Implications of precursor chemistry on the alkaline hydrothermal synthesis of titania/titanate nanostructures

A systematic study of four parameters within the alkaline hydrothermal treatment of three commercial titania powders—anatase, rutile, and Degussa P25—was made. These powders were treated with 5, 7.5, 9, and 10 M NaOH between 100 and 220 °C for 20 h. The effects of alkaline concentration, hydrothermal temperature, and precursor phase and crystallite size on the resultant nanostructure formation have been studied through X-ray diffraction, Raman spectroscopy, transmission electron microscopy, and nitrogen adsorption. Through the correlation of these data, morphological phase diagrams were constructed for each commercial powder. Interpretation of the resultant morphological phase diagrams indicates that alkaline concentration and hydrothermal temperature affect nanostructure formation independently, where nanoribbon formation is significantly influenced by temperature for initial formation. The phase and crystallite size of the precursor also significantly influenced nanostructure formation, with rutile displaying a slower rate of precursor consumption compared with anatase. Small crystallite titania precursors formed nanostructures at reduced hydrothermal temperatures.

Synthesis and characterization of sodalite–polyimide nanocomposite membranes

Nanocomposite membranes are fabricated from sodalite nanocrystals (Sod-N) dispersed in BTDA-MDA polyimide matrices and then characterized structurally and for gas separation. No voids are found upon investigation of the interfacial contact between the inorganic and organic phases, even at a Sod-N loading of up to 35 wt.%. This is due to the functionalization of the zeolite nanocrystals with amino groups (==Si_(CH3)(CH2)3NH2), which covalently link the particles to the polyimide chains in the matrices. The addition of Sod-N increases the hydrogen-gas permeability of the membranes, while nitrogen permeability decreases. Overall, these nanocomposite membranes display substantial selectivity improvements. The sodalite–polyimide membrane containing 35 wt.% Sod-N has a hydrogen permeability of 8.0 Barrers and a H2/N2 ideal selectivity of 281 at 25 C whereas the plain polyimide membrane exhibits a hydrogen permeability of 7.0 Barrers and a H2/N2 ideal selectivity of 198 at the same testing temperature.

A Theoretical and Analytical Synthesis of Autopoiesis and Sociolinguistics for the Study of Organisational Communication

The purpose of this paper is threefold. First, we propose a systemic view of communication based in autopoiesis, the theory of living systems formulated by Maturana & Varela (1980, 1987). Second, we show the links between the underpinning assumptions of autopoiesis and the sociolinguistic approaches of Halliday (1978), Fairclough (1989, 1992, 1995) and Lemke (1995, 1994). Third, we propose a theoretical and analytical synthesis of autopoiesis and sociolinguistics for the study of organisational communication. In proposing a systemic theory for organisational communication, we argue that traditional approaches to communication, information, and the role of language in human organisations have, to date, been placed in teleological constraints because of an inverted focus on organisational purpose-the generally perceived role of an organisation within society-that obscure, rather than clarify, the role of language within human organisations. We argue that human social systems are, according to the criteria defined by Maturana and Varela, third-order, non-organismic living systems constituted in language. We further propose that sociolinguistics provides an appropriate analytical tool which is both compatible and penetrating in synthesis with the systemic framework provided by an autopoietic understanding of social organisation.

Image synthesis based on a model of human vision

Modern computer graphics systems are able to construct renderings of such high quality that viewers are deceived into regarding the images as coming from a photographic source. Large amounts of computing resources are expended in this rendering process, using complex mathematical models of lighting and shading. However, psychophysical experiments have revealed that viewers only regard certain informative regions within a presented image. Furthermore, it has been shown that these visually important regions contain low-level visual feature differences that attract the attention of the viewer. This thesis will present a new approach to image synthesis that exploits these experimental findings by modulating the spatial quality of image regions by their visual importance. Efficiency gains are therefore reaped, without sacrificing much of the perceived quality of the image. Two tasks must be undertaken to achieve this goal. Firstly, the design of an appropriate region-based model of visual importance, and secondly, the modification of progressive rendering techniques to effect an importance-based rendering approach. A rule-based fuzzy logic model is presented that computes, using spatial feature differences, the relative visual importance of regions in an image. This model improves upon previous work by incorporating threshold effects induced by global feature difference distributions and by using texture concentration measures. A modified approach to progressive ray-tracing is also presented. This new approach uses the visual importance model to guide the progressive refinement of an image. In addition, this concept of visual importance has been incorporated into supersampling, texture mapping and computer animation techniques. Experimental results are presented, illustrating the efficiency gains reaped from using this method of progressive rendering. This visual importance-based rendering approach is expected to have applications in the entertainment industry, where image fidelity may be sacrificed for efficiency purposes, as long as the overall visual impression of the scene is maintained. Different aspects of the approach should find many other applications in image compression, image retrieval, progressive data transmission and active robotic vision.

