Proton conductivity and luminiscence properties of lanthanide aminotriphosphonates

Metal phosphonates are multifunctional solids with tunable properties, such as internal H-bond networks, and high chemical and thermal stability [1]. In the present work, we describe the synthesis, structural characterization, luminescent properties and proton conduction performance of a new family of isostructural cationic compounds with general formula [Ln(H4NMP)(H2O)2]Cl·2H2O [Ln = La3+, Pr3+, Sm3+, Gd3+, Tb3+, Dy3+, Ho3+, H6NMP = nitrilotris(methylphosphonic acid)]. These solids are formed by positively charge layers, which consist of isolated LnO8 polyhedra and bridge chelating NMP2- ligands, held apart by chloride ions and water molecules. This arrangement result in extended interlayer hydrogen networks with possible proton transfer pathways. The proton conductivity of Gd3+ sample, selected as prototype of the series, was measured. In the range between range 25º and 80 ºC, the conductivity increase with the temperature up to a maximum value of 3.10-4 S·cm-1, at relative humidity of 95 %. The activation energy obtained from the Arrhenius plot (Figure 1) is in the range corresponding to a Grotthuss transfer mechanism.

Ammonia effects on proton conductivity properties of coordination polymers

Crystalline metal phosphonates are referred to as a type of structurally versatile coordination polymers [1]. Many of them contain guest molecules (H2O, heterocyclics, etc.), acidic sites and, furthermore, their structure can be also amenable for post‐synthesis modifications in order to enhance desired properties [2]. In the present work, we examine the relationships between crystal structure and proton conductivity for several metal phosphonates derive from multifunctional ligands, such as 5-(dihydroxyphosphoryl)isophthalic acid (PiPhtA) [3] and 2-hydroxyphosphonoacetic acid (H3HPAA). Crystalline divalent metal derivatives show a great structural diversity, from 1D to 3D open-frameworks, possessing hydrogen-bonded water molecules and acid groups. These solids present a proton conductivity range between 7.2·10-6 and 1.3·10−3 S·cm-1. Upon exposure to ammonia vapor, from an aqueous solution, solid state transformations are observed accompanied of enhance proton conductivities. The stability of these solids under different environment conditions (temperature and relative humidities) as well as the influence of the ammonia adsorption on the proton conduction properties of the resulting solids will be discussed.