Synthesis and proton conduction properties of lanthanide amino-sulfophosphonates

Crystalline acid-functionalized metal phosphonates are potential candidates as proton conducting electrolytes. Their frameworks can be chemically modified to contain proton carriers such as acidic groups (P-OH; -SO3H, -COOH,…) and guest molecules (H2O, NH3,…) that generates hydrogen bond networks stable in a wide range of temperature [1,2]. In this work, focus is laid on properties derived from the combination of lanthanide ions with the amino-sulfophosphonate ligand (H2O3PCH2)2-N-(CH2)2-SO3H. Hightrough-put screening was followed to reach the optimal synthesis conditions under solvothermal conditions at 140 ºC. Isolated polycrystalline solids, Ln[(O3PCH2)2-NH-(CH2)2-SO3H].2H2O (Ln= La, Pr and Sm), crystallize in the monoclinic (La) and orthorhombic (Pr and Sm) systems with unit cell volume of ~2548 Å3. Preliminary proton conductivity measurements for Sm derivative have been carried out between 25º and 80 ºC at relative humidity (RH) values of 70 % and 95 %. The sample exhibits enhanced conductivity at high RH and T (Figure 1) and constant activation energies of 0.4 eV, typical of a Grothuss mechanism of proton.

Structural and functional interaction between polyamine related molecules and biological membranes

Changes induced by PA on nucleic acid (NA) conformation and synthesis is proven to be a major reason for PA essentiality (1-3). However, PA interactions with other polyanions, for instance polyanionic membrane lipid bilayers and glyosaminoglycans have received less attention (3-4). The functional importance of these interactions still is an obscure but interesting area of cell and molecular biology, especially in mammalian cells for which specific PA transport systems are not fully characterized (5). In mammals, activity and turnover of the polyamine (PA) synthesis key enzyme is controlled by a set of proteins: Antizymes (OAZ1-3) and antizyme inhibitors (AZIN1 and 2). It is demonstrated that AOZ modulate polyamine uptake (6), and that PA transport to mitochondria is linked to the respiratory chain state and modulates mitochondrial permeability transition (7). Antizyme expression variants have been located in mitochondria, being proposed as a proapoptotic factor (7-8). AZIN 2 is only expressed in a reduced set of tissues that includes mast cells, where it is associated to mast cell granules membrane (9). This fact, together to the abnormalities observed in bone marrow derived mast cell granules when they are differentiated under restricted PA synthesis conditions (10 and unpublished results), point out to important roles of PA and their related proteins in structure and function of mast cell granules. We will also present novel biophysical results on tripartite interactions of PA that remark the interest of the characterization of PA interactions with lipid bilayers for biomedicine and biotechnology. Thus, the information reported in this paper integrates previously reported information with our still unpublished results, all indicating that PA and their related proteins also are important factors for structure and dynamics of biological membranes and their associated functions essential in human physiology; for instance, solute interchange with the environment (uptake and secretion), oxidative metabolism and apoptosis. The importance of these involved processes for human homeostasis claim for further research efforts. 1. Ruiz-Chica J, Medina MA, Sánchez-Jiménez F and Ramírez FJ (2001) Fourier Transform Raman study of the structural specificities on the interaction between DNA and biogenic polyamines. Biophysical J. 80:443-454. 2. Lightfoot HL, Hall J (2014) Endogenous polyamine function--the RNA perspective. Nucleic Acids Res. 42:11275-11290. 3. Igarashi K, Kashiwagi K (2010) Modulation of cellular function by polyamines. Int J Biochem Cell Biol. 42:39-51. 4. Finger S, Schwieger C, Arouri A, Kerth A, Blume A (2014) Interaction of linear polyamines with negatively charged phospholipids: the effect of polyamine charge distance. Biol Chem. 395:769-778. 5. Poulin R, Casero RA, Soulet D. (2012) Recent advances in the molecular biology of metazoan polyamine transport. Amino Acids. 42:711-723. 6. Kahana C (2009) Regulation of cellular polyamine levels and cellular proliferation by antizyme and antizyme inhibitor. Essays Biochem. 4:47-61. 7. Agostinelli E, Marques MP, Calheiros R, Gil FP, Tempera G, Viceconte N, Battaglia V, Grancara S, Toninello A (2010) Polyamines: fundamental characters in chemistry and biology. Amino Acids 38:393-403. 8. Liu GY, Liao YF, Hsu PC, Chang WH, Hsieh MC, Lin CY, Hour TC, Kao MC, Tsay GJ, Hung HC (2006) Antizyme, a natural ornithine decarboxylase inhibitor, induces apoptosis of haematopoietic cells through mitochondrial membrane depolarization and caspases' cascade. Apoptosis 11:1773-1788. 9. Kanerva K, Lappalainen J, Mäkitie LT, Virolainen S, Kovanen PT, Andersson LC (2009). Expression of antizyme inhibitor 2 in mast cells and role of polyamines as selective regulators of serotonin secretion. PLoS One 31:e6858. 10. García-Faroldi G, Rodríguez CE, Urdiales JL, Pérez-Pomares JM, Dávila JC, Pejler G, Sánchez-Jiménez F, Fajardo I (2010) Polyamines are present in mast cell secretory granules and are important for granule homeostasis. PLoS One 30:e15071.

