A nanometre-scale non-periodic structural variation in high temperature superconducting ceramics and the implications for properties

Non-periodic structural variation has been found in the high Tc cuprates, YBa2Cu3O7-x and Hg0.67Pb0.33Ba2Ca2Cu 3O8+δ, by image analysis of high resolution transmission electron microscope (HRTEM) images. We use two methods for analysis of the HRTEM images. The first method is a means for measuring the bending of lattice fringes at twin planes. The second method is a low-pass filter technique which enhances information contained by diffuse-scattered electrons and reveals what appears to be an interference effect between domains of differing lattice parameter in the top and bottom of the thin foil. We believe that these methods of image analysis could be usefully applied to the many thousands of HRTEM images that have been collected by other workers in the high temperature superconductor field. This work provides direct structural evidence for phase separation in high Tc cuprates, and gives support to recent stripes models that have been proposed to explain various angle resolved photoelectron spectroscopy and nuclear magnetic resonance data. We believe that the structural variation is a response to an opening of an electronic solubility gap where holes are not uniformly distributed in the material but are confined to metallic stripes. Optimum doping may occur as a consequence of the diffuse boundaries between stripes which arise from spinodal decomposition. Theoretical ideas about the high Tc cuprates which treat the cuprates as homogeneous may need to be modified in order to take account of this type of structural variation.

YBa2Cu3O7-x films on yttria-stabilized ZrO2 substrates : influence of the substrate morphology

c-axis-oriented YBa2Cu3O7-x (YBCO) thin films were laser deposited on (001) yttria-stabilized ZrO2 (YSZ) substrates with different surface morphologies. The in-plane orientation of the films on smooth substrates was sensitive to the deposition conditions, often resulting in mixed orientations. However, a strongly dominating [110] YBCO//[110]YSZ orientation was obtained at a deposition temperature of 770°C. Films on substrates with surface steps, induced by depositing a homoepitaxial buffer layer or by thermally annealing the substrate, had a [110]YBCO//[100]YSZ orientation when deposited at the same temperature. It was concluded that the [110]YBCO//[100] YSZ orientation was promoted by a graphoepitaxial mechanism. Films prepared under identical conditions on smooth and stepped substrates grew with extended c axes on the former. It is proposed that the extension can be induced by disorder, invoked by a low oxygen pressure and a low density of adsorption sites. The disorder may be eliminated by either an increase of the oxygen pressure or an increase of the density of adsorption sites in the form of steps. The film microstructure influenced the microwave surface resistance, which was similar for films with one exclusive in-plane orientation and higher for films with mixed orientations. The films on the stepped surfaces had superior superconducting properties; inductive measurements gave a Tc onset of 88 K, a ΔT(90%-10%) c of 0.2 K, and the transport jc was 1.5×106 A/cm2 at 83 K, for films on substrates with homoepitaxial buffer layers.

Phase composition of the rapidly quenched melt of YBa2Cu3O7-y+20 mol% Y2BaCuO5

Samples of YBa2Cu3O7-y+20 mol% Y2BaCuO5, with thicknesses ranging between 50-250 μm, have been melt processed and rapidly quenched from temperatures between 985 and 1100°C by immersing them in liquid nitrogen. The phase composition and microstructures of these samples have been characterised using a combination of X-ray diffractometry, optical microscopy and scanning electron microscopy with energy dispersive X-ray spectroscopy. The quenched melt of samples quenched from temperatures greater than 985°C appears relatively homogeneous but consists of Ba2Cu3Ox (BC1.5) and BaCu2O2 (BC2) regions. At about 985°C, BaCuO2 (BC1) crystallises from the melt and most of the BC1.5 decomposes into BC1 and CuO or into BC1 and BC2. The crystallisation of BC1 induces segregation of elements in the melt and this is very significant for the melt texturing of YBCO.

YBa2Cu3O7/NdGaO3/YBa 2Cu3O7 trilayers by modified off-axis sputtering

High-quality epitaxial YBa2Cu3O7-δ (YBCO) thin films were achieved by a modified off-axis sputtering technique with high deposition rates (3.3 nm/min). The film quality and the deposition rate depended crucially on the target-to-substrate separation. Epitaxial YBCO/NdGaO3(NGO)/YBCO trilayers were successfully grown onto SrTiO3, Y-ZrO2, and LaAlO3 substrates by dc and rf sputtering. The epitaxial relations were found to be [001] YBCO//[001]NGO, [100]YBCO, or [010] YBCO//[110]NGO and [001]YBCO//[110] NGO, [100]YBCO, or [010]YBCO//[001] NGO, where the latter orientation relationship was dominating. Subsequent top YBCO layers grew c axis oriented independently of the two epitaxial orientations of the NGO. The orientation relationships between YBCO and NGO were the same. Auger electron depth profiles and transmission electron microscopy indicated that the interdiffusion at the interface between the YBCO and NGO layers was not strong even at 740°C. The superconducting transition temperatures of the top and bottom YBCO layers were about the same as that of YBCO single layers, i.e., 87-90 K. Scanning electron microscopy of the surface morphologies of the YBCO and the NGO showed that a smaller substrate-target distance resulted in smoother films.