In-situ Molibdenum X-ray powder diffraction study of the early hydration of cementitious systems on a humidity chamber

The durability of cement-based construction materials depends on the environmental conditions during their service life. A further factor is the microstructure of the cement bulk, established by formation of cement hydrates. The development of the phases and microstructure under given conditions is responsible of the high strength of cementitious materials. The investigation on the early hydration behavior of cements and cementing systems has been for a long time a very important area of research: understanding the chemical reactions that lead to hardening is fundamental for the prediction of performances and durability of the materials. The production of 1 ton of Ordinary Portland Cement, OPC, releases into the atmosphere ~0.97 tons of CO2. This implies that the overall CO2 emissions from the cement industry are 6% of all anthropogenic carbon dioxide. An alternative to reduce the CO2 footprint consists on the development of eco-cements composed by less calcite demanding phases, such as belite and ye'elimite. That is the case of Belite-Ye’elimite cements (BY). Since the reactivity of belite is not quick enough, these materials develop low mechanical strengths at intermediate hydration ages. A possible solution to this problem goes through the production of cements which jointly contain alite with the two previously mentioned phases, named as Belite-Alite-Ye’elimite (BAY) cements. The reaction of alite and ye'elimite with water will develop cements with high mechanical strengths at early ages, while belite will contribute to later values. The final goal is to understand the hydration mechanisms of a variety of cementing systems (OPC, BAY and pure phases) as a function of water content, superplasticizer additives and type and content of sulfate source. In order to do so, in-situ laboratory humidity chambers with Molybdenum X-ray Powder diffraction are employed. In the first 2h of hydration, reaction degree (α) of ye'elimite had been decreased for superplasticizer.

Dispersion and optimization of a calcium sulfoaluminate mortar prepared with superplasticizer

Calcium sulfoaluminate (CSA) cements/mortars are receiving increasing attention since their manufacture produces less CO2 than ordinary Portland cement (OPC) (up to 22% of decrease depending on its composition). These systems are complex and there are many parameters affecting their hydration mechanism, such as water-to-cement (w/c) ratio, type and amount of sulfate source, and so on. Low w/c ratios, within certain limits, may reduce the porosity and consequently, improve the mechanical strengths. However, it is accompanied by an increasing of viscosity and lack of both workability and homogeneity, with the consequent negative effect on the mechanical properties. The dispersion of the particles through the adsorption of the right amount and type of additives, such as superplasticizers, is a key point to improve the workability of mortars allowing both the preparation of homogeneous mixtures and the reduction of the amount of mixing water. This work deals with the preparation and optimization of homogeneous CSA-mortars with improved mechanical strengths. The optimum amount of superplasticizer was optimized through rheological measurements. The effect of different amounts of the superplasticizer on the viscosity of the mortars, its hydration mechanism and corresponding mechanical properties has been studied and will be discussed.

Synthesis and behavior of Belite-Alite-Ye’elimite (BAY) cement

Ye’elimite based cements have been studied since 70’s years in China, due to the irrelevant characteristics from a hydraulic and environmental point of view. One of them is the reduced fuel consumption, related to the lower temperature reaction required for this kind of cement production as compared to Ordinary Portland Cement (OPC), another characteristic is the reduced requirement of carbonates as a typical raw material, compared to OPC, with the consequent reduction in CO2 releases (~22%)from combustion. Thus, Belite-Ye’elimite-Ferrite (BYF) cements have been developed as potential OPC substitutes. BYF cements contain belite as main phase (>50 wt%) and ye´elimite as the second content phase (~30 wt%). However, an important technological problem is associated to them, related to the low mechanical strengths developed at intermediate hydration ages (3, 7 and 28 days). One of the proposed solutions to this problem is the activation of BYF clinkers by preparing clinkers with high percentage of coexisting alite and ye'elimite. These clinkers are known Belite-Alite-Ye’elimite (BAY) cements. Their manufacture would produce ~15% less CO2 than OPC. Alite is the main component of OPC and is responsible for early mechanical strengths. The reaction of alite and ye´elimite with water will develop cements with high mechanical strengths at early ages, while belite will contribute to later curing times. Moreover, the high alkalinity of BAY cement pastes/mortars/concretes may facilitate the use of supplementary cementitious materials with pozzolanic activity which also contributes to decrease the CO2 footprint of these ecocements. The main objective of this work was the design and optimization of all the parameters evolved in the preparation of a BAY eco-cement that develop higher mechanical strengths than BYF cements. These parameters include the selection of the raw materials (lime, gypsum, kaolin and sand), milling, clinkering conditions (temperature, and holding time), and clinker characterization The addition of fly ash has also been studied. All BAY clinker and pastes (at different hydration ages) were mineralogically characterized through laboratory X-ray powder diffraction (LXRPD) in combination with the Rietveld methodology to obtain the full phase assemblage including Amorphous and Crystalline non-quantified, ACn, contents. The pastes were also characterized through rheological measurements, thermal analyses (TA), scanning electronic microscopy (SEM) and nuclear magnetic resonance (NMR). The compressive strengths were also measured at different hydration times and compared to BYF.