Cyclic-oxidation behavior of Ti3SiC2-base material at 1100°c

The cyclic-oxidation behavior of Ti3SiC2-base material was studied at 1100°C in air. Scale spallation and weight loss were not observed in the present tests and the weight gain would just continue if the experiments were not interrupted. The present results demonstrated that the scale growth on Ti3SiC2-base material obeyed a parabolic rate law up to 20 cycles. It then changed to a linear rate with further increasing cycles. The scales formed on the Ti3SiC2base material were composed of an inward-growing, fine-grain mixture of Ti022 + SiO2 and an outward-growing, coarse-grain TiO2. Theoretical calculations show that the mismatch in thermal expansion coefficients between the inner scale and Ti3SiC2-base matrix is small. The outer TiO2 layer was under very low compressive stress, while the inner TiO2 + SiO2 layer was under tensile stress during cooling. Scale spaliation is, therefore, not expected and the scale formed on Ti3SiC2-base material is adherent and resistant to cyclic oxidation.

Ageing and learning in Australia: Arguing an evidence base for informed and equitable policy

Given Australia’s population ageing and predicted impacts related to health, productivity, equity and enhancing quality of life outcomes for senior Australians, lifelong learning has been identified as a pathway for addressing the risks associated with an ageing population. To date Australian governments have paid little attention to addressing these needs and thus, there is an urgent need for policy development for lifelong learning as a national priority. The purpose of this article is to explore the current lifelong learning context in Australia and to propose a set of factors that are most likely to impact learning in later years.