Pull-through failure tests of thin steel roof battens under wind uplift load

Thin profiled steel roof sheeting and battens are increasingly used in the construction of roofing systems of residential, commercial, industrial and farm buildings in Australia. The critical load combination of external wind suction and internal wind pressures that occur during high wind events such as thunderstorms and tropical cylcones often dislocate the roofing systems partially or even completely due to premature roof connection failures. Past wind damage investigations have shown that roof sheeting failures occured at their screw connections to battens. In most of these cases, the screw fastener head pulled through the thin roof sheeting whilst the screw fasteners also pulled out from the battens. Research studis undertaken on the roof sheeting to batten connection failures have improved this situation. However, the batten to rafter or truss connections have not been investigated adequately. Failure of these connections can cause the failure of the entire roof structure as observed during the recent high wind events. Therefore a detailed experimental study consisting of both small scale and full scale tests has been undertaken to investigate the steel roof batten pull-through failures in relation to many critical parameters such as steel batten geometry, thickness and grade, screw fastener head sizes and screw tightening. This paper presents the details of this experimental study and the pull-through failure load results obtained from them. Finally it discusses the development of suitable design rules that can be used to determine the pull-through connection capacities of thin steel roof battens under wind uplift loads.

Field performance of in-service cast iron water reticulation pipe buried in reactive clay

Field monitoring is an important means for understanding soil behaviour and its interaction with buried structures such as pipeline. This paper details the successful instrumentation of a section of an in-service cast iron water main buried in an area of reactive clay where frequent water pipe breakage has been observed. The instrumentation included measurement of pipe strain; pipe water pressure and temperature; soil pressure, temperature, moisture content and matric suction, as well as the meteorological conditions on site. The data generally indicated that changes in soil temperature, suction and moisture content were directly related to the local climatic variations. The suction and moisture content data indicated that the soil profile at the site down to around 700 mm, and probably down to 1000 mm, is affected by changes in surface weather, while soil conditions below this depth appear to be more stable. Analysis of pipe strain indicated that the pipe behaves like a cantilever beam, with the top experiencing predominantly tensile strains during summer. Subsequently, these trends reduce to compressive strains as soil swelling occurs due to increase of moisture content with the onset of winter.

Numerical modeling of thin steel roof battens under wind uplift loads

Extreme wind events such as tropical cyclones, tornadoes and storms are more likely to impact the Australian coastal regions due to possible climate changes. Such events can be extremely destructive to building structures, in particular, low-rise buildings with lightweight roofing systems that are commonly made of thin steel roofing sheets and battens. Large wind uplift loads that act on the roofs during high wind events often cause premature roof connection failures. Recent wind damage investigations have shown that roof failures have mostly occurred at the batten to rafter or truss screw connections. In most of these cases, the screw fastener heads pulled through the bottom flanges of thin steel roof battens. This roof connection failure is very critical as both roofing sheets and battens will be lost during the high wind events. Hence, a research study was conducted to investigate this critical pull-through failure using both experimental and numerical methods. This paper presents the details of numerical modeling and the results.

Effects of layer orientation of CFRP strengