Quantitative phase Analisis: A comparative study of Mo and Cu strictly monochromatic radiations

A comparison of the Rietveld quantitative phase analyses (RQPA) obtained using Cu-Kα1, Mo-Kα1, and synchrotron strictly monochromatic radiations is presented. The main aim is to test a simple hypothesis: high energy Mo-radiation, combined with high resolution laboratory X-ray powder diffraction optics, could yield more accurate RQPA, for challenging samples, than well-established Cu-radiation procedure(s). In order to do so, three set of mixtures with increasing amounts of a given phase (spiking-method) were prepared and the corresponding RQPA results have been evaluated. Firstly, a series of crystalline inorganic phase mixtures with increasing amounts of an analyte was studied in order to determine if Mo-Kα1 methodology is as robust as the well-established Cu-Kα1 one. Secondly, a series of crystalline organic phase mixtures with increasing amounts of an organic compound was analyzed. This type of mixture can result in transparency problems in reflection and inhomogeneous loading in narrow capillaries for transmission studies. Finally, a third series with variable amorphous content was studied. Limit of detection in Cu-patterns, ~0.2 wt%, are slightly lower than those derived from Mo-patterns, ~0.3 wt%, for similar recording times and limit of quantification for a well crystallized inorganic phase using laboratory powder diffraction was established ~0.10 wt%. However, the accuracy was comprised as relative errors were ~100%. Contents higher than 1.0 wt% yielded analyses with relative errors lower than 20%. From the obtained results it is inferred that RQPA from Mo-Kα1 radiation have slightly better accuracies than those obtained from Cu-Kα1. This behavior has been established with the calibration graphics obtained through the spiking method and also from Kullback-Leibler distance statistic studies. We explain this outcome, in spite of the lower diffraction power for Mo-radiation (compared to Cu-radiation), due to the larger volume tested with Mo, also because higher energy minimize pattern systematic errors and the microabsorption effect.

Synthesis and behavior of Belite-Alite-Ye’elimite (BAY) cement

Ye’elimite based cements have been studied since 70’s years in China, due to the irrelevant characteristics from a hydraulic and environmental point of view. One of them is the reduced fuel consumption, related to the lower temperature reaction required for this kind of cement production as compared to Ordinary Portland Cement (OPC), another characteristic is the reduced requirement of carbonates as a typical raw material, compared to OPC, with the consequent reduction in CO2 releases (~22%)from combustion. Thus, Belite-Ye’elimite-Ferrite (BYF) cements have been developed as potential OPC substitutes. BYF cements contain belite as main phase (>50 wt%) and ye´elimite as the second content phase (~30 wt%). However, an important technological problem is associated to them, related to the low mechanical strengths developed at intermediate hydration ages (3, 7 and 28 days). One of the proposed solutions to this problem is the activation of BYF clinkers by preparing clinkers with high percentage of coexisting alite and ye'elimite. These clinkers are known Belite-Alite-Ye’elimite (BAY) cements. Their manufacture would produce ~15% less CO2 than OPC. Alite is the main component of OPC and is responsible for early mechanical strengths. The reaction of alite and ye´elimite with water will develop cements with high mechanical strengths at early ages, while belite will contribute to later curing times. Moreover, the high alkalinity of BAY cement pastes/mortars/concretes may facilitate the use of supplementary cementitious materials with pozzolanic activity which also contributes to decrease the CO2 footprint of these ecocements. The main objective of this work was the design and optimization of all the parameters evolved in the preparation of a BAY eco-cement that develop higher mechanical strengths than BYF cements. These parameters include the selection of the raw materials (lime, gypsum, kaolin and sand), milling, clinkering conditions (temperature, and holding time), and clinker characterization The addition of fly ash has also been studied. All BAY clinker and pastes (at different hydration ages) were mineralogically characterized through laboratory X-ray powder diffraction (LXRPD) in combination with the Rietveld methodology to obtain the full phase assemblage including Amorphous and Crystalline non-quantified, ACn, contents. The pastes were also characterized through rheological measurements, thermal analyses (TA), scanning electronic microscopy (SEM) and nuclear magnetic resonance (NMR). The compressive strengths were also measured at different hydration times and compared to BYF.

In situ characterization of porous VPO catalysts with fibrous structure: Identifying the redox behavior and the stability of active sites

Two VPO materials with fibrillar morphology have been prepared by the aid of electrospinning technique. One is a VPO carbon-supported material (VCF200) with fibrous morphology and very high surface area that is stable under oxidizing conditions up to 350C. The other material is a bulk mixed VPO oxide (VPO500) with fibrous structure obtained after optimizing the calcination of the carbon support in VCF200. Despite it is a bulk oxide material, this material exhibits a high surface area (> 60 m2/g). The redox behavior of both samples was monitored by in situ Raman spectroscopy under oxidation/reduction cycles. For the dehydrated supported sample (VCF200), the pyrophosphate phase (VO)2P2O7 (Raman ~930 cm-1) is detected, which has been described as the active phase (see Figure (a) below). This phase is quite stable since it does not disappear upon subsequent oxidation/reduction cycles. Under reduction conditions at 125C, in consecutive cycles, additional Raman bands appear at ~1090 cm-1 that are characteristic of the αII-VOPO4 phase. On the other hand, the bulk phases show a reversible behavior under redox cycles (Figure (b)). Under reducing conditions, a Raman band appears at ~980 cm-1 (β-VPO phase), whereas under oxidation conditions some segregation to VOx oxides occurs. Nevertheless, this segregation is reversible and the β-VPO phase forms again under reducing conditions. Thus, these results demonstrate that the active VPO phases of these fibrous catalysts are quite stable, and that their structure is reversible under several redox cycles, which make them suitable as oxidation catalysts.