Use of Spirulina platensis micro and nanoparticles for the removal synthetic dyes from aqueous solutions by biosorption

In this research, micro and nanoparticles of Spirulina platensis dead biomass were obtained, characterized and employed to removal FD&C red no. 40 and acid blue 9 synthetic dyes from aqueous solutions. The effects of particle size (micro and nano) and biosorbent dosage (from 50 to 750 mg) were studied. Pseudofirst order, pseudo-second order and Elovich models were used to evaluate the biosorption kinetics. The biosorption nature was verified using energy dispersive X-ray spectroscopy (EDS). The best results for both dyes were found using 250 mg of nanoparticles, in these conditions, the biosorption capacities were 295 mg g−1 and 1450 mg g−1, and the percentages of dye removal were 15.0 and 72.5% for the FD&C red no. 40 and acid blue 9, respectively. Pseudo-first order model was the more adequate to represent the biosorption of both dyes onto microparticles, and Elovich model was more appropriate to the biosorption onto nanoparticles. The EDS results suggested that the dyes biosorption onto microparticles occurred mainly by physical interactions, and for the nanoparticles, chemisorption was dominant.

Evaluation of molar weight and deacetylation degree of chitosan during chitin deacetylation reaction: Used to produce biofilm

Chitosan is a polysaccharide derived from chitin, mainly of crustacean shells and shrimp wastes. The utilization of chitosan is related to the molar weight and deacetylation degree of the biopolymer. The aim of this work is to study the chitin deacetylation reaction, by the viscosity average molar weight and deacetylation degree of chitosan as a function of reaction time. Deacetylation was carried out in concentrated alkaline solution, 421 g L−1, at 130◦C and the reaction occurred during 4 h. Chitosan paste obtained after 20, 90 and 240 min was used to produce biofilms, which were characterized according water vapor permeability and mechanical properties (tensile strength and percentage tensile elongation at break). During the reaction time deacetylation degree reached 93%, and a 50% reduction in the viscosity average molar weight value in relation to the value of the first 20 min of reaction was found Both reactions presented a kinetic behavior of the pseudo-first order. Biofilm produced from the paste of chitosan with high deacetylation degree showed higher water vapor permeability (WVP), tensile strength (TS) and elongation (E) when compared to films with a low deacetylation.

Adsorption of food dyes onto chitosan: Optimization process and kinetic

Adsorption of food dyes acid blue 9 and food yellow 3 onto chitosan was optimized. Chitosan was obtained from shrimp wastes and characterized.Afull factorial design was used to analyze the effects of pH, stirring rate and contact time in adsorption capacity. In the optimal conditions, adsorption kinetics was studied and the experimental data were fitted with three kinetic models. The produced chitosan showed good characteristics for dye adsorption. The optimal conditions were: pH 3, 150rpm and 60 min for acid blue 9 and pH 3, 50rpm and 60 min for food yellow 3. In these conditions, the adsorption capacities values were 210mgg−1 and 295mgg−1 for acid blue 9 and food yellow 3, respectively. The Elovich kinetic model was the best fit for experimental data and it showed the chemical nature of dyes adsorption onto chitosan.