Influência da incorporação de nanofibras de poliamida 6 com e sem nanotubos de carbono como reforço de prótese parcial fixa adesiva

The aim of this study was to evaluate the behavior of reinforced composites with polyamide 6 fibers aligned (6000 rpm) and alignment (120 rpm) with or without CNT using the flexural strength test. After preparation of nanofibers aligned nylon 6 (6000 rpm) and alignment (120 rpm) with and without incorporation of nanotube carbon by the method of electrospinning, were performed one control group (n = 10) and 4 experimental groups (n = 40) G1: Control (just resin Charisma - Heraeus Kulzer) ;G2 Resin + N6 aligned (6000 rpm) + CNT; G3:Resin + N6 alignment (120 rpm) + CNT; G4: Resin + aligned ( 6000 rpm) N6. G5: Resin + N6 alignment (120 rpm). The fibers were cut to the dimensions of 0,3 x 15 mm and were applied an adhesive at the surface (Single Bond 2) for 5 min and cured. In the matrix, was added resin in the proximal box (Charisma A2, Heraeus Kulzer) and cured for 40 s. (power 1100 mW / cm²). A first layer of resin and on the resin was deposited. The resin layers specimens were light irradiated with three overlapping exposures delivered. For each resin layer were light irradiated for 40 sec. The samples were tested with a cross-speed of 1 mm / min, and a 50 Kgf at Universal testing machine (EMIC mod.DL2000). The Dunnet test showed that only the nanotube group was significantly different from the control group. The ANOVA two-way indicates that the nanotube factor was statistically significant (p < 0.05) and there is no interaction between factors and orientation nanotube. The presence of nanotube showed lower fracture resistance values for aligned and unaligned groups. The results of this study showed that the orientation of the fibers does not influence the strength of composite resins and the incorporation of nylon nanofibers with carbon nanotubes decreased the fracture resistance values. The presence of the fibers has not been able to improve the strength of the material in any of the...

Aplicação de projeto de experimento no processo de manufatura de uma bobina de alumínio

TProducts must follow specifications in order to attend demands requested. In terms of rolled aluminum, one of the most significant items for customers is coil thickness. This is because only a tiny variation in thickness might cause a serious problem on customer's manufacturing line. Thereby, this research aims to analyze through design of experiments which factors and how they affect the thickness of aluminum coils. The response variable of the experiment is the thickness of aluminum coil, tensile strenght and yield strenght are the factors of the experiment and trimmers machines were considered as blocking. Data were obtained through tensile tests. The result of the experiment states that, according to the analysis of variance (ANOVA), while there is significant difference between the two levels of tensile strength, there is not any difference between the two levels of yield strength and trimmers machines. The thickness of the aluminum coils with high values of tensile strength tends to be thicker when compared with low values of tensile strength