is dramatically dependent on the surface–interface defect states.