Caracterização elementar de ligas metálicas em implantes dentários

An ideal biomaterial for dental implants must have very high biocompatibility, which means that such materials should not provoke any serious adverse tissue response. Also, used metal alloys must have high fatigue resistance due the masticatory force and good corrosion resistance. These properties are rendered by using alpha and beta stabilizers, such as Al, V, Ni, Fe, Cr, Cu, Zn. Commercially pure titanium (TiCP) is used often for dental and orthopedic implants manufacturing. However, sometimes other alloys are employed and consequently it is essential to research the chemical elements present in those alloys that could bring prejudice for the health. Present work investigated TiCP metal alloys used for dental implant manufacturing and evaluated the presence of stabilizing elements within existing limits and standards for such materials. For alloy characterization and identification of stabilizing elements it was used EDXRF technique. This method allows to perform qualitative and quantitative analysis of the materials using the spectra of the characteristic X-rays emitted by the elements present in the metal samples. The experimental setup was based on two X- rays tubes (AMPTEK Mini X model with Ag and Au targets), a X-123SDD detector (AMPTEK) and a 0.5mm Cu collimator, developed due to the sample characteristics. The other experimental setup used as a complementary technique is composed of an X-ray tube with a Mo target, collimator 0.65mm and XFlash (SDD) detector - ARTAX 200 (BRUKER). Other method for elemental characterization by energy dispersive spectroscopy (EDS) applied in present work was based on Scanning Electron Microscopy (SEM) EVO® (Zeeis). This method also was used to evaluate the surface microstructure of the sample. The percentual of Ti obtained in the elementary characterization was among 93.35 ± 0.17% and 95.34 ± 0.19 %. These values are considered below the reference limit of 98.635% to 99.5% for TiCP, established by Association of metals centric materials engineers and scientists Society (ASM). The presence of elements Al and V in all samples also contributed to underpin the fact that are not TiCP implants. The values for Al vary between 6.3 ± 1.3% and 3.7 ± 2.0% and for V, between 0.26 ± 0.09% and 0.112 ± 0.048%. According to the American Society for Testing and Materials (ASTM), these elements should not be present in TiCP and in accordance with the National Institute of Standards and Technology (NIST), the presence of Al should be <0.01% and V should be of 0.009 ± 0.001%. Obtained results showed that implant materials are not exactly TiCP but, were manufactured using Ti-Al-V alloy, which contained Fe, Ni, Cu and Zn. The quantitative analysis and elementary characterization of experimental results shows that the best accuracy and precision were reached with X-Ray tube with Au target and collimator of 0.5 mm. Use of technique of EDS confirmed the results of EDXRF for Ti-Al-V alloy. Evaluating the surface microstructure by SEM of the implants, it was possible to infer that ten of the thirteen studied samples are contemporaneous, rough surface and three with machined surface.

Desenvolvimento e caracterização de micropartículas de amido reticuladas com agente fosfatado e avaliação da adsorção do azul de metileno

Starch has properties that make it one of the most studied biopolymers today. It is biodegradable, biocompatible, stable and non-toxic. This work has synthesis of starch and tapioca microparticles, through chemical modification by crosslinking with sodium tripolyphosphate agent in concentrations 7.5 and 15% (m / m). The amylose content was measured for starch and commercial cassava starch at 21.8% and 28.6%, respectively. According to the solubility index, processing in basic medium does not change the solubility of the material, but the addition of crosslinking agent increases this index, which changed from 12.8% for the control unprocessed, to 22.4% for the A5R15 sample. Soluble starch-based materials had a significant increase in the crosslinking density by increasing the concentration of crosslinker, from 1.4 in A5R7,5 sample, to 1.9 in A5R15. The cassava starch-based materials exhibited an opposite behavior: to increase the concentration of crosslinker crosslinking density decreased significantly in F5R7.5 from 2.9, to 1.9 in F5R15 sample. The point of zero charge (PZC) shows that below pH 4 the surface is positively charged. The surface area data is between 3,04 and 1,15 m2.g-1. The pore volume between 2.94 and 1.33 cm3.g-1 and pore size around 1.5 nm. The SEM indicates uneven distribution of microparticles, which are smooth, with no ridges. The maximum adsorption capacity of the materials were tested at pH 7.7 and for A5R15 and CA sample, at pH 2, 5, 6 and 9. It is noted that the processing in basic medium reduces the adsorption capacity of CA and CF in respect fo A and F. The adsorption in A5R15 sample has great dependency on the pH, reaching a value of 587 μg.g-1 in pH 7.7. The samples A5R15 and F5R7,5 adsorbed similar amounts, according to the statistical analysis, and significantly higher than their respective controls and showed lower desorption, indicating that the modification process was effective to control the release of methylene blue. The infrared spectra not show the characteristic bands of the phosphate bonds to the material formed, however, developments in hydroxyl characteristic band suggest modification in the way this group was linked after the reaction. After adsorption, the infrared spectra show different format in the band of hydroxyl. PCA analysis shows that the greatest changes observed in the IR spectra are observed in the region of 3500 cm-1. Thermal analysis showed three thermal events related to dehydration and material degradation. It is observed that the processing increases the temperature to the first mass loss, fixed at 12%, but not observed increased stability due to the presence of crosslinker or process.

Caracterização do ciclo da marcha em amputado transtibial com prótese inteligente

This work presents an application of optical fiber sensors based on Bragg gratings integrated to a transtibial prosthesis tube manufactured with a polymeric composite systrem of epoxy resin reinforced with glass fiber. The main objective of this study is to characterize the sensors applied to the gait cycle and changes in the gravity center of a transtibial amputee, trough the analysis of deformation and strengh of the transtibial prosthesis tube. For this investigation it is produced a tube of the composite material described above using the molding method of resin transfer (RTM) with four optical sensors. The prosthesis in which the original tube is replaced is classified as endoskeletal, has vacuum fitting, aluminium conector tube and carbon fiber foot cushioning. The volunteer for the tests was a man of 41 years old, 1.65 meters tall, 72 kilograms and left-handed. His amputation occurred due to trauma (surgical section is in the medial level, and was made below the left lower limb knee). He has been a transtibial prosthesis user for two years and eight months. The characterization of the optical sensors and analysis of mechanical deformation and tube resistance occurred through the gait cycle and the variation of the center of gravity of the body by the following tests: stand up, support leg without the prosthesis, support in the leg with the prosthesis, walk forward and walk backward. Besides the characterization of optical sensors during the gait cycle and the variation of the gravity center in a transtibial amputated, the results also showed a high degree of integration of the sensors in the composite and a high mechanical strength of the material.