Thermal treatment of natural goethite : thermal transformation and physical properties

XRD (X-ray diffraction), XRF (X-ray fluorescence), TG (thermogravimetry), FT-IES (Fourier transform infrared emission spectroscopy), FESEM (field emission scanning electron microscope), TEM (transmission electron microscope) and nitrogen–adsorption–desorption analysis were used to characterize the composition and thermal evolution of the structure of natural goethite. The in situ FT-IES demonstrated the start temperature (250 °C) of the transformation of natural goethite to hematite and the thermodynamic stability of protohematite between 250 and 600 °C. The heated products showed a topotactic relationship to the original mineral based on SEM analysis. Finally, the nitrogen–adsorption–desorption isotherm provided the variation of surface area and pore size distribution as a function of temperature. The surface area displayed a remarkable increase up to 350 °C, and then decreased above this temperature. The significant increase in surface area was attributed to the formation of regularly arranged slit-shaped micropores running parallel to elongated direction of hematite microcrystal. The main pore size varied from 0.99 nm to 3.5 nm when heating temperature increases from 300 to 400 °C. The hematite derived from heating goethite possesses high surface area and favors the possible application of hematite as an adsorbent as well as catalyst carrier.

Removal of phosphorus using NZVI derived from reducing natural goethite

Nano zero valent iron (NZVI) prepared by reducing natural goethite in hydrogen at 550 °C was used to remove phosphate. The effect of particle size, reaction time, NZVI dose, pH, initial phosphorus concentration, and oxygen amount in reaction system on phosphorus removal was investigated. The characterization of X-ray fluorescence (XRF), X-ray diffraction (XRD), N2 adsorption and desorption (BET analysis), transmission electron microscope (TEM), field emission scanning electron microscope with a energy dispersive X-ray detector (FESEM/EDS) and X-ray photoelectron spectroscopy (XPS) indicated that nanoscale of iron (around 80–150 nm length and 5–30 nm width) was prepared successfully with high dispersion and relative large surface area around 22 m2/g. The results of batch experiments and XPS analysis suggested that this kind of NZVI had a good performance on removal of phosphate (over 99%) despite in slightly acidic media as the initial concentration of P was 5 mg/L. The reason was ascribed to the effective corrosion of this NZVI under the function of proton and dissolved oxygen in spite of the existence of thin passive films.

A new approach to prepare ZVI and its application in removal of Cr(VI) from aqueous solution

Zero valent iron (ZVI) was prepared by reducing natural goethite (NG-ZVI) and synthetic goethite (SG-ZVI) in hydrogen at 550 °C. XRD, TEM, FESEM/EDS and specific surface area (SSA) and pore analyser were used to characterize goethites and reduced goethites. Both NG-ZVI and SG-ZVI with a size of nanoscale to several hundreds of nanometers were obtained by reducing goethites at 550 °C. The reductive capacity of the ZVIs was assessed by removal of Cr(VI) at ambient temperature in comparison with that of commercial iron powder (CIP). The effect of contact time, initial concentration and reaction temperature on Cr(VI) removal was investigated. Furthermore, the uptake mechanism was discussed according to isotherms, thermodynamic analysis and the results of XPS. The results showed that SG-ZVI had the best reductive capacity to Cr(VI) and reduced Cr(VI) to Cr(III). The results suggest that hydrogen reduction is a good approach to prepare ZVI and this type of ZVI is potentially useful in remediating heavy metals as a material of permeable reaction barrier.

Development of new gas sensors based on oxidized galinstan

For the first time, we have fabricated and tested conductometric sensors based on oxidized liquid galinstan towards NO2 and NH3 gases at low operating temperatures. Galinstan based films on silicon substrates have been studied with two different loadings. Surface morphology of the films was investigated by means of field emission scanning electron microscopy (FESEM). The sensor with higher galinstan loading showed a better sensitivity, which can be attributed to a higher surface area, as confirmed by SEM. At 100°C, a detection limit as low as 1 and 20 ppm was measured for NO2 and NH3, respectively.