Poly(vinyl alcohol) with sulfonic acid groups as catalyst for the alpha-pinene alkoxylation

The alkoxylation of a-pinene was carried out over poly(vinyl alcohol) containing sulfonic acid groups, as catalyst. The main product of a-pinene alkoxylation was a-terpinyl methyl ether being also formed bornyl methyl ether, fenchyl methyl ether, limonene and terpinolene as by-products. The absorption band at 1037 cm-1 in the FTIR spectrum of PVA_SSA40 (PVA membrane containing 40% of –OH groups esterified with SSA) which does not appear in the spectrum of PVA, indicates the presence of the sulfonic acid groups. The catalytic activity of PVA with sulfonic acid groups increases when the amount of sulfosuccinic acid used in the polymer crosslinking is increased from 5% to 40%. However, when the crosslinking degree increases from 20% to 40%, the conversion of a-pinene increases only slightly. Good values of selectivity to a-terpinyl methyl ether were obtained over poly(vinyl alcohol) with sulfonic acid groups. A simple kinetic model, which fits experimental concentration data quite well, was developed.

Long term performance evaluation of small-diameter vascular grafts based on polyvinyl alcohol hydrogel and dextran and MSCs-based therapies using the ovine pre-clinical animal model.

The functional and structural performance of a 5 cm synthetic small diameter vascular graft (SDVG) produced by the copolymerization of polyvinyl alcohol hydrogel with low molecular weight dextran (PVA/Dx graft) associated to mesenchymal stem cells (MSCs)-based therapies and anticoagulant treatment with heparin, clopidogrel and warfarin was tested using the ovine model during the healing period of 24 weeks. The results were compared to the ones obtained with standard expanded polyetetrafluoroethylene grafts (ePTFE graft). Blood flow, vessel and graft diameter measurements, graft appearance and patency rate (PR), thrombus, stenosis and collateral vessel formation were evaluated by B-mode ultrasound, audio and color flow Doppler. Graft and regenerated vessels morphologic evaluation was performed by scanning electronic microscopy (SEM), histopathological and immunohistochemical analysis. All PVA/Dx grafts could maintain a similar or higher PR and systolic / diastolic laminar blood flow velocities were similar to ePTFE grafts. CD14 (macrophages) and α-actin (smooth muscle) staining presented similar results in PVA/Dx/MSCs and ePTFE graft groups. Fibrosis layer was lower and endothelial cells were only detected at graft-artery transitions where it was added the MSCs. In conclusion, PVA/Dx graft can be an excellent scaffold candidate for vascular reconstruction, including clinic mechanically challenging applications, such as SDVGs, especially when associated to MSCs-based therapies to promote higher endothelialization and lower fibrosis of the vascular prosthesis, but also higher PR values.