Evaluation of portable Raman spectroscopy and handheld X-ray fluorescence analysis (hXRF) for the direct analysis of glyptics

In archaeometry, the advantages of a combined use of Raman spectroscopy and X-ray fluorescence spectroscopy are extensively discussed for applications such as the analysis of paintings, manuscripts, pottery, etc. Here, we demonstrate for the first time the advantage of using both techniques for analysing glyptics. These engraved gemstones or glass materials were originally used as stamps, to identify the owner, for instance on letters, but also on wine vessels. For this research, a set of 64 glyptics (42 Roman glass specimens and 22 modern ones), belonging to the collection of the museum ‘Quinta das Cruzes’ in Funchal (Madeira, Portugal), was analysed with portable Raman spectroscopy and handheld X-ray fluorescence (hXRF). These techniques were also used to confirm the gemological identification of these precious objects and can give extra information about the glass composition. Raman spectroscopy identifies the molecular composition as well as on the crystalline phases present. On the other hand, hXRF results show that the antique Roman glass samples are characterised with low Pb and Sn levels and that the modern specimens can be discriminated in two groups: lead-based and non-lead-based ones.

Detection of Glass pattern configurations by the primary visual cortex

The neurons in the primary visual cortex that respond to the orientation of visual stimuli were discovered in the late 1950s (Hubel, D.H. & Wiesel, T.N. 1959. J. Physiol. 148:574-591) but how they achieve this response is poorly understood. Recently, experiments have demonstrated that the visual cortex may use the image processing techniques of cross or auto-correlation to detect the streaks in random dot patterns (Barlow, H. & Berry, D.L. 2010. Proc. R. Soc. B. 278: 2069-2075). These experiments made use of sinusoidally modulated random dot patterns and of the so-called Glass patterns - where randomly positioned dot pairs are oriented in a parallel configuration (Glass, L. 1969. Nature. 223: 578-580). The image processing used by the visual cortex could be inferred from how the threshold of detection of these patterns in the presence of random noise varied as a function of the dot density in the patterns. In the present study, the detection thresholds have been measured for other types of patterns including circular, hyperbolic, spiral and radial Glass patterns and an indication of the type of image processing (cross or auto-correlation) by the visual cortex is presented. As a result, it is hoped that this study will contribute to an understanding of what David Marr called the ‘computational goal’ of the primary visual cortex (Marr, D. 1982. Vision: A Computational Investigation into the Human Representation and Processing of Visual Information. New York: Freeman.)

Characterization of medieval glass artefacts from Miranduolo site, Chiusdino, Italy

This archaeovitreological study deals with artefacts of Miranduolo site, Tuscany region (Italy), dated 1250-1350 AD. The Miranduolo site is a medieval hill-village dated from 7th to 14th century. The information obtained reveal that Miranduolo was under control of noble families, which displayed the social, economic and political power. It is marked by controlling the farmers and metal workers on the site, as well as having control over agricultural surpluses. No in situ glass workshop has been recovered, implying that the glass artefacts were imported. One aim of this work is application of SEM-EDS to visualize textural characteristics and thickness of the pristine glass and corrosion layers. Preliminary qualification and semi-quantification of major and minor chemical elements will provide the data on the glass group present and fluxes employed. The data obtained will be integrated with the one obtained by more sensitive techniques such as PIXE/PIGE and LA-ICP-MS. Twenty cross-sections of transparent glasses (colorless, azure, and different hues of yellow and) have been analyzed by VP-SEM. All the analyzed glasses display a homogenous matrix. Only four samples (MD 24, MD 139, MD 143, MD 259) show corrosion layers of various thickness with 2.25μm, 136-500 μm, 26.8 μm and 17.01 μm. EDS linescan analyses indicate strong depletion in the corrosion layers of Na and K, while Ca depletes to a minor extent. In general, both glass composition and the burial conditions were favorable for preservation. Samples can be classified as mainly plant ash Na-Ca-Si glasses made with both unpurified and purified Levantine ash. Only sample MD 243 is made from Barilla plant ash. Sample MD 139 cannot be classified into main compositional groups as K2O is 1.33 wt% and MgO 5.92 wt%. In 8 samples MnO content is lower than 0.8 wt%, meaning that in these samples MnO is naturally present. In other 12 samples, MnO above 0.8 wt% indicates deliberate addition as a decolorant agent to intentionally obtain different hues or the amount added was not successful in making the glass transparent. The results considering fluxes are compatible with archaeovitreological study from contemporary primary glass workshops in Tuscany. For determining the provenance of silica sources, further analysis with more sensitive techniques has to be carried out; Resumo: Este estudo “arqueovitreologia” lida com artefatos do local Miranduolo, região da Toscana (Itália), datados de 1250-1350 AD. O sitio de Miranduolo é uma colina vila medieval datada do séc.VII ao séc.XIV. As informações obtidas revelam que Miranduolo estava sob o controle de famílias nobres, que exibiu o poder social, económico e político. É marcado por controlar os agricultores e trabalhadores do metal no sitio, bem como ter controlo sobre os excedentes agrícolas. Não há na oficina de vidro in situ foi recuperado, o que implica que os artefactos de vidro foram importados. Um dos objetivos deste trabalho é a aplicação de SEM-EDS para visualizar características de textura e espessura das camadas de corrosão do vidro também como da áreas originais. qualificação preliminar e semi-quantificação de maiores e menores elementos químicos irá fornecer os dados sobre o grupo presente vidro e fluxos empregado. Os dados obtidos são integrados com os dados obtidos por meio de técnicas mais sensíveis, como PIXE / PIGE e LA-ICP-MS. Vinte secções transversais de vidros transparentes (incolor, azul celeste, e diferentes tons de amarelo) foram analisados por VP-SEM. Todos os vidros analisados exibir uma matriz homogénea. Apenas quatro amostras (MD 24, MD 139, MD 143, MD 259) mostram camadas de corrosão de várias espessuras com 2.25μm, 136-500μm, 26,8μm e 17,01μm. Análises Linescan EDS indicam forte esgotamento nas camadas de corrosão de Na e K, enquanto Ca esgota, em menor grau. Em geral, tanto a composição de vidro e as condições de depósito foram favoráveis para a preservação. As amostras podem ser classificados como vidros principalmente Na-Ca-Si feitas com cinzas de plantas do tipo levantino, não purificada e purificada. Apenas a amostra MD 243 é feita a partir de cinzas vegetais tipo “Barilla”. A amostra MD 139 não pode ser classificada em grupos principais de composição porque K2O é 1,33% em peso e MgO 5,92% em peso. Em 8 amostras, o teor de MnO é menor do que 0,8% em peso, o que significa que nestas amostras MnO está naturalmente presente. Em outras 12 amostras, MnO acima de 0,8% em peso indica adição intencional como um agente de colorante para obter intencionalmente diferentes matizes ou o valor acrescentado não foi bem sucedido em fazer o vidro transparente. Os resultados, considerando os fluxos são compatíveis com o estudo “arqueovitreologico” com as principais oficinas de vidro contemporâneos na Toscana. Para determinar a origem das fontes de sílica, uma análise mais aprofundada com técnicas mais sensíveis tem de ser levada a cabo.