Azo-linked corner porphyrin systems: synthesis, crystal structures and spectroscopic investigation

1,2-Bis[10,15-di(3,5-di-tert-butyl)phenylporphyrinatonickel(II)-5-yl]diazene was synthesised via copper catalysed coupling of aminated nickel(II) 5,10-diarylporphyrin (“corner porphyrin”) and its X-ray crystal structure was determined. Two different crystals yielded different structures, one with the free meso positions in a trans-like orientation, and the other with a cis-like disposition. The free meso positions of the obtained dimer have been further functionalised while the synthesis of a zinc analogue has so far been unsuccessful. The X-ray crystal structure of the dinitro derivative of the dinickel(II) azoporphyrin was determined, and the structure showed a cis-like disposition of the nitro groups.

Synthesis and modifications of metal oxide nanostructures and their applications

Transition metal oxides are functional materials that have advanced applications in many areas, because of their diverse properties (optical, electrical, magnetic, etc.), hardness, thermal stability and chemical resistance. Novel applications of the nanostructures of these oxides are attracting significant interest as new synthesis methods are developed and new structures are reported. Hydrothermal synthesis is an effective process to prepare various delicate structures of metal oxides on the scales from a few to tens of nanometres, specifically, the highly dispersed intermediate structures which are hardly obtained through pyro-synthesis. In this thesis, a range of new metal oxide (stable and metastable titanate, niobate) nanostructures, namely nanotubes and nanofibres, were synthesised via a hydrothermal process. Further structure modifications were conducted and potential applications in catalysis, photocatalysis, adsorption and construction of ceramic membrane were studied. The morphology evolution during the hydrothermal reaction between Nb2O5 particles and concentrated NaOH was monitored. The study demonstrates that by optimising the reaction parameters (temperature, amount of reactants), one can obtain a variety of nanostructured solids, from intermediate phases niobate bars and fibres to the stable phase cubes. Trititanate (Na2Ti3O7) nanofibres and nanotubes were obtained by the hydrothermal reaction between TiO2 powders or a titanium compound (e.g. TiOSO4·xH2O) and concentrated NaOH solution by controlling the reaction temperature and NaOH concentration. The trititanate possesses a layered structure, and the Na ions that exist between the negative charged titanate layers are exchangeable with other metal ions or H+ ions. The ion-exchange has crucial influence on the phase transition of the exchanged products. The exchange of the sodium ions in the titanate with H+ ions yields protonated titanate (H-titanate) and subsequent phase transformation of the H-titanate enable various TiO2 structures with retained morphology. H-titanate, either nanofibres or tubes, can be converted to pure TiO2(B), pure anatase, mixed TiO2(B) and anatase phases by controlled calcination and by a two-step process of acid-treatment and subsequent calcination. While the controlled calcination of the sodium titanate yield new titanate structures (metastable titanate with formula Na1.5H0.5Ti3O7, with retained fibril morphology) that can be used for removal of radioactive ions and heavy metal ions from water. The structures and morphologies of the metal oxides were characterised by advanced techniques. Titania nanofibres of mixed anatase and TiO2(B) phases, pure anatase and pure TiO2(B) were obtained by calcining H-titanate nanofibres at different temperatures between 300 and 700 °C. The fibril morphology was retained after calcination, which is suitable for transmission electron microscopy (TEM) analysis. It has been found by TEM analysis that in mixed-phase structure the interfaces between anatase and TiO2(B) phases are not random contacts between the engaged crystals of the two phases, but form from the well matched lattice planes of the two phases. For instance, (101) planes in anatase and (101) planes of TiO2(B) are similar in d spaces (~0.18 nm), and they join together to form a stable interface. The interfaces between the two phases act as an one-way valve that permit the transfer of photogenerated charge from anatase to TiO2(B). This reduces the recombination of photogenerated electrons and holes in anatase, enhancing the activity for photocatalytic oxidation. Therefore, the mixed-phase nanofibres exhibited higher photocatalytic activity for degradation of sulforhodamine B (SRB) dye under ultraviolet (UV) light than the nanofibres of either pure phase alone, or the mechanical mixtures (which have no interfaces) of the two pure phase nanofibres with a similar phase composition. This verifies the theory that the difference between the conduction band edges of the two phases may result in charge transfer from one phase to the other, which results in effectively the photogenerated charge separation and thus facilitates the redox reaction involving these charges. Such an interface structure facilitates charge transfer