X-Ray powder diffraction laboratory @ University of Málaga (UMA)

X-Ray Powder Diffraction (XRPD) laboratory is a facility placed at Servicios Centrales de apoyo a la Investigación (SCAI) at University of Malaga (UMA) http://www.scai.uma.es/. This facility has three XRPD diffractometers and a diffractometer to measure high-resolution thin-films. X´Pert PRO MPD from PANalytical. This is a bragg-brentano (theta/2theta) with reflection geometry diffractometer which allows to obtain high resolution XRPD data with strictly monochromatic CuKα1 radiation (λ=1.54059Å) [Ge(111) primary monochromator] and an automatic sample charger. Moreover, it has parallel monochromatic CuKα1 radiation (λ=1.54059Å) with an hybrid Ge(220) monochromator for capillary and multiproposal (bulk samples up to 1 Kg) sample holders. The HTK1200N chamber from Anton Paar allows collecting high resolution high temperature patterns. EMPYREAN from PANalytical. This diffractometer works in reflection and transmission geometries with theta/theta goniometer, using CuKα1,2 radiation (λ=1.5418Å), a focusing X-ray mirror and a ultra-fast PIXCEL 3D detector with 1D and 2D collection data modes (microstructural and preferred orientation analysis). Moreover, the TTK450N chamber allows low temperature and up to 450ºC studies. A D8 ADVANCE (BRUKER) was installed in April 2014. It is the first diffractometer in Europe equipped with a Johansson Ge(111) primary monochromator, which gives a strictly monochromatic Mo radiation (λ=0.7093 Å) [1]. It works in transmission mode (with a sample charger) with this high resolution configuration. XRPD data suitable for PDF (Pair Distribution Function) analysis can be collected with a capillary sample holder, due to the high energy and high resolution capabilities of this diffractometer. Moreover, it has a humidity chamber MHC-trans from Anton Paar working on transmission mode with MoKα1 (measurements can be collected at 5 to 95% of relative humidity (from 20 to 80 ºC) and up to 150ºC [2]). Furthermore, this diffractometer also has a reaction chamber XRK900 from Anton Paar (which uses CuKα1,2 radiation in reflection mode), which allows data collection from room temperature to 900ºC with up to 10 bar of different gases. Finally, a D8 DISVOVER A25 from BRUKER was installed on December 2014. It has a five axis Euler cradler and optics devices suitable for high resolution thin film data collection collected in in-plane and out-of-plane modes. To sum up, high-resolution thin films, microstructural, rocking-curve, Small Angle X-ray Scattering (SAXS), Grazing incident SAXS (GISAXS), Ultra Grazing incident diffraction (Ultra-GID) and microdiffraction measurements can be performed with the appropriated optics and sample holders. [1] L. León-Reina, M. García-Maté, G. Álvarez-Pinazo, I. Santacruz, O. Vallcorba, A.G. De la Torre, M.A.G. Aranda “Accuracy in Rietveld quantitative phase analysis: a comparative study of strictly monochromatic Mo and Cu radiations” J. Appl. Crystallogr. 2016, 49, 722-735. [2] J. Aríñez-Soriano, J. Albalad, C. Vila-Parrondo, J. Pérez-Carvajal, S. Rodríguez-Hermida, A. Cabeza, F. Busqué, J. Juanhuix, I. Imaz, Daniel Maspoch “Single-crystal and humidity-controlled powder diffraction study of the breathing effect in a metal-organic framework upon water adsorption/desorption” Chem. Commun., 2016, DOI: 10.1039/C6CC02908F.

Preparación y caracterización de biomateriales híbridos de hidroxiapatito con fosfonato (2-Hidroxi fosfonoacetato)

El hidroxiapatito es el biomineral de los tejidos duros de los mamíferos y por ello ha sido ampliamente estudiado como biomaterial en cementos óseos, recubrimientos de metales implantables y scaffold en ingeniería de tejidos. En este trabajo, se estudia un proceso síntesis y caracterización de un derivado de este material, donde el ion fosfonato: 2- hidroxifosfonoacetato sustituye parcialmente al ion fosfato [1-10%]. El proceso de síntesis de hidroxiapatito consiste en dos etapas: (1) una reacción a 100ºC entre el ácido fosfórico (añadido lentamente) y una mezcla de hidróxido de calcio + 2-hidroxifosfonoacetato de calcio (Relación Ca/P=1.67). (2) un tratamiento térmico de los sólidos obtenidos en (1) a 150ºC. Los productos finales se han caracterizado mediante análisis químico, análisis termogravimétrico, difracción de rayos-X con análisis de Rietveld, microscopía SEM y determinación de la superficie específica y porosidad. En las fases cristalinas, el grado de pureza de los hidroxiapatitos oscila entre 91-100%. Todos presentan estructura monoclínica, en contraste con la estructura hexagonal que habitualmente se obtiene aplicando métodos de síntesis similares. Esta variación se atribuye a la presencia de fosfonato. El contenido de éste también influye en la morfología y en la porosidad de los materiales, siendo las muestras con más fosfonato las más porosas. Los materiales, al menos aquellos con una cantidad menor o igual 5% de fosfonato, muestran una biocompatibilidad similar a un material de hidroxiapatito de referencia.

