152 resultados para Sharp
em Queensland University of Technology - ePrints Archive
Resumo:
An electropolishing method has been developed for preparing sharp needles from polycrystalline YBa2Cu3O7- by modifying a recipe for TEM specimen preparation. The method is characterized by a polishing temperature of below 0C, a non-acidic electrolyt and an even removal of the constituent phases. An approach was employed of combining I-V measurements for polishing process and microscopical observation of surface morphology in finding optimum polishing conditions. TEM evidenced that no preferential attack appeared to grain boundaries. X-ray diffractometry and electron diffraction implied that no change in oxygen content occurred during electropolishing. The sharpness of the tip was examined by field-ion microscopy.
Resumo:
The molecular structure of the uranyl mineral rutherfordine has been investigated by the measurement of the NIR and Raman spectra and complemented with infrared spectra including their interpretation. The spectra of the rutherfordine show the presence of both water and hydroxyl units in the structure as evidenced by IR bands at 3562 and 3465 cm-1 (OH) and 3343, 3185 and 2980 cm-1 (H2O). Raman spectra show the presence of four sharp bands at 3511, 3460, 3329 and 3151 cm-1. Corresponding molecular water bending vibrations were only observed in both Raman and infrared spectra of one of two studied rutherfordine samples. The second rutherfordine sample studied contained only hydroxyl ions in the equatorial uranyl plane and did not contain any molecular water. The infrared spectra of the (CO3)2- units in the antisymmetric stretching region show complexity with three sets of carbonate bands observed. This combined with the observation of multiple bands in the (CO3)2- bending region in both the Raman and IR spectra suggests that both monodentate and bidentate (CO3)2- units may be present in the structure. This cannot be exactly proved and inferred from the spectra; however, it is in accordance with the X-ray crystallographic studies. Complexity is also observed in the IR spectra of (UO2)2+ antisymmetric stretching region and is attributed to non-identical UO bonds. U-O bond lengths were calculated using wavenumbers of the 3 and 1 (UO2)2+ and compared with data from X-ray single crystal structure analysis of rutherfordine. Existence of solid solution having a general formula (UO2)(CO3)1-x(OH)2x.yH2O ( x, y 0) is supported in the crystal structure of rutherfordine samples studied.
Resumo:
The mixed anion mineral parnauite Cu9[(OH)10|SO4|(AsO4)2].7H2O has been studied by Raman spectroscopy. Characteristic bands associated with arsenate, sulphate, hydroxyl units are identified. Broad bands are observed and are resolved into component bands. Two intense bands at 859 and 830 cm-1 are assigned to the 1 (AsO4)3- symmetric stretching and 3 (AsO4)3- antisymmetric stretching modes. The comparatively sharp band at 976 cm-1 is assigned to the 1 (SO4)2- symmetric stretching mode and a broad spectral profile centered upon 1097 cm-1 is attributed to the 3 (SO4)2- antisymmetric stretching mode. A comparison of the Raman spectra is made with other arsenate bearing minerals such as carminite, clinotyrolite, kankite, tilasite and pharmacosiderite.
Resumo:
The essays in this book catalogue a wide and varied range of instances where 'things go wrong' in the practice of criminal justice. The contributions document instances where laws, policies and practices have produced unintended consequences of the most deleterious kind, drawing attention to 'boot camps', detention centres and specific penal policies such as 'short, sharp shock' and 'three strikes and you're out'. Also examined are policing practices such as 'zero tolerance', 'saturation policing' and punitive laws in the area of drug use, sex offences, and prostitution. It will be demonstrated that in each of these cases, the objectives of government resulted in the creation of new and unforeseen problems requiring further reform to the justice system.
