Sulfated fibrous ZrO2/Al2O3 core and shell nanocomposites : a novel strong acid catalyst with hierarchically macro-mesoporous nanostructure

A series of solid strong acid catalysts were synthesised from fibrous ZrO2/Al2O3 core and shell nanocomposites. In this series, the zirconium molar percentage was varied from 2 % to 50 %. The ZrO2/Al2O3 nanocomposites and their solid strong acid counterparts were characterised by a variety of techniques including 27Al magic angle spinning nuclear magnetic resonance (MAS-NMR), scanned electronic microscopy (SEM), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), Nitrogen adsorption and infrared emission spectroscopy (IES). NMR results show that the interaction between zirconia species and alumina strongly correlates with pentacoordinated aluminium sites. This can also be detected by the change in binding energy of the 3d electrons of the zirconium. The acidity of the obtained solid acids was tested by using them as catalysts for the benzolyation of toluene. It was found that a sample with a 50 % zirconium molar percentage possessed the highest surface acidity equalling that of pristine sulfated zirconia despite the reduced mass of zirconia.

The influence of architecture on degradation and tissue ingrowth into three-dimensional poly(lactic-co-glycolic acid) scaffolds in vitro and in vivo

The in vitro and in vivo degradation properties of poly(lactic-co-glycolic acid) (PLGA) scaffolds produced by two different technologies - thermally induced phase separation (TIPS), and solvent casting and particulate leaching (SCPL) were compared. Over 6 weeks, in vitro degradation produced changes in SCPL scaffold dimension, mass, internal architecture and mechanical properties. TIPS scaffolds produced far less changes in these parameters providing significant advantages over SCPL. In vivo results were based on a microsurgically created arteriovenous (AV) loop sandwiched between two TIPS scaffolds placed in a polycarbonate chamber under rat groin skin. Histologically, a predominant foreign body giant cell response and reduced vascularity was evident in tissue ingrowth between 2 and 8 weeks in TIPS scaffolds. Tissue death occurred at 8 weeks in the smallest pores. Morphometric comparison of TIPS and SCPL scaffolds indicated slightly better tissue ingrowth but greater loss of scaffold structure in SCPL scaffolds. Although advantageous in vitro, large surface area:volume ratios and varying pore sizes in PLGA TIPS scaffolds mean that effective in vivo (AV loop) utilization will only be achieved if the foreign body response can be significantly reduced so as to allow successful vascularisation, and hence sustained tissue growth, in pores less than 300 μm. © 2005 Elsevier Ltd. All rights reserved.

4-(4-Aminophenylsulfonyl)aniline-3,5-dinitrobenzoic acid (1/1)

In the title co-crystalline adduct of the drug Dapsone with 3,5-dinitrobenzoic acid, C~12~H~12~N~2~O~2~S . C~7~H~4~N~4~O~6~, the dihedral angle between the two aromatic rings of the Dapsone molecule is 75.4(2)deg. and those between these rings and that of the 3,5-dinitrobenzoic acid are 64.5(2) and 68.4(2)deg. A strong inter-species carboxylic acid O-H---N(amine) hydrogen-bond is found, which together with intermolecular amine N-H...O hydrogen-bonding associations with carboxyl, nitro and sulfone O-atom acceptors as well as weak pi-pi interactions between one of the Dapsone phenyl rings and the 3,5-dinitrobenzoic acid ring [minimum ring centroid separation 3.774(2)Ang.], give a two-dimensional network structure.