Quantitative phase Analisis: A comparative study of Mo and Cu strictly monochromatic radiations

A comparison of the Rietveld quantitative phase analyses (RQPA) obtained using Cu-Kα1, Mo-Kα1, and synchrotron strictly monochromatic radiations is presented. The main aim is to test a simple hypothesis: high energy Mo-radiation, combined with high resolution laboratory X-ray powder diffraction optics, could yield more accurate RQPA, for challenging samples, than well-established Cu-radiation procedure(s). In order to do so, three set of mixtures with increasing amounts of a given phase (spiking-method) were prepared and the corresponding RQPA results have been evaluated. Firstly, a series of crystalline inorganic phase mixtures with increasing amounts of an analyte was studied in order to determine if Mo-Kα1 methodology is as robust as the well-established Cu-Kα1 one. Secondly, a series of crystalline organic phase mixtures with increasing amounts of an organic compound was analyzed. This type of mixture can result in transparency problems in reflection and inhomogeneous loading in narrow capillaries for transmission studies. Finally, a third series with variable amorphous content was studied. Limit of detection in Cu-patterns, ~0.2 wt%, are slightly lower than those derived from Mo-patterns, ~0.3 wt%, for similar recording times and limit of quantification for a well crystallized inorganic phase using laboratory powder diffraction was established ~0.10 wt%. However, the accuracy was comprised as relative errors were ~100%. Contents higher than 1.0 wt% yielded analyses with relative errors lower than 20%. From the obtained results it is inferred that RQPA from Mo-Kα1 radiation have slightly better accuracies than those obtained from Cu-Kα1. This behavior has been established with the calibration graphics obtained through the spiking method and also from Kullback-Leibler distance statistic studies. We explain this outcome, in spite of the lower diffraction power for Mo-radiation (compared to Cu-radiation), due to the larger volume tested with Mo, also because higher energy minimize pattern systematic errors and the microabsorption effect.

The use of mo and cu monochromatic radiations for quantitative phase analysis: study of the accuracy

Cement hydration is a very complex process in which crystalline phases are dissolving in water and after supersaturation hydrated crystalline and amorphous phases precipitate. Great efforts are being made to develop analytical tools to accurately quantify these processes and X-ray Powder Diffraction (XRPD) combined with Rietveld methodology is a suitable tool to quantify these complex mixtures and their time evolutions. However, some problems/drawbacks should be overcome to fully apply it to cement pastes characterization in order to get accurate phase analyses. In order to tackle this issue, a comparison of the Rietveld quantitative phase analyses (RQPA) obtained using Cu-Kα1, Mo-Kα1, and synchrotron strictly monochromatic radiations of three set of mixtures with increasing amounts of a given phase (spiking-method) is presented. The main aim is to test a simple hypothesis: high energy Mo-radiation, combined with high resolution laboratory X-ray powder diffraction optics, could yield more accurate RQPA, for challenging samples, than well-established Cu-radiation procedure(s). Firstly, a series of crystalline inorganic phase mixtures with increasing amounts of an analyte was studied in order to determine if Mo-Kα1 methodology is as robust as the well-established Cu-Kα1 one. Secondly, a series of crystalline organic phase mixtures with increasing amounts of an organic compound was analyzed. This type of mixture can result in transparency problems in reflection and inhomogeneous loading in narrow capillaries for transmission studies. Finally, a third series with variable amorphous content was studied. Limit of detection in Cu-patterns, ~0.2 wt%, are slightly lower than those derived from Mo-patterns, ~0.3 wt%, for similar recording times and limit of quantification for a well crystallized inorganic phase using laboratory powder diffraction was established ~0.10 wt%. From the obtained results it is inferred that RQPA from Mo-Kα1 radiation have slightly better accuracies than those obtained from Cu-Kα1. The results obtained in the previous comparison have been taken into account to obtain accurate RQPA, including the amorphous component with internal standard methodology, of hydrating cement pastes. The final goal of this second study was understanding the early-stage hydration mechanisms of a variety of cementing systems (Ordinary Portland Cement or Belite Alite Ye’elimite cement) as a function of water content, superplasticizer additives and type and content of sulfate source. In order to do so, X-ray powder diffraction data were taken in-situ with the humidity chamber coupled to the Mo-Kα1 powder diffractometer. Some results of this ongoing investigation will be reported and discussed.

Procesamiento y análisis de mamografías para la detección de tumores

Este trabajo nace de una idea conjunta del desarrollo de un software capaz de trabajar con una máquina de rayos X para la toma de mamografías, y ser una herramienta para los radiólogos a la hora de analizar las imágenes y localizar zonas que pudieran ser sensibles de tener algún tipo de tumoración. No se trata de un software que pretenda suplantar la función de un radiólogo; es importante tener claro que el experto en radiología es el único capaz de analizar, comparar y tomar decisiones reales, y este software pretende simplificar esa tarea al máximo. Este programa utiliza como recursos para su funcionamiento una base de datos de mamografías procesadas anteriormente, a partir de las cuales entrena a la red neuronal para que sea capaz de clasificar mamografías nuevas y mostrar las posibles zonas críticas. Esta base de datos debe indicar a la red qué mamografías presentan algún tumor y dónde, para que la red aprenda a diferenciar entre zonas críticas y zonas no críticas. Esta idea deriva en la realización de dos trabajos que se especializan en los dos ámbitos del proyecto, en primer lugar el procesamiento y el análisis de esas mamografías obtenidas de la máquina de rayos X, que da lugar al presente trabajo; y en segundo lugar, deriva en un trabajo paralelo que explica la obtención, el análisis y la clasificación de los datos que se desprenden de este proyecto utilizando redes neuronales, titulado “Detección y clasificación de tumores en mamografías a través de redes neuronales”; realizado por Rodrigo Culotta López