Resumo:
Raman spectra of brandholzite Mg[Sb(OH)6].6H2O were studied, complemented with infrared spectra, and related to the structure of the mineral. An intense Raman sharp band at 618 cm-1 is attributed to the SbO symmetric stretching mode. The low intensity band at 730 cm-1 is ascribed to the SbO antisymmetric stretching vibration. Low intensity Raman bands were found at 503, 526 and 578 cm-1. Corresponding infrared bands were observed at 527, 600, 637, 693, 741 and 788 cm-1. Four Raman bands observed at 1043, 1092, 1160 and 1189 cm-1 and eight infrared bands at 963, 1027, 1055, 1075, 1108, 1128, 1156 and 1196 cm-1 are assigned to SbOH deformation modes. A complex pattern resulting from the overlapping band of the water and hydroxyl units is observed. Raman bands are observed at 3240, 3383, 3466, 3483 and 3552 cm-1, infrared bands at 3248, 3434 and 3565 cm-1. The first two Raman bands and the first infrared band are assigned to water stretching vibrations. The two higher wavenumber Raman bands observed at 3466 and 3552 cm-1 and two infrared bands at 3434 and 3565 cm-1 are assigned to the stretching vibrations of the hydroxyl units. Observed Raman and infrared bands are connected with O-HO hydrogen bonds and their lengths 2.72, 2.79, 2.86, 2.88 and 3.0 (Raman) and 2.73, 2.83 and 3.07 (infrared).
Relative income, happiness, and utility : an explanation for the Easterlin paradox and other puzzles
Resumo:
The well-known Easterlin paradox points out that average happiness has remained constant over time despite sharp rises in GNP per head. At the same time, a micro literature has typically found positive correlations between individual income and individual measures of subjective well-being. This paper suggests that these two findings are consistent with the presence of relative income terms in the utility function. Income may be evaluated relative to others (social comparison) or to oneself in the past (habituation). We review the evidence on relative income from the subjective well-being literature. We also discuss the relation (or not) between happiness and utility, and discuss some nonhappiness research (behavioral, experimental, neurological) related to income comparisons. We last consider how relative income in the utility function can affect economic models of behavior in the domains of consumption, investment, economic growth, savings, taxation, labor supply, wages, and migration.
Resumo:
Raman spectroscopy has been used to study the rare earth mineral churchite-(Y) of formula (Y,REE)(PO4) 2H2O. The mineral contains yttrium and depending on the locality, a range of rare earth metals. The Raman spectra of two churchite-(Y) mineral samples from Jchymov and Medvdn in the Czech Republic were compared with the Raman spectra of churchite-(Y) downloaded from the RRUFF data base. The Raman spectra of churchite-(Y) are characterized by an intense sharp band at 975 cm-1 assigned to the 1 (PO4)3- symmetric stretching mode. A lower intensity band observed at around 1065 cm-1 is attributed to the 3 (PO43-) antisymmetric stretching mode. The (PO43-) bending modes are observed at 497 cm-1 (2) and 563 cm-1(4). Some small differences in the band positions between the four churchite-(Y) samples from four different localities were found. These differences are possible to explain as different compositions of the churchite-(Y) minerals.
Resumo:
Media organizations are simultaneously key elements of an effective democracy and, for the most part, commercial entities seeking success in the market. They play an essential role in the formation of public opinion and the influence on personal choices. Yet most of them are commercial enterprises seeking readers or viewers, advertising, favorable regulatory decisions for their media, and other assets. This creates some intrinsic difficulties and produces some sharp tensions within media ethics. In this article, we examine such tensionsin theory and practice. We then consider the feasibility of introducing an ethics regime to the media industrya regime that would be effective in a deregulated environment in protecting public interest and social responsibility. In the article, we also outline a rationale and a methodology for the institutionalization of an acceptable and workable media ethics regime that aims to protect the integrity of the industry in a future of undoubtedly increasing commercial pressure.
Resumo:
The mineral lewisite, (Ca,Fe,Na)2(Sb,Ti)2O6(O,OH)7 an antimony bearing mineral has been studied by Raman spectroscopy. A comparison is made with the Raman spectra of other minerals including bindheimite, stibiconite and romite. The mineral lewisite is characterised by an intense sharp band at 517 cm-1 with a shoulder at 507 cm-1 assigned to SbO stretching modes. Raman bands of medium intensity for lewisite are observed at 300, 356 and 400 cm-1. These bands are attributed to OSbO bending vibrations. Raman bands in the OH stretching region are observed at 3200, 3328, 3471 cm-1 with a distinct shoulder at 3542 cm-1. The latter is assigned to the stretching vibration of OH units. The first three bands are attributed to water stretching vibrations. The observation of bands in the 3200 to 3500 cm-1 region suggests that water is involved in the lewisite structure. If this is the case then the formula may be better written as Ca, Fe2+, Na)2(Sb, Ti)2(O,OH)7 xH2O.
