Determinação comparativa do grau de deformação plástica aplicado a componentes obtidos por conformação

The manufacturing process of components of Pressure Vessels has a great importance in the efficiency during the operation and life cycle of the equipment. Taking this into account, the objective of this dissertation was to analyze the methods to determine the strain rate in formed components by measuring the components themselves, and posterior results comparison with the values found in manufacturing standards of Pressure vessels. In this study the whole manufacturing process of a component from a pressure vessel, known as Head or End, was accompanied. Using the methodology obtained from literatures it was possible to execute the relative and logarithmic deformation measurements of these components and compare with the obtained results by means of equations presented in the Standards as AD-Merkblatt and ASME (for pressure vessels). The found results were also compared with the logarithmic methodology, taking into account the deformation of the empirical mesh and the thickness of the components studied. It is possible to conclude from this study that despite the existence of empirical methods of measurement of strain rate in components plastically formed, it is recommended the adoption in all situation of the component manufacturing standard. It can be noticed and explained during the development of this study and through the results found

Análise da resistência à fadiga de tubos de aço API 5CT N80 Tipo Q soldados via processo de indução magnética de alta frequência (HFIW)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência à corrosão da liga Ti-30Ta submetida a diferentes taxas de deformação visando aplicações biomédicas

This study aims to evaluate the corrosion resistance of Ti-30Ta alloy when subjected to different strain rates. Samples of the alloy Ti-30Ta were obtained from the melting of pure elements in the arc furnace in inert atmosphere (argon gas). Then, the samples were subjected to a thermal treatment and to cold worked to obtain bars. After forging, the samples were machined in accordance with ASTME9-09 standard for carried out compression tests. To microstructural characterization, samples were sectioned longitudinal and transversally and embedded in resin. After, the wet sanding and polishing were performed, followed by a chemical attack, in order to study the microstructure under an optical microscope. Microhardness was measured on the samples that were subjected to microstructural characterization by using microhardness tester. Phases were evaluated by x-rays diffraction. Corrosion tests were carried out to evaluate the influence of deformation on the corrosion resistance. Results show that microstructure was not influenced by deformation

Análise e comparação de orelhamento na liga AA3104 após laminação a quente

Aluminum has been widely used in the forming and manufacture of beverage cans, specific aluminum alloy AA3104, which manufacturers are increasingly demanding as to mechanical properties, quality and reducing waste. This work describes the analysis and comparison of the behavior of earing AA3104 aluminum alloy samples of final thicknesses of 1.80 and 2.10 mm. Were obtained after a hot rolling process, a total population of 86 samples for the two different thicknesses, of which 23 samples of 1.80 mm and 2.10 mm 63 samples. After removal of samples, there was a mechanical test inlay, then characterizing the earing in them. The results earing to the thicknesses of 1.80 and 2.10 mm were analyzed and compared statistically to give 7.1% and 7.4% on average, respectively, correlated with the hot rolling process variables, showing that they are statistically equal and that the process variables do not affect the end result desired, ranging from 7.0 to 7,5%

Estratigrafia do Andar Alagoas na sub-bacia do Tucano Norte, Bahia

Pós-graduação em Geociências e Meio Ambiente - IGCE