Evaluation of molecular weight of Chitosan in thin-layer and spouted bed drying

Chitosan is chitin in deacetylated form and is the main constituent of crustacean exoskeletons. Commercially, chitosan is dried in tray driers, and during the operation, polymerization may occur as the chitosan is composed of carbohydrates. The aim of this work was to analyze chitosan in spouted bed and thin-layer drying, considering viscosity average molecular weight of the chitosan samples in the process. Results showed that spouted bed-dried chitosan presented a molecular weight value similar (160 kDa) to that of the raw one (150 kDa). However, when dried on tray dryers, the molecular weight was 300 kDa, indicating that molecule polymerization occurred.

Use of Spirulina platensis micro and nanoparticles for the removal synthetic dyes from aqueous solutions by biosorption

In this research, micro and nanoparticles of Spirulina platensis dead biomass were obtained, characterized and employed to removal FD&C red no. 40 and acid blue 9 synthetic dyes from aqueous solutions. The effects of particle size (micro and nano) and biosorbent dosage (from 50 to 750 mg) were studied. Pseudofirst order, pseudo-second order and Elovich models were used to evaluate the biosorption kinetics. The biosorption nature was verified using energy dispersive X-ray spectroscopy (EDS). The best results for both dyes were found using 250 mg of nanoparticles, in these conditions, the biosorption capacities were 295 mg g−1 and 1450 mg g−1, and the percentages of dye removal were 15.0 and 72.5% for the FD&C red no. 40 and acid blue 9, respectively. Pseudo-first order model was the more adequate to represent the biosorption of both dyes onto microparticles, and Elovich model was more appropriate to the biosorption onto nanoparticles. The EDS results suggested that the dyes biosorption onto microparticles occurred mainly by physical interactions, and for the nanoparticles, chemisorption was dominant.

Influence of the cutting edge micro-geometry of PCBN tools on the flank wear in orthogonal quenched and tempered turning M2 steel

Quenched and tempered high-speed steels obtained by powder metallurgy are commonly used in automotive components, such as valve seats of combustion engines. In order to machine these components, tools with high wear resistance and appropriate cutting edge geometry are required. This work aims to investigate the influence of the edge preparation of polycrystalline cubic boron nitride (PCBN) tools on the wear behavior in the orthogonal longitudinal turning of quenched and tempered M2 high-speed steels obtained by powder metallurgy. For this research, PCBN tools with high and low-CBN content have been used. Two different cutting edge geometries with a honed radius were tested: with a ground land (S shape) and without it (E shape). Also, the cutting speed was varied from 100 to 220 m/min. A rigid CNC lathe was used. The results showed that the high-CBN, E-shaped tool presented the longest life for a cutting speed of 100 m/min. High-CBN tools with a ground land and honed edge radius (S shaped) showed edge damage and lower values of the tool’s life. Low-CBN, S-shaped tools showed similar results, but with an inferior performance when compared with tools with high CBN content in both forms of edge preparation.