Equilibrium studies of ammonium exchange with Australian natural zeolites

This paper is concerned with the study of the equilibrium exchange of ammonium ions with two natural zeolite samples sourced in Australia from Castle Mountain Zeolites and Zeolite Australia. A range of sorption models including Langmuir Vageler, Competitive Langmuir, Freundlich, Temkin, Dubinin Astakhov and Brouers–Sotolongo were applied in order to gain an insight as to the exchange process. In contrast to most previous studies, non-linear regression was used in all instances to determine the best fit of the experimental data. Castle Mountain natural zeolite was found to exhibit higher ammonium capacity than Zeolite Australia material when in the freshly received state, and this behavior was related to the greater amount of sodium ions present relative to calcium ions on the zeolite exchange sites. The zeolite capacity for ammonium ions was also found to be dependent on the solution normality, with 35–60% increase inuptake noted when increasing the ammonium concentration from 250 to 1000 mg/L. The optimal fit ofthe equilibrium data was achieved by the Freundlich expression as confirmed by use of Akaikes Information Criteria. It was emphasized that the bottle-point method chosen influenced the isotherm profile in several ways, and could lead to misleading interpretation of experiments, especially if the constant zeolite mass approach was followed. Pre-treatment of natural zeolite with acid and subsequently sodium hydroxide promoted the uptake of ammonium species by at least 90%. This paper highlighted the factors which should be taken into account when investigating ammonium ion exchange with natural zeolites.

Surface-mediated selective photocatalytic aerobic oxidation reactions on TiO2 nanofibres

N-doped TiO2 nanofibres were observed to possess lower aerobic oxidation activity than undoped TiO2 nanofibres in the selective photocatalytic aerobic oxidation of enzylamine and 4-methoxybenzyl alcohol. This was attributed to the reduction free energy of O2 adsorption in the vicinity of nitrogen dopant sites, as indicated by density functional theory (DFT) calculations when three-coordinated oxygen atoms are substituted by nitrogen atoms. It was found that the activity recovered following a controlled calcination of the N-doped NFs in air. The dependence of the conversion of benzylamine and 4-methoxybenzyl alcohol on the intensity of light irradiation confirmed that these reactions were driven by light. Action spectra showed that the two oxidation reactions are responsive to light from the UV region through to the visible light irradiation range. The extended light absorption wavelength range in these systems compared to pure TiO2 materials was found to result from the formation of surface complex species following adsorption of reactants onto the catalysts' surface, evidenced by the in situ IR experiment. Both catalytic and in situ IR results reveal that benzaldehyde is the intermediate in the aerobic oxidation of benzylamine to N-benzylidenebenzylamine process.

Heterojunctions between amorphous and crystalline niobium oxide with enhanced photoactivity for selective aerobic oxidation of benzylamine to imine under visible light

The formation of heterojunctions between two crystals with different band gap structures, acting as a tunnel for the unidirectional transfer of photo-generated charges, is an efficient strategy to enhance photocatalytic performance in semiconductor photocatalysts. The heterojunctions may also promote the photoactivity in the visible-light-response of any surface complex catalysts by influencing the transfer of photo-generated electrons. Herein, Nb2O5 microfibers, with a high surface area of interfaces between an amorphous phase and crystalline phase, were designed and synthesised by the calcination of hydrogen-form niobate while controlling the crystallization The photoactivity of these microfibers towards selective aerobic oxidation reactions was investigated. As predicted, the Nb2O5 microfibres containing heterojunctions exhibited the highest photoactivity. This could be due to the band gap difference between the amorphous phase and the crystalline phase, which shortened the charge mobile distance and improved the efficiency.

Cyclic-oxidation behavior of Ti3SiC2-base material at 1100°c

The cyclic-oxidation behavior of Ti3SiC2-base material was studied at 1100°C in air. Scale spallation and weight loss were not observed in the present tests and the weight gain would just continue if the experiments were not interrupted. The present results demonstrated that the scale growth on Ti3SiC2-base material obeyed a parabolic rate law up to 20 cycles. It then changed to a linear rate with further increasing cycles. The scales formed on the Ti3SiC2base material were composed of an inward-growing, fine-grain mixture of Ti022 + SiO2 and an outward-growing, coarse-grain TiO2. Theoretical calculations show that the mismatch in thermal expansion coefficients between the inner scale and Ti3SiC2-base matrix is small. The outer TiO2 layer was under very low compressive stress, while the inner TiO2 + SiO2 layer was under tensile stress during cooling. Scale spaliation is, therefore, not expected and the scale formed on Ti3SiC2-base material is adherent and resistant to cyclic oxidation.