Raman spectra of the uranyl titanate mineral holfertite CaxU2-xTi(O8-xOH4x)•3H2O were analysed and related to the mineral structure. Observed bands are attributed to the TiO and (UO2)2+ stretching and bending vibrations, U-OH bending vibrations, H2O stretching, bending. The mineral holfertite is metamict as is evidenced by order/disorder of the mineral. Unexpectedly the Raman spectrum of holfertite does not show any metamictization. The intensity of the UO stretching and bending modes show normal intensity and the bands are sharp.
Resumo:
The mineral dussertite, a hydroxy-arsenate mineral of formula BaFe3+3(AsO4)2(OH)5, has been studied by Raman complimented with infrared spectroscopy. The spectra of three minerals from different origins were investigated and proved quite similar, although some minor differences were observed. In the Raman spectra of Czech dussertite, four bands are observed in the 800 to 950 cm-1 region. The bands are assigned as follows: the band at 902 cm-1 is assigned to the (AsO4)3- ν3 antisymmetric stretching mode, at 870 cm-1 to the (AsO4)3- ν1 symmetric stretching mode, and both at 859 cm-1 and 825 cm-1 to the As-OM2+/3+ stretching modes/and or hydroxyls bending modes. Raman bands at 372 and 409 cm-1 are attributed to the ν2 (AsO4)3- bending mode and the two bands at 429 and 474 cm-1 are assigned to the ν4 (AsO4)3- bending mode. An intense band at 3446 cm-1 in the infrared spectrum and a complex set of bands centred upon 3453 cm-1 in the Raman spectrum are attributed to the stretching vibrations of the hydrogen bonded (OH)- units and/or water units in the mineral structure. The broad infrared band at 3223 cm-1 is assigned to the vibrations of hydrogen bonded water molecules. Raman spectroscopy identified Raman bands attributable to (AsO4)3- and (AsO3OH)2- units.
Resumo:
The mineral thorikosite Pb3(OH)(SbO3,AsO3)Cl2 is named after the ancient city of Thorikos, in the region of Attica, where the ancient mine sites dating back to the bronze ages are found. Raman spectra of the antimonate bearing mineral thorikosite Pb3(OH)(SbO3,AsO3)Cl2 were studied, and related to the structure of the mineral. Two intense Raman peaks are observed at 596 and 730 cm-1 and are assigned to the Sb3+O3 and As3+O3 stretching vibrations. A peak at 1085 cm-1 is assigned to the Sb3+OH deformation mode. Raman band at 325 cm-1 is assigned to an OAsO bending vibration of the As3+O3 units and the bands at 269 and 275 cm-1 are attributed to the OSbO bending modes of the Sb3+O3 units. The intense Raman bands at 112 and 133 cm-1 are associated with PbCl stretching modes. Minerals such as nealite and thorikosite are minerals of archaeological significance. Yet no spectroscopic studies of these minerals have been undertaken.
Resumo:
The mineral nealite Pb4Fe2+(AsO3)2Cl4•2H2O is of archaeological significance as it is man made mineral formed through the dumping of mine wastes in the sea. The mineral has been studied by Raman spectroscopy. Raman spectroscopy identifies intense Raman bands at 708 and 732 cm-1 assigned to AsO33- stretching vibrations. In addition low intensity bands are observed at 604 and 632 cm-1 which are attributed to As2O42- symmetric and antisymmetric stretching modes. Low intensity Raman band is observed at 831 cm-1 and is assigned to the AsO44- stretching vibration. Intense Raman bands at 149 and 183 cm-1 are attributed to M-Cl stretching vibrations. Raman spectroscopy identifies arsenic anions in different oxidation states in the mineral. The molecular structure of the mineral nealite, as indicated by Raman spectroscopy, is more complex than has been reported by previous studies.
Raman spectroscopic study of a hydroxy-arsenate mineral containing bismuth-atelestite Bi2O(OH)(AsO4)
Resumo:
The Raman spectrum of atelestite Bi2O(OH)(AsO4), a hydroxy-arsenate mineral containing bismuth, has been studied in terms of spectra-structure relations. The studied spectrum is compared with the Raman spectrum of atelestite downloaded from the RRUFF database. The sharp intense band at 834 cm-1 is assigned to the 1 AsO43- (A1) symmetric stretching mode and the three bands at 767, 782 and 802 cm-1 to the 3 AsO43- antisymmetric stretching modes. The bands at 310, 324, 353, 370, 395, 450, 480 and 623 cm-1 are assigned to the corresponding ν4 and ν2 bending modes and Bi-O-Bi (vibration of bridging oxygen) and Bi-O (vibration of non-bridging oxygen) stretching vibrations. Lattice modes are observed at 172, 199 and 218 cm-1. A broad low intensity band at 3095 cm-1 is attributed to the hydrogen bonded OH units in the atelestite structure. A weak band at 1082 cm-1 is assigned to (Bi-OH) vibration.
Resumo:
Raman spectroscopy has been used to study the molecular structure of the vanadate mineral pascoite. Pascoite, rauvite and huemulite are examples of simple salts involving the decavanadate anion (V10O28)6-. Decavanadate consists of four distinct VO6 units which are reflected in Raman bands occurring at higher wavenumbers. The Raman spectrum of pascoite is characterised by two intense bands at 991 and 965 cm-1. Raman bands are observed at 991, 965, 958 and 905 cm-1 and originate from four distinct VO6 sites in the mineral structure. In the infrared spectra of pascoite, two wavenumber regions are observed between: 1) 837 and 860, and 2) between 803 and 833 cm-1. These bands are assigned to ν3 antisymmetric stretching modes of (V10O28)6- or (V5O14)3- units. The spectrum is highly complex in the lower wavenumber region, and therefore the assignment of bands is difficult. Bands observed in the 404 to 458 cm-1 region are assigned to the ν2 bending modes of (V10O28)6- or (V5O14)3- units. Raman bands observed in the 530 to 620 cm-1 region are assigned to the ν4 bending modes of (V10O28)6- or (V5O14)3- units. The Raman spectra of the vanadates in the low wavenumber region are complex with multiple overlapping bands which are probably due to VO subunits and MO bonds.
Resumo:
Hydrotalcites have been synthesised using three different pH solutions to assess the effect of pH on the uptake of arsenate and vanadate. The ability of these hydrotalcites to remove vanadate and arsenate from solution has been determined by ICP-OES. Raman spectroscopy is used to monitor changes in the anionic species for hydrotalcites synthesised at different pH values. The results show a reduction in the concentration of arsenate and vanadate anions that are removed in extremely alkaline solutions. Hydrotalcites containing arsenate and vanadate are stable in solutions up to pH 10. Exposure of these hydrotalcites to higher pH values results in the removal of large percentages of arsenate and vanadate from the hydrotalcite interlayer.
Resumo:
Raman spectra of the uranyl titanate mineral brannerite were analysed and related to the mineral structure. A comparison is made with the Raman spectra of uranyl oxyhydroxide hydrates. Observed bands are attributed to the TiO and (UO2)2+ stretching and bending vibrations, U-OH bending vibrations, H2O and (OH)- stretching, bending and libration modes. U-O bond lengths in uranyls and O-H…O bond lengths are calculated from the wavenumbers assigned to the stretching vibrations. Raman bands of brannerite are in harmony with those of the uranyl oxyhydroxides. The mineral brannerite is metamict as is evidenced by the intensity of the UO stretching and bending modes being of lower intensity than expected and with bands that are significantly broader.