Synthesis of active Belite-Alite-Ye'elimite clinker (BAY)

Ordinary Portland cement (OPC) is an environmentally contentious material, as for every ton of OPC produced, on average, 0.97 tons of CO2 are released. Ye'elimite-rich cements are considered as eco-cements because their manufacturing process releases less CO2 into the atmosphere than OPC; this is due to the low calcite demand. Belite-Alite-Ye’elimite (BAY) cements are promising eco-friendly building materials as OPC substitutes at a large scale. The reaction of alite and ye´elimite with water should develop cements with high mechanical strengths at early ages, while belite will contribute to later curing times. However, they develop lower mechanical strengths at early-medium ages than OPC. It is known that the presence of different polymorphs of ye'elimite and belite affects the hydration due to the different reactivity of those phases. Thus, a solution to this problem may be well the activation of BAY clinkers by preparing them with 'H-belite and pseudo-cubic-ye'elimite, jointly with alite. The aim of this work is the preparation and characterization of active-BAY clinkers which contain high percentages of coexisting 'H-belite and pseudo-cubic-ye'elimite, jointly with alite to develop, in a future step, comparable mechanical strengths to OPC. The parameters evolved in the preparation of the clinker have been optimized, including the selection of raw materials (mineralizers and activators) and clinkering conditions. Finally, the clinker was characterized through laboratory X-ray powder diffraction, in combination with the Rietveld methodology, and scanning electron microscopy.

Synthesis and behavior of Belite-Alite-Ye’elimite (BAY) cement

Ye’elimite based cements have been studied since 70’s years in China, due to the irrelevant characteristics from a hydraulic and environmental point of view. One of them is the reduced fuel consumption, related to the lower temperature reaction required for this kind of cement production as compared to Ordinary Portland Cement (OPC), another characteristic is the reduced requirement of carbonates as a typical raw material, compared to OPC, with the consequent reduction in CO2 releases (~22%)from combustion. Thus, Belite-Ye’elimite-Ferrite (BYF) cements have been developed as potential OPC substitutes. BYF cements contain belite as main phase (>50 wt%) and ye´elimite as the second content phase (~30 wt%). However, an important technological problem is associated to them, related to the low mechanical strengths developed at intermediate hydration ages (3, 7 and 28 days). One of the proposed solutions to this problem is the activation of BYF clinkers by preparing clinkers with high percentage of coexisting alite and ye'elimite. These clinkers are known Belite-Alite-Ye’elimite (BAY) cements. Their manufacture would produce ~15% less CO2 than OPC. Alite is the main component of OPC and is responsible for early mechanical strengths. The reaction of alite and ye´elimite with water will develop cements with high mechanical strengths at early ages, while belite will contribute to later curing times. Moreover, the high alkalinity of BAY cement pastes/mortars/concretes may facilitate the use of supplementary cementitious materials with pozzolanic activity which also contributes to decrease the CO2 footprint of these ecocements. The main objective of this work was the design and optimization of all the parameters evolved in the preparation of a BAY eco-cement that develop higher mechanical strengths than BYF cements. These parameters include the selection of the raw materials (lime, gypsum, kaolin and sand), milling, clinkering conditions (temperature, and holding time), and clinker characterization The addition of fly ash has also been studied. All BAY clinker and pastes (at different hydration ages) were mineralogically characterized through laboratory X-ray powder diffraction (LXRPD) in combination with the Rietveld methodology to obtain the full phase assemblage including Amorphous and Crystalline non-quantified, ACn, contents. The pastes were also characterized through rheological measurements, thermal analyses (TA), scanning electronic microscopy (SEM) and nuclear magnetic resonance (NMR). The compressive strengths were also measured at different hydration times and compared to BYF.