Sinteractive anodic powders improve densification and electrochemical properties of BaZr0.8Y0.2O3-δ electrolyte films for anode-supported solid oxide fuel cells

The difficult sintering of BaZr0.8Y0.2O 3-δ (BZY20) powders makes the fabrication of anode-supported BZY20 electrolyte films complex. Dense BZY20 membranes were successfully fabricated on anode substrates made of sinteractive NiO-BZY20 powders, prepared by a combustion method. With respect to traditional anode substrates made of powders prepared by mechanical mixing, the anode substrates made of the wet-chemically synthesized composite NiO-BZY20 powders significantly promoted the densification of BZY20 membranes: dense BZY20 films were obtained after co-pressing and co-firing at 1300 °C, a much lower temperature than those usually needed for densifying BZY20 membranes. Improved electrochemical performance was also observed: the supported BZY20 films maintained a high proton conductivity, up to 5.4 × 10-3 S cm-1 at 700 °C. Moreover, an anode-supported fuel cell with a 30 m thick BZY20 electrolyte film fabricated at 1400 °C on the anode made of the wet-chemically synthesized NiO-BZY20 powder showed a peak power density of 172 mW cm-2 at 700 °C, using La0.6Sr0.4Co 0.2Fe0.8O3-δ-BaZr0.7Y 0.2Pr0.1O3-δ as the cathode material, with a remarkable performance for proton-conducting solid oxide fuel cell (SOFC) applications.

Hydrolysis and dispersion properties of aqueous Y2Si 2O7 suspensions

The dispersion of aqueous γ-Y2Si2O7 suspensions, which contain only one component but have a complex ion environment, was studied by the introduction of two different polymer dispersants, polyethylenimine (PEI) and polyacrylic acid (PAA). The suspension without any dispersant remains stable in the pH range of 9-11.5 because of electrostatic repulsion, while it is flocculated upon stirring due to the readsorption of hydrolyzed ions on the colloid surface. However, suspensions with 1 dwb% PEI exhibit greater stability in the pH range of 4-11.5. The addition of PEI shifts the isoelectric point (IEP) of the suspensions from pH 5.8 to 10.8. Near the IEP (pHIEP=10.8), the stability of the suspensions with PEI is dominated by the steric effect. When the pH is decreased to acid direction, the stabilization mechanism is changed from steric hindrance to an electrosteric effect little by little. PAA also has the effect of reducing the hydrolysis speed via a "buffer effect" in the basic pH range, but the lack of adsorption between the highly ionized anionic polymer molecules and the negative colloid particle surfaces shows no positive effect on hydrolysis of colloids and on the stabilization of Y2Si 2O7 suspensions.