Resumo:
Raman spectra of the uranyl titanate mineral euxenite were analyzed and related to the mineral structure. A comparison is made with the Raman spectra of uranyl oxyhydroxide hydrates. The obsd. bands are attributed to the Ti[n.63743]O and (UO2)2+ stretching and bending vibrations, as well as lattice vibrations of rare-earth ions. The Raman bands of euxenite are in harmony with those of the uranyl oxyhydroxides. The mineral euxenite is metamict as is evidenced by the intensity of the U[n.63743]O stretching and bending modes, which are of lower intensity than expected, and with bands that are significantly broader.
Resumo:
We have successfully synthesized hydrotalcites (HTs) contg. calcium, which are naturally occurring minerals. Insight into the unique structure of HTs has been obtained using a combination of X-ray diffraction (XRD) as well as IR and Raman spectroscopies. Calcium-contg. hydrotalcites (Ca-HTs) of the formula Ca4Al2(CO3)(OH)12·4H2O (2:1 Ca-HT) to Ca8Al2(CO3)(OH)20· 4H2O (4:1 Ca-HT) have been successfully synthesized and characterised by XRD and Raman spectroscopy. XRD has shown that 3:1 calcium HTs have the largest interlayer distance. Raman spectroscopy complemented with selected IR data has been used to characterize the synthesized Ca-HTs. The Raman bands obsd. at around 1086 and 1077 cm-1 were attributed to the ν1 sym. stretching modes of the (CO32-) units of calcite and carbonate intercalated into the HT interlayer. The corresponding ν3 CO32- antisym. stretching modes are found at around 1410 and 1475 cm-1.
Resumo:
Thermogravimetry combined with evolved gas mass spectrometry has been used to ascertain the stability of the soil minerals destinezite and diadochite. These two minerals are identical except for their morphology. Diadochite is amorphous whereas destinezite is crystalline. Both minerals are found in soils. It is important to understand the stability of these minerals because soils are subject to bush fires especially in Australia. The thermal analysis patterns of the two minerals are similar but not identical. Subtle differences are observed in the DTG patterns. For destinezite, two DTG peaks are observed at 129 and 182°C attributed to the loss of hydration water, whereas only a broad peak with maximum at 84°C is observed for diadochite. Higher temperature mass losses at 685°C for destinezite and 655°C for diadochite, based upon the ion current curves, are due to sulphate decomposition. This research has shown that at low temperatures the minerals are stable but at high temperatures, as might be experienced in a bush fire, the minerals decompose.
Resumo:
The Raman spectrum of bukovskýite, Fe3+2(OH)(SO4)(AsO4)•7H2O has been studied and compared with the Raman spectrum of an amorphous gel containing specifically Fe, As and S elements and is understood as an intermediate product in the formation of bukovskýite. Observed bands are assigned to the stretching and bending vibrations of (SO4)2- and (AsO4)3- units, stretching and bending vibrations and librational modes of hydrogen bonded water molecules, stretching and bending vibrations of hydrogen bonded (OH)- ions and Fe3+-(O,OH) units. Approximate range of O-H...O hydrogen bond lengths is inferred from the Raman spectra. Raman spectra of crystalline bukovskýite and of the amorphous gel differ in that the bukovskýite spectrum is more complex, observed bands are sharp, the degenerate bands of (SO4)2- and (AsO4)3- are split and more intense. Lower wavenumbers of H2O bending vibration in the spectrum of the amorphous gel may indicate the presence of weaker hydrogen bonds compared with those in bukovskýite.
Resumo:
The results of pressure-tuning Raman spectroscopic, X-ray powder diffraction and solid-state 13C-NMR studies of selected dicarboxylate anions intercalated in a Mg-Al layered double hydroxide (talcite) lattice are reported. The pressure dependences of the vibrational modes are linear for pressures up to 4.6 GPa indicating that no phase transitions occur. The interlayer spacings show that the oxalate, malonate and succinate dianions are oriented perpendicular to the layers, but the glutarate and adipate are tilted. The solid-state 13C-NMR spectra of these materials show full chemical shift anisotropy and, therefore, the anions are not mobile at room temperature.