Resumo:
Free-radical processes underpin the thermo-oxidative degradation of polyolefins. Thus, to extend the lifetime of these polymers, stabilizers are generally added during processing to scavenge the free radicals formed as the polymer degrades. Nitroxide radical precursors, such as hindered amine stabilizers (HAS),1,2 are common polypropylene additives as the nitroxide moiety is a potent scavenger of polymer alkyl radicals (R). Oxidation of HAS by radicals formed during polypropylene degradation yields nitroxide radicals (RRNO), which rapidly trap the polymer degradation species to produce alkoxyamines, thus retarding oxidative polymer degradation. This increase in polymer stability is demonstrated by a lengthening of the induction period of the polymer (the time prior to a sharp rise in the oxidation of the polymer). Instrumental techniques such as chemiluminescence or infrared spectroscopy are somewhat limited in detecting changes in the polymer during the initial stages of degradation. Therefore, other methods for observing polymer degradation have been sought as the useful life of a polymer does not extend far beyond its induction period
Resumo:
Raman spectra of antimonate mineral brizziite NaSbO3 were studied and related to the structure of the mineral. Two sharp bands at 617 and 660 cm-1 are attributed to the SbO3- symmetric stretching mode. The reason for two symmetric stretching vibrations depends upon the bonding of the SbO3- units. The band at 617 cm-1 is assigned to bonding through the Sb and the 660 cm-1 to bonding through the oxygen. The low intensity band at 508 cm-1 is ascribed to the SbO antisymmetric stretching vibration. Low intensity bands were found at 503, 526 and 578 cm-1. Sharp Raman bands observed at 204, 230, 307 and 315 cm-1are assigned to OSbO bending modes. Raman spectroscopy enables a better understanding of the molecular structure of the mineral brizziite.
Resumo:
The transition of cubic indium hydroxide to cubic indium oxide has been studied by thermogravimetric analysis complimented with hot stage Raman spectroscopy. Thermal analysis shows the transition of In(OH)3 to In2O3 occurs at 219C. The structure and morphology of In(OH)3 synthesised using a soft chemical route at low temperatures was confirmed by X-ray diffraction and scanning electron microscopy. A topotactical relationship exists between the micro/nano-cubes of In(OH)3 and In2O3. The Raman spectrum of In(OH)3 is characterised by an intense sharp band at 309 cm-1 attributed to 1 In-O symmetric stretching mode, bands at 1137 and 1155 cm-1 attributed to In-OH deformation modes, bands at 3083, 3215, 3123 and 3262 cm-1 assigned to the OH stretching vibrations. Upon thermal treatment of In(OH)3 new Raman bands are observed at 125, 295, 488 and 615 cm-1 attributed to In2O3. Changes in the structure of In(OH)3 with thermal treatment is readily followed by hot stage Raman spectroscopy.
Resumo:
What does it mean when we design for accessibility, inclusivity and "dissolving boundaries" -- particularly those boundaries between the design philosophy, the software/interface actuality and the stated goals? This paper is about the principles underlying a research project called 'The Little Grey Cat engine' or greyCat. GreyCat has grown out of our experience in using commercial game engines as production environments for the transmission of culture and experience through the telling of individual stories. The key to this endeavour is the potential of the greyCat software to visualize worlds and the manner in which non-formal stories are intertwined with place. The apparently simple dictum of "show, don't tell" and the use of 3D game engines as a medium disguise an interesting nexus of problematic issues and questions, particularly in the ramifications for cultural dimensions and participatory interaction design. The engine is currently in alpha and the following paper is its background story. In this paper we discuss the problematic, thrown into sharp relief by a particular project, and we continue to unpack concepts and early designs behind the greyCat itself.