BaZr0.8Y0.2O3--NiO composite anodic powders for proton-conducting SOFCs prepared by a combustion method

BaZr0.8Y0.2O3- (BZY)-NiO composite powders with different BZY-NiO weight ratios were prepared by a combustion method as anodes for proton-conducting solid oxide fuel cells (SOFCs). After heating to 1100C for 6 h, the composite powders were made of a well-dispersed mixture of two phases, BZY and NiO. Chemical stability tests showed that the BZY-NiO anodic powders had good stability against CO2, whereas comparative tests under the same conditions showed degradation for BaCe0.7Zr 0.1Y0.2O3--NiO, which is at present the most used anode material for proton-conducting SOFCs. Area specific resistance (ASR) measurements for BZY-NiO anodes showed that their electrochemical performance depended on the BZY-NiO weight ratio. The best performance was obtained for the anode containing 50 wt BZY and 50 wt NiO, which showed the smallest ASR values in the whole testing temperature range (0.37 cm2 at 600C). The 50 wt BZY and 50 wt NiO anode prepared by combustion also showed superior performance than that of the BZY-NiO anode conventionally made by a mechanical mixing route, as well as that of Pt.

Sinteractivity, proton conductivity and chemical stability of BaZr 0.7In0.3O3-δ for solid oxide fuel cells (SOFCs)

In3+ was used as dopant for BaZrO3 proton conductor and 30 at%-doped BaZrO3 samples (BaZr0.7In 0.3O3-δ, BZI) were prepared as electrolyte materials for proton-conducting solid oxide fuel cells (SOFCs). The BZI material showed a much improved sinteractivity compared with the conventional Y-doped BaZrO 3. The BZI pellets reached almost full density after sintering at 1600 °C for 10 h, whereas the Y-doped BaZrO3 samples still remained porous under the same sintering conditions. The conductivity measurements indicated that BZI pellets showed smaller bulk but improved grain boundary proton conductivity, when compared with Y-doped BaZrO3 samples. A total proton conductivity of 1.7 × 10-3 S cm -1 was obtained for the BZI sample at 700 °C in wet 10% H 2 atmosphere. The BZI electrolyte material also showed adequate chemical stability against CO2 and H2O, which is promising for application in fuel cells.

Trade wars in the TRIPS Council: Intellectual property, technology transfer, and climate change

This Chapter considers the geopolitical conflicts in respect of intellectual property, trade, and climate change in the TRIPS Agreement 1994 under the World Trade Organization (WTO). In particular, it focuses upon debates in the TRIPS Council on the topic of patent law and clean energy in 2013 and 2014. The chapter highlights the development agenda of a number of developing countries who are keen for access to clean energy to combat climate change and global warming. It also considers the mixed contributions of members of the BRICS/ BASIC group – including Brazil, India, China, and South Africa. This chapter highlights the intellectual property maximalist position of a number of developed countries on intellectual property, climate change, and trade. Seeking to overcome this conflict and stalemate, this Chapter puts forward both procedural and substantial reform options in respect of intellectual property, trade, and climate change in the TRIPS Council and the WTO. It also flags that the TRIPS Agreement 1994 could well be displaced by the rise of mega-regional trade agreements – such as the Trans-Pacific Partnership (TPP), and the Trans-Atlantic Trade and Investment Partnership (TTIP).