Iron burning in pressurised oxygen under microgravity conditions

An investigation of cylindrical iron rods burning in pressurised oxygen under microgravity conditions is presented. It has been shown that, under similar experimental conditions, the melting rate of a burning, cylindrical iron rod is higher in microgravity than in normal gravity by a factor of 1.8 ± 0.3. This paper presents microanalysis of quenched samples obtained in a microgravity environment in a 2.0 s duration drop tower facility in Brisbane, Australia. These images indicate that the solid/liquid interface is highly convex in reduced gravity, compared to the planar geometry typically observed in normal gravity, which increases the contact area between liquid and solid phases by a factor of 1.7 ± 0.1. Thus, there is good agreement between the proportional increase in solid/liquid interface surface area and melting rate in microgravity. This indicates that the cause of the increased melting rates for cylindrical iron rods burning in microgravity is altered interfacial geometry at the solid/liquid interface.

Re-melting of Bi-2212/Ag laminated tapes by partial melting process

Bi-2212 tapes are prepared by a combination of dip-coating and partial melt processing. We investigate the effect of re-melting of those tapes by partial melting followed by slow cooling on the structure and superconducting properties. Microstructural studies of re-melted samples show that they have the same overall composition as partially melted tapes. However, the fractional volumes of the secondary phases differ and the amounts and distribution of the secondary phases have a significant effect on the critical current. Critical current of Bi-2212/Ag tapes strongly depends on the maximum processing temperature. Initial J(c)'s of the tapes, which are partially melted, then slowly solidified at optimum conditions and finally post-annealed in an inert atmosphere, are up to 10.4 x 10(3) A/cm(2). It is found that the maximum processing temperature at initial partial melting has an influence on the optimum re-heat treatment conditions for the tapes. Re-melted tapes processed at optimum conditions recover superconducting properties after post-annealing in an inert atmosphere: the J(c) values of the tapes are about 80-110% of initial J(c)'s of those tapes.

Stefan problems for melting nanoscaled particles

Under certain conditions, the mathematical models governing the melting of nano-sized particles predict unphysical results, which suggests these models are incomplete. This thesis studies the addition of different physical effects to these models, using analytic and numerical techniques to obtain realistic and meaningful results. In particular, the mathematical "blow-up" of solutions to ill-posed Stefan problems is examined, and the regularisation of this blow-up via kinetic undercooling. Other effects such as surface tension, density change and size-dependent latent heat of fusion are also analysed.

Hydrazine-hydrate intercalated halloysite under controlled-rate thermal analysis conditions

The thermal behaviour of halloysite fully expanded with hydrazine-hydrate has been investigated in nitrogen atmosphere under dynamic heating and at a constant, pre-set decomposition rate of 0.15 mg min-1. Under controlled-rate thermal analysis (CRTA) conditions it was possible to resolve the closely overlapping decomposition stages and to distinguish between adsorbed and bonded reagent. Three types of bonded reagent could be identified. The loosely bonded reagent amounting to 0.20 mol hydrazine-hydrate per mol inner surface hydroxyl is connected to the internal and external surfaces of the expanded mineral and is present as a space filler between the sheets of the delaminated mineral. The strongly bonded (intercalated) hydrazine-hydrate is connected to the kaolinite inner surface OH groups by the formation of hydrogen bonds. Based on the thermoanalytical results two different types of bonded reagent could be distinguished in the complex. Type 1 reagent (approx. 0.06 mol hydrazine-hydrate/mol inner surface OH) is liberated between 77 and 103°C. Type 2 reagent is lost between 103 and 227°C, corresponding to a quantity of 0.36 mol hydrazine/mol inner surface OH. When heating the complex to 77°C under CRTA conditions a new reflection appears in the XRD pattern with a d-value of 9.6 Å, in addition to the 10.2 Ĺ reflection. This new reflection disappears in contact with moist air and the complex re-expands to the original d-value of 10.2 Å in a few h. The appearance of the 9.6 Å reflection is interpreted as the expansion of kaolinite with hydrazine alone, while the 10.2 Å one is due to expansion with hydrazine-hydrate. FTIR (DRIFT) spectroscopic results showed that the treated mineral after intercalation/deintercalation and heat treatment to 300°C is slightly more ordered than the original (untreated) clay.

Effect of surface conditions on flow of a micropolar fluid driven by a porous stretching sheet

-