Tratamento térmico de normalização em tampos de vasos de pressão fabricados de material P275NH

In a market environment increasingly competitive, the companies need to control of this process accurately, avoiding rework or rejection of materials during industrialization. This can be achieved by defining procedure that assure the maintenance of the materials characteristics, as specified initially in the projects. This graduation work has the objective of defining the best heat treatment parameter of normalizing for Heads, part of a pressure vessel, formed in P275NH material. The methodology applied is based on the execution of a sequence of Heat Treatments, using different parameters. The process variables were the cooling velocity, the hold time and the hold temperature variation. As a result of this study, it is noticed that the mechanical properties of the materials are strongly influenced by the hold temperature variation and by the cooling velocity, both determined for the heat treatment cycle

Análise do perfil de dureza e microestrutura de um aço forjado AISI A2 submetido a tratamento térmico com resfriamento em água

Due to the large use of steel in several processes around the world, there is the increasingly concern to find new materials and/or optimization and improvement of the processes, as the need to reduce the cost and a productivity increase in the primary industry, such as the siderurgy. The rolling is the most used mechanical process in the world and therefore is required the development of new tools in high volume and with optimum characteristics to support the market demand. Forged rolls used are for rolling. These rolls have heat treatment that has the purpose to achieve the appropriated mechanical properties to support the variables of the rolling process. The objective of this work is to analyze the hardness profile and the microstructure a tool steel similar to AISI A2, forged in an opened die process and submitted to heat treatment with water-cooling. The results allowed plotting a hardness profile and performing a microstructure analysis, and whereby to confirm that the heat treatment is not a quenching, but it is a material beneficiation by the hardening of superficial layer, since there is no martensitic microstructure. Therefore, this paper provides the support to future studies about the possibility to perform enhancements in this thermal heat made in the rolls produced at Gerdau Plant in Pindamonhangaba

Caracterização da liga Ti-30Ta após tratamento biomimético associado à incorporação de antibiótico

Surface treatments have been used to modify the surface of titanium alloys. The purpose of this study is to evaluate the surface of Ti-30Ta alloy after biomimetic approach associated to antibiotic incorporation. The ingots were obtained in arc melting furnace, treated and cold-worked by swaging. The surface treatment was performed in two steps: biomimetic treatment and antibiotic incorporation. For biomimetic treatment, first an alkaline treatment (NaOH 1M at 60ºC) was performed, followed by heat treatment and immersion in SBFx5 (Simulated Body Fluid) for a period of 24 hours. In order to incorporate the antibiotic, samples were immersed in a solution formed by drugs plus SBFx5 for 48 hours. The sample surfaces were analyzed by scanning electron microscopy (SEM), X-Ray diffraction (XRD), atomic force microscopy (AFM) and contact angle measurements. The release of antibiotic from coated implants was measured in phosphate buffer saline at pH 7.4 by using UV/VIS spectrometry. Results have shown changes on the surface after incorporating the drug, which is gradually co-precipitated with the Ca-P crystals, forming a uniform and rough layer on the metal surface

Influência do peróxido e do uso de diferentes substâncias de combate à dor na inflamação e na expressão de neuropeptídeos pró-inflamatórios após o tratamento clareador

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)