The effects of sintering profiles on the resistance and flatness of transparent conducting oxide substrates for DSC

The effects of sintering on several properties of FTO and ITO substates used in DSC have been investigated. FTO & ITO substrates were prepared with a range of sizes and aspect ratios - emulated laboratory style test cells through to prototype modules. Time and temperature of the sintering profiles were varied and sheet resistance and flatness measured. Electrical properties of the substrates were then further characterized by electrochemical impedance spectroscopy, and module sized devices were assembled and thickness variations over the device area were determined and related to performance.

Ultrafast near infrared sintering of TiO2 layers on metal substrates for dye-sensitized solar cells

A limiting step to roll-to-roll production of dye-sensitized solar cells on metals is TiO2 sintering (10-30 min). Near infrared (NIR) heating is a novel process innovation which directly heats titanium substrates giving rapid binder removal and sintering. NIR heating (for 12.5 s) at varying power gave titanium temperatures of 545, 685 and 817 degrees Celsius yielding cells with efficiencies of 2.9, 2.8 and 2.5%. Identical cells prepared in a conventional oven (1800 s) at 500, 600 and 800 degrees Celsius gave 2.9, 2.6 and 0.2% efficiency. NIR sintering is ultrafast and has a wide process window making it ideal for rapid manufacturing on metals.

Flammability and Sensitivity of Materials in Oxygen-Enriched Atmospheres : 13th Volume

"Seventeen peer-reviewed papers cover the latest research on the ignition and combustion of metals and non-metals, oxygen compatibility of components and systems, analysis of ignition and combustion, failure analysis and safety. It includes aerospace, military, scuba diving, and industrial oxygen applications. Topics cover: • Development of safe oxygen systems • Ignition mechanisms within oxygen systems and how to avoid them • Specific hazards that exist with the oxygen mixture breathed by divers in the scuba industry • Issues related to oxygen system level safety • Issues related to oxygen safety in breathing systems • Detailed investigations and discussions related to the burn curves that have been generated for metals that are burning in a standard test fixture This new publication is a valuable resource for professionals in the air separation industries, oxygen manufacturers, manufacturers of materials intended for oxygen service, and users of oxygen and oxygen-enriched atmospheres, including aerospace, medical, industrial gases, chemical processing, steel and metals refining, as well as to military, commercial or recreational diving."--- publisher website

Sintering and densification mechanisms of Y2BaCuO5 pellets

The sintering and densification of Y2BaCuO5 (Y-211) pellets made from powders with different characteristics have been investigated in the temperature range 1000-1140°C. A pellet made from powder containing Ba-rich secondary phases shows very early liquid-assisted sintering and densification and clear evidence of exaggerated grain growth. The melting of BaCuO2 and YBa2Cu3O7-δ (Y-123) secondary phases increases the rate of densification of Y-211 pellets made from other powders at temperatures above 1025-1030°C. All the liquid produced by the melting of the latter phases recrystallizes as intergranular layers of Y-123. These intergranular layers account for the darker appearance and for measurable electrical conductivities at room temperature of the pellets sintered at the higher temperatures. The development of exaggerated grain growth within a uniform fine-grained matrix opens the possibility of using controlled secondary recrystallization to obtain large single domains of Y-211, provided that the trapping of porosity can be avoided or minimized. © 1999 Elsevier Science S.A.

Atmospheres : Aesthetics of emotional spaces[Review]

More problematic than his avoidance of recent geographic scholarship is his treatment of indigenous, ethnographic and postcolonial perspectives on island life. Not only is much of this scholarship absent, the bits that are there are mostly derided. He slams Kamau Braithwaite and his concept of ‘tidalectics’ as ‘unpackable’ (p. 20) and also claims that Greg Dening’s approach to islands as having ‘permeable cultural boundaries’ has ‘intellectual costs’ (p. 23). In a section of the book on ‘Naming and Sovereignty’, instead of an in-depth examination of the processes of decoding and recoding that goes on in indigenous island landscapes under colonialism (as could be discussed at length if Shell chose to examine Aotearoa, Hawaii, or hundreds of other places) we are instead presented a vignette about his childhood street fights with other kids over the naming of a hometown island in Canada, as well as ruminations about what Herman Melville and Ellen Semple thought of islands in the nineteenth century. In short, if you want to know what dead Caucasians like Shakespeare, Melville, Kant, Mackinder, More, and ancient Athenians thought about islands, then this book is a good resource. If, however, you are looking for information about what islands are like today – and what they mean to the people who live on and interact with them – then you will have to look elsewhere.

Lowering grain boundary resistance of BaZr0.8Y0.2O3−δ with LiNO3 sintering-aid improves proton conductivity for fuel cell operation

A novel sintering additive based on LiNO3 was used to overcome the drawbacks of poor sinterability and low grain boundary conductivity in BaZr0.8Y0.2O3-δ (BZY20) protonic conductors. The Li-additive totally evaporated during the sintering process at 1600°C for 6 h, which led to highly dense BZY20 pellets (96.5% of the theoretical value). The proton conductivity values of BZY20 with Li sintering-aid were significantly larger than the values reported for BZY sintered with other metal oxides, due to the fast proton transport in the "clean" grain boundaries and grain interior. The total conductivity of BZY20-Li in wet Ar was 4.45 × 10-3 S cm-1 at 600°C. Based on the improved sinterability, anode-supported fuel cells with 25 μm-thick BZY20-Li electrolyte membranes were fabricated by a co-firing technique. The peak power density obtained at 700°C for a BZY-Ni/BZY20-Li/La0.6Sr0.4Co0.2Fe 0.8O3-δ (LSCF)-BZY cell was 53 mW cm-2, which is significantly larger than the values reported for fuel cells using electrolytes made of BZY sintered with the addition of ZnO and CuO, confirming the advantage of using Li as a sintering aid.

