Fresh water and acid sensitivity of authigenic clays in sandstone reservoirs

Authigenic illite-smectite and chlorite in reservoir sandstones from several Pacific rim sedimentary basins in Australia and New Zealand have been examined using an Electroscan Environmental Scanning Electron Microscope (ESEM) before, during, and after treatment with fresh water and HCl, respectively. These dynamic experiments are possible in the ESEM because, unlike conventional SEMs that require a high vacuum in the sample chamber (10-6 torr), the ESEM will operate at high pressures up to 20 torr. This means that materials and processes can be examined at high magnifications in their natural states, wet or dry, and over a range of temperatures (-20 to 1000 degrees C) and pressures. Sandstones containing the illite-smectite (60-70% illite interlayers) were flushed with fresh water for periods of up to 12 hours. Close examination of the same illite-smectite lines or filled pores, both before and after freshwater treatments, showed that the morphology of the illite-smectite was not changed by prolonged freshwater treatment. Chlorite-bearing sandstones (Fe-rich chlorite) were reacted with 1M to 10M HCl at temperatures of up to 80 degrees C and for periods of up to 48 hours. Before treatment the chlorites showed typically platy morphologies. After HCl treatment the chlorite grains were coated with an amorphous gel composed of Ca, Cl, and possibly amorphous Si, as determined by EDS analyses on the freshly treated rock surface. Brief washing in water removed this surface coating and revealed apparently unchanged chlorite showing no signs of dissolution or acid attack. However, although the chlorite showed no morphological changes, elemental analysis only detected silicon and oxygen.

High-resolution imaging of ordered mixed-layer clays

HRTEM has been used to examine illite/smectite from the Mancos shale, rectorite from Garland County, Arkansas; illite from Silver Hill, Montana; Na-smectite from Crook County, Wyoming; corrensite from Packwood, Washington; and diagenetic chlorite from the Tuscaloosa formation. Thin specimens were prepared by ion milling, ultra-microtome sectioning and/or grain dispersal on a porous carbon substrate. Some smectite-bearing clays were also examined after intercalation with dodecylamine hydrochloride (DH). Intercalation of smectite with DH proved to be a reliable method of HRTEM imaging of expanded smectite, d(001) 16 A which could then be distinguished from unexpanded illite, d(001) 10 A. Lattice fringes of basal spacings of DH-intercalated rectorite and illite/smectite showed 26 A periodicity. These data support XRD studies which suggest that these samples are ordered, interstratified varieties of illite and smectite. The ion-thinned, unexpanded corrensite sample showed discrete crystallites containing 10 A and 14 A basal spacings corresponding with collapsed smectite and chlorite, respectively. Regions containing disordered layers of chlorite and smectite were also noted. Crystallites containing regular alternations of smectite and chlorite were not common. These HRTEM observations of corrensite did not corroborate XRD data. Particle sizes parallel to the c axis ranged widely for each sample studied, and many particles showed basal dimensions equivalent to > five layers. -J.M.H.

Microanalysis of clays at low temperature

Accurate thin-film energy dispersive spectroscopic (EDS) analyses of clays with low-atomic-number (low Z) elements (e.g. Na, Al, Si), presents a challenge to the microscopist not only because of the spatial resolution required, but also because of their susceptibility to electron beam-induced radiation damange and very low X-ray count rates. Most common clays, such as kaolinite, smectite and illite occur as submicrometer crystallites with varying degrees of structural disorder in at least two directions and may have dimensions as small as one or two unit cells along the basal direction. Thus, even clays with relatively large a-b dimenstions (e.g., 100 x 100 nm) may be <5nm in the c-axis direction. For typical conditions in an analytical electron microscope (AEM), this sample thickness gives rise to very poor count rates (<200cps) and necessitates long counting times (>300s) in order to obtain satisfactory statistical precision. Unfortunately, beam damage rates for the common clays are very rapid (<10s in imaging mode) between 100kV and 200kV. With a focussed probe for elemental analyses, the damage rate is exacerbated by a high current density and may result in loss of low-Z elements during data collection and consequent loss of analytical accuracy.

Synthesis, characterisation and application of organic surfactants modified clays for water purification

This thesis offered a step forward in the development of cheap and effective materials for water treatment. It described the modification of naturally abundant clay minerals with organic molecules, and used the modified clays as effective adsorbents for the removal of recalcitrant organic water pollutants. The outcome of the study greatly extended our understanding of the synthesis and characteristic properties of clay and modified clay minerals, provided optimistic evaluation of the modified clays for environmental remediation and offered potential utility for clay minerals in the industry and environment.