Identification of copper species present in Cu-ZSM-5 catalysts for NOx reduction

The structure of Cu-ZSM-5 catalysts that show activity for direct NO decomposition and selective catalytic reduction of NOx by hydrocarbons has been investigated by a multitude of modern surface analysis and spectroscopy techniques including X-ray photoelectron spectroscopy, thermogravimetric analysis, and in situ Fourier transform infrared spectroscopy. A series of four catalysts were prepared by exchange of Na-ZSM-5 with dilute copper acetate, and the copper loading was controlled by variation of the solution pH. Underexchanged catalysts contained isolated Cu2+OH-(H2O) species and as the copper loading was increased Cu2+ ions incorporated into the zeolite lattice appeared. The sites at which the latter two copper species were located were fundamentally different. The Cu2+OH-(H2O) moieties were bound to two lattice oxygen ions and associated with one aluminum framework species. In contrast, the Cu2+ ions were probably bound to four lattice oxygen ions and associated with two framework aluminum ions. Once the Cu-ZSM-5 samples attained high levels of exchange, the development of [Cu(μ-OH)2Cu]n2+OH-(H2O) species along with a small concentration of Cu(OH)2 was observed. On activation in helium to 500°C the Cu2+OH-(H2O) species transformed into Cu2+O- and Cu+ moieties, whereas the Cu2+ ions were apparently unaffected by this treatment (apart from the loss of ligated water molecules). Calcination of the precursors resulted in the formation of Cu2+O2- and a one-dimensional CuO species. Temperature-programmed desorption studies revealed that oxygen was removed from the latter two species at 407 and 575°C, respectively. © 1999 Academic Press.

Spectroscopic investigation of the polymerisation of pyrrole and thiophene within zeolite channels

The reaction of pyrrole and thiophene monomers with copper- or nickel-exchanged mordenite has been investigated using X-ray photoelectron (XPS) and photoacoustic infrared (PAIRS) spectroscopies. Because of the differing oxidising powers of the cations studied, polymerisation occurred only with copper-exchanged mordenite. PAIRS and XPS data indicated that both polypyrrole and polythiophene were partially oxidised when synthesised within the zeolite structure. IR spectra of polythiophene and polythiophene and polypyrrole showed intense bands typical of ring vibrations which could couple to the large dipole change induced by charges moving along the polythiophene chain. In addition it was noted that only vibrations typical of oxidised polymer structures were recorded, suggesting that the charge carrier was located within these segments. Furthermore, N 1s spectra contained a high binding energy peak at 402.5 eV which was attributed to a positively charged nitrogen species, in agreement with IR data. Significantly, C 1s spectra confirmed that molecular wires were formed within the confines of the zeolite lattice. Depth-profiling experiments suggested that polypyrrole was distributed throughout the entire zeolite host. By contrast, polythiophene may have been restricted to the uppermost zeolite channels owing to the ability of sulfur species to bond to CuI sites [produced by reduction of copper(II) ions during the polymerisation process], thus obstructing movement along the channels.

Practical applications for clay-derived zeolite N : an ammonium-selective ion exchanger for industry use

Over the past ten years, scaled-up utilisation of a previously under-exploited zeolite, Zeolite N1, has been demonstrated for selective ion exchange of ammonium and other ions in aqueous environments. As with many zeolite syntheses, the required source material should contain predictable levels of aluminium and silicon and, for full-scale industrial applications, kaolin and/or montmorillonite serve such a purpose. Field, pilot and commercial scale trials of kaolin-derived Zeolite N have focused on applications in agriculture and water treatment as these sectors are primary producers or users of ammonium. The format for the material – as fine powders, granules or extrudates – depends on the specific application albeit each has been evaluated.

A vibrational spectroscopic study of the silicate mineral analcime – Na2(Al4SiO4O12)·2H2O : a natural zeolite

We have studied the mineral analcime using a combination of scanning electron microscopy with energy dispersive spectroscopy and vibrational spectroscopy. The mineral analcime Na2(Al4SiO4O12)·2H2O is a crystalline sodium silicate. Chemical analysis shows the mineral contains a range of elements including Na, Al, Fe2+ and Si. The mineral is characterized by intense Raman bands observed at 1052, 1096 and 1125 cm−1. The infrared bands are broad; nevertheless bands may be resolved at 1006 and 1119 cm−1. These bands are assigned to SiO stretching vibrational modes. Intense Raman band at 484 cm−1 is attributed to OSiO bending modes. Raman bands observed at 2501, 3542, 3558 and 3600 cm−1 are assigned to the stretching vibrations of water. Low intensity infrared bands are noted at 3373, 3529 and 3608 cm−1. The observation of multiple water bands indicate that water is involved in the structure of analcime with differing hydrogen bond strengths. This concept is supported by the number of bands in the water bending region. Vibrational spectroscopy assists with the characterization of the mineral analcime.

Raman spectroscopic characteristics of phthalocyanine and naphthalocyanine in sandwich-type phthalocyaninato and porphyrinato rare earth complexes Part 5. – Raman spectroscopic characteristics of naphthalocyanine in mixed [tetrakis(4-tert-butylphenyl)porphyrinato]-(naphthalocyaninato) rare earth double-deckers

Raman spectra were recorded in the range 400–1800 cm−1 for a series of 15 mixed \[tetrakis(4-tert-butylphenyl)porphyrinato](2,3-naphthalocyaninato) rare earth double-deckers M(TBPP)(Nc) (M = Y; La–Lu except Pm) using laser excitation at 632.8 and 785 nm. Comparisons with bis(naphthalocyaninato) rare earth counterparts reveal that the vibrations of the metallonaphthalocyanine M(Nc) fragment dominate the Raman features of M(TBPP)(Nc). When excited with radiation of 632.8 nm, the most intense vibration appears at about 1595 cm−1, due to the naphthalene stretching. These complexes exhibit the marker Raman band for Nc•− as a medium-intense band in the range 1496–1507 cm−1, attributed to the coupling of pyrrole and aza stretching, while the marker Raman band of Nc2− in intermediate-valence Ce(TBPP)(Nc) appears as a strong band at 1493 cm−1 and is due to the isoindole stretchings. By contrast, when excited with radiation of 785 nm that is in close resonance with the main Q absorption band of the naphthalocyanine ligand, the ring radial vibrations at ca 680 and 735 cm−1 for MIII(TBPP)(Nc) are selectively intensified and are the most intense bands. For the cerium double-decker, the most intense vibration also acting as the marker Raman band of Nc2− appears at 1497 cm−1 with contributions from both pyrrole CC and aza CN stretches. The same vibrational modes show weak to medium intensity scattering at 1506–1509 cm−1 for MIII(TBPP)(Nc) and this is the marker Raman band of Nc•− when thus excited. The scatterings due to the Nc breathings, ring radial vibration, aza group stretchings, naphthalene stretchings, benzoisoindole stretchings and the coupling of pyrrole CC and aza CN stretchings in MIII(TBPP)(Nc) are all slightly blue shifted along with the decrease in rare earth ionic radius, confirming the effects of increased ring–ring interactions on the Raman characteristics of naphthalocyanine in the mixed ring double-deckers.