Tailoring texture of γ-Y2Si2O7 by strong magnetic field alignment and two-step sintering

In this study, a well-dispersed γ-Y2Si2O 7 ethanol-based suspension with 30 vol% solid loading was prepared by adding 1 dwb% polyethylene imine dispersant, which allows feeble magnetic γ-Y2Si2O7 particles with anisotropic magnetic susceptibility to rotate in a 12 T strong magnetic field during slip casting, resulting in the development of a strong texture in green bodies. Pressureless sintering gives rise to more pronounced grain growth in the textured sample than in the untextured sample prepared without the magnetic field due to the rapid migration of the grain boundaries of the well-oriented grains, which was revealed by constant-heating-rate sintering kinetics. It was found that the use of two-step sintering is very efficient not only for inhibiting the grain growth but also for enhancing the texture. This implies that controlled grain growth is crucial for enhancing texture development in γ-Y2Si2O7.

Effect of LiYO2 on the synthesis and pressureless sintering of Y2SiO5

Y2SiO5 has potential applications as a high-temperature structural ceramic and environmental/thermal barrier coating. In this work, we synthesized single-phase Y2SiO5 powders utilizing a solid-liquid reaction method with LiYO2 as an additive. The reaction path of the Y2O3/SiO2/LiYO2 mixture with variation in temperatures and the role of the LiYO2 additive on preparation process were investigated in detail. The powders obtained by this method have good sinterability. Through a pressureless sintering process, almost fully dense Y2SiO5 bulk material was achieved with a very high density of 99.7% theoretical.

Low-temperature synthesis and sintering of γ-Y2Si2O7

In this article, a novel pressureless solid-liquid reaction method is presented for preparation of yttrium disilicate (γ-Y2Si2O7). Single-phase γ-Y2Si2O7 powder was synthesized by calcination of SiO2 and Y2O3 powders with the addition of LiYO2 at 1400 °C for 4 h. The addition of LiYO2 significantly decreased the synthesis temperature, shortened the calcination time, and enhanced the stability of γ-Y2Si2O7. The sintering of these powders in air and O2 was studied by means of thermal mechanical analyzer. It is shown that the γ-Y2Si2O7 sintered in oxygen had a faster densification rate and a higher density than that sintered in air. Furthermore, single-phase γ-Y2Si2O7 with a density of 4.0 g/cm3 (99% of the theoretical density) was obtained by pressureless sintering at 1400 °C for 2 h in oxygen. Microstructures of the sintered samples are studied by scanning electron microscope.

Determination of burn criterion for promoted combustion testing

Promoted ignition testing [1–3] is used to determine the relative flammability of metal rods in oxygen-enriched atmospheres. In these tests, a promoter is used to ignite each metal rod to start the sample burning. Experiments were performed to better understand the promoted ignition test by obtaining insight into the effect a burning promoter has on the preheating of a test sample. Test samples of several metallic materials were prepared and coupled to fast-responding thermocouples along their length. Various ignition promoters were used to ignite the test samples. The thermocouple measurements and test video were synchronized to determine temperature increase with respect to time and length along each test sample. A recommended length of test sample that must be consumed to be considered a flammable material was determined based on the preheated zone measured from these tests. This length was determined to be 30 mm (1.18 in.). Validation of this length and its rationale are presented.

A review of rapid prototyping techniques for tissue engineering purposes

Rapid prototyping (RP) is a common name for several techniques, which read in data from computer-aided design (CAD) drawings and manufacture automatically threedimensional objects layer-by-layer according to the virtual design. The utilization of RP in tissue engineering enables the production of three-dimensional scaffolds with complex geometries and very fine structures. Adding micro- and nanometer details into the scaffolds improves the mechanical properties of the scaffold and ensures better cell adhesion to the scaffold surface. Thus, tissue engineering constructs can be customized according to the data acquired from the medical scans to match the each patient’s individual needs. In addition RP enables the control of the scaffold porosity making it possible to fabricate applications with desired structural integrity. Unfortunately, every RP process has its own unique disadvantages in building tissue engineering scaffolds. Hence, the future research should be focused into the development of RP machines designed specifically for fabrication of tissue engineering scaffolds, although RP methods already can serve as a link between tissue and engineering.

Heat effects of promoters and determination of burn criterion in promoted combustion testing

Promoted ignition testing (NASA) Test 17) [1] is used to determine the relative flammability of metal rods in oxygen-enriched atmospheres. A promotor is used to ignite a metal sample rod, initiating sample burning. If a predetermined length of the sample burns, beyond the promotor, the material is considered flammable at the condition tested. Historically, this burn length has been somewhat arbitrary. Experiments were performed to better understand this test by obtaining insight into the effect a burning promotor has on the preheating of a test sample. Test samples of several metallic materials were prepared and coupled to fast-responding thermocouples along their length. Thermocouple measurements and test video were synchronized to determine temperature increase with respect to time and length along each test sample. A recommended flammability burn length, based on a sample preheat of 500 degrees fahrenheit, was determined based on the preheated zone measured from these tests. This length was determined to be 30 mm (1.18 in.). Validation of this length and its rationale are presented.