crossing the interfaces. The knowledge acquired in this study is important not only for design of efficient TiO2 photocatalysts but also for understanding the photocatalysis process. Moreover, the fibril titania photocatalysts are of great advantage when they are separated from a liquid for reuse by filtration, sedimentation, or centrifugation, compared to nanoparticles of the same scale. The surface structure of TiO2 also plays a significant role in catalysis and photocatalysis. Four types of large surface area TiO2 nanotubes with different phase compositions (labelled as NTA, NTBA, NTMA and NTM) were synthesised from calcination and acid treatment of the H-titanate nanotubes. Using the in situ FTIR emission spectrescopy (IES), desorption and re-adsorption process of surface OH-groups on oxide surface can be trailed. In this work, the surface OH-group regeneration ability of the TiO2 nanotubes was investigated. The ability of the four samples distinctively different, having the order: NTA > NTBA > NTMA > NTM. The same order was observed for the catalytic when the samples served as photocatalysts for the decomposition of synthetic dye SRB under UV light, as the supports of gold (Au) catalysts (where gold particles were loaded by a colloid-based method) for photodecomposition of formaldehyde under visible light and for catalytic oxidation of CO at low temperatures. Therefore, the ability of TiO2 nanotubes to generate surface OH-groups is an indicator of the catalytic activity. The reason behind the correlation is that the oxygen vacancies at bridging O2- sites of TiO2 surface can generate surface OH-groups and these groups facilitate adsorption and activation of O2 molecules, which is the key step of the oxidation reactions. The structure of the oxygen vacancies at bridging O2- sites is proposed. Also a new mechanism for the photocatalytic formaldehyde decomposition with the Au-TiO2 catalysts is proposed: The visible light absorbed by the gold nanoparticles, due to surface plasmon resonance effect, induces transition of the 6sp electrons of gold to high energy levels. These energetic electrons can migrate to the conduction band of TiO2 and are seized by oxygen molecules. Meanwhile, the gold nanoparticles capture electrons from the formaldehyde molecules adsorbed on them because of gold’s high electronegativity. O2 adsorbed on the TiO2 supports surface are the major electron acceptor. The more O2 adsorbed, the higher the oxidation activity of the photocatalyst will exhibit. The last part of this thesis demonstrates two innovative applications of the titanate nanostructures. Firstly, trititanate and metastable titanate (Na1.5H0.5Ti3O7) nanofibres are used as intelligent absorbents for removal of radioactive cations and heavy metal ions, utilizing the properties of the ion exchange ability, deformable layered structure, and fibril morphology. Environmental contamination with radioactive ions and heavy metal ions can cause a serious threat to the health of a large part of the population. Treatment of the wastes is needed to produce a waste product suitable for long-term storage and disposal. The ion-exchange ability of layered titanate structure permitted adsorption of bivalence toxic cations (Sr2+, Ra2+, Pb2+) from aqueous solution. More importantly, the adsorption is irreversible, due to the deformation of the structure induced by the strong interaction between the adsorbed bivalent cations and negatively charged TiO6 octahedra, and results in permanent entrapment of the toxic bivalent cations in the fibres so that the toxic ions can be safely deposited. Compared to conventional clay and zeolite sorbents, the fibril absorbents are of great advantage as they can be readily dispersed into and separated from a liquid. Secondly, new generation membranes were constructed by using large titanate and small ã-alumina nanofibres as intermediate and top layers, respectively, on a porous alumina substrate via a spin-coating process. Compared to conventional ceramic membranes constructed by spherical particles, the ceramic membrane constructed by the fibres permits high flux because of the large porosity of their separation layers. The voids in the separation layer determine the selectivity and flux of a separation membrane. When the sizes of the voids are similar (which means a similar selectivity of the separation layer), the flux passing through the membrane increases with the volume of the voids which are filtration passages. For the ideal and simplest texture, a mesh constructed with the nanofibres 10 nm thick and having a uniform pore size of 60 nm, the porosity is greater than 73.5 %. In contrast, the porosity of the separation layer that possesses the same pore size but is constructed with metal oxide spherical particles, as in conventional ceramic membranes, is 36% or less. The membrane constructed by titanate nanofibres and a layer of randomly oriented alumina nanofibres was able to filter out 96.8% of latex spheres of 60 nm size, while maintaining a high flux rate between 600 and 900 Lm–2 h–1, more than 15 times higher than the conventional membrane reported in the most recent study.

Correctness ensuring process configuration : an approach based on partner synthesis

A configurable process model describes a family of similar process models in a given domain. Such a model can be configured to obtain a specific process model that is subsequently used to handle individual cases, for instance, to process customer orders. Process configuration is notoriously difficult as there may be all kinds of interdependencies between configuration decisions.} In fact, an incorrect configuration may lead to behavioral issues such as deadlocks and livelocks. To address this problem, we present a novel verification approach inspired by the ``operating guidelines'' used for partner synthesis. We view the configuration process as an external service, and compute a characterization of all such services which meet particular requirements using the notion of configuration guideline. As a result, we can characterize all feasible configurations (i.\,e., configurations without behavioral problems) at design time, instead of repeatedly checking each individual configuration while configuring a process model.

Elucidating the links between UV radiation and vitamin D synthesis : using an in vitro model

Ultraviolet radiation (UV) is the carcinogen that causes the most common malignancy in humans – skin cancer. However, moderate UV exposure is essential for producing vitaminDin our skin. VitaminDincreases the absorption of calcium from the diet, and adequate calcium is necessary for the building and maintenance of bones. Thus, low levels of vitamin D can cause osteomalacia and rickets and contribute to osteoporosis. Emerging evidence also suggests vitamin D may protect against falls, internal cancers, psychiatric conditions, autoimmune diseases and cardiovascular diseases. Since the dominant source of vitamin D is sunlight exposure, there is a need to understand what is a “balanced” level of sun exposure to maintain an adequate level of vitamin D but minimise the risks of eye damage, skin damage and skin cancer resulting from excessive UV exposure. There are many steps in the pathway from incoming solar UV to the eventual vitamin D status of humans (measured as 25-hydroxyvitamin D in the blood), and our knowledge about many of these steps is currently incomplete. This project begins by investigating the levels of UV available for synthesising vitamin D, and how these levels vary across seasons, latitudes and times of the day. The thesis then covers experiments conducted with an in vitro model, which was developed to study several aspects of vitamin D synthesis. Results from the model suggest the relationship between UV dose and vitamin D is not linear. This is an important input into public health messages regarding ‘safe’ UV exposure: larger doses of UV, beyond a certain limit, may not continue to produce vitamin D; however, they will increase the risk of skin cancers and eye damage. The model also showed that, when given identical doses of UV, the amount of vitamin D produced was impacted by temperature. In humans, a temperature-dependent reaction must occur in the top layers of human skin, prior to vitamin D entering the bloodstream. The hypothesis will be raised that cooler temperatures (occurring in winter and at high latitudes) may reduce vitamin D production in humans. Finally, the model has also been used to study the wavelengths of UV thought to be responsible for producing vitamin D. It appears that vitamin D production is limited to a small range of UV wavelengths, which may be narrower than previously thought. Together, these results suggest that further research is needed into the ability of humans to synthesise vitamin D from sunlight. In particular, more information is needed about the dose-response relationship in humans and to investigate the proposed impact of temperature. Having an accurate action spectrum will also be essential for measuring the available levels of vitamin D-effective UV. As this research continues, it will contribute to the scientific evidence-base needed for devising a public health message that will balance the risks of excessive UV exposure with maintaining adequate vitamin D.

Carbodiimide-mediated synthesis of poly(L-lactide)-based networks

Poly(L-lactide-co-succinic anhydride) networks were synthesised via the carbodiimide-mediated coupling of poly(L-lactide) (PLLA) star polymers. When 4-(dimethylamino)pyridine (DMAP) alone was used as the catalyst gelation did not occur. However, when 4-(dimethylamino)pyridinium p-toluenesulfonate (DPTS), the salt of DMAP and p-toluenesulfonic acid (PTSA), was the catalyst, the networks obtained had gel fractions comparable to those which were reported for networks synthesised by conventional methods. Greater gel fractions and conversion of the prepolymer terminal hydroxyl groups were observed when the hydroxyl-terminated star prepolymers reacted with succinic anhydride in a one-pot procedure than when the hydroxyl-terminated star prepolymers reacted with presynthesised succinic-terminated star prepolymers. The thermal properties of the networks, glass transition temperature (Tg), melting temperature (Tm) and crystallinity (Xc) were all strongly influenced by the average molecular weights between the crosslinks ((M_c). The network with the smallest (M_c )(1400 g/mol) was amorphous and had a Tg of 59 °C while the network with the largest (M_c ) (7800 g/mol) was 15 % crystalline and had a Tg of 56 °C.

Low temperature synthesis of zeolite N from kaolinites and montmorillonites

Zeolite N was produced from a variety of kaolinites and montmorillonites at low temperature (b100 °C) in a constantly stirred reactor using potassic and potassic+sodic mother liquors with chloride or hydroxyl anions. Reactions were complete (N95% product) in less than 20 h depending on initial batch composition and type of clay minerals. Zeolite N with 1.0bSi/Alb2.2 was produced under these conditions using KOH in the presence of KCl, NaCl, KCl+NaCl and KCl+NaOH. Zeolite N was also formed under high potassium molarities in the absence of KCl. Zeolite synthesis was more sensitive to water content and temperature when sodium was used in initial batch compositions. Syntheses of zeolite N by these methods were undertaken at bench, pilot and industrial scales.

Synthesis and thermal stability of hydrotalcites containing manganese

The hydrotalcite based upon manganese known as charmarite Mn4Al2(OH)12CO3•3H2O has been synthesised with different Mn/Al ratios from 4:1 to 2:1. Impurities of manganese oxide, rhodochrosite and bayerite at low concentrations were also produced during the synthesis. The thermal stability of charmarite was investigated using thermogravimetry. The manganese hydrotalcite decomposed in stages with mass loss steps at 211, 305 and 793°C. The product of the thermal decomposition was amorphous material mixed with manganese oxide. A comparison is made with the thermal decomposition of the Mg/Al hydrotalcite. It is concluded that the synthetic charmarite is slightly less stable than hydrotalcite.

Carbon nanotube synthesis from germanium nanoparticles on patterned substrates

Controlled synthesis of carbon nanotubes (CNTs) is highly desirable for nanoelectronic applications. To date, metallic catalyst particles have been deemed unavoidable for the nucleation and growth of any kind of CNTs. Ordered arrays of nanotubes have been obtained by controlled deposition of the metallic catalyst particles. However, the presence of metal species mixed with the CNTs represents a shortcoming for most electronic applications, as metal particles are incompatible with silicon semiconductor technology. In the present paper we report on a metal-catalyst-free synthesis of CNTs, obtained through Ge nanoparticles on a Si(001) surface patterned by nanoindentation. By using acetylene as the carbon feed gas in a low-pressure Chemical Vapor Deposition (CVD) system, multi-walled carbon nanotubes (MWNT) have been observed to arise from the smallest Ge islands. The CNTs and the Ge three-dimensional structures have been analysed by SEM, EDX and AFM in order to assess their elemental features and properties. EDX and SEM results allow confirmation of the absence of any metallic contamination on the surface, indicating that the origin of the CNT growth is due to the Ge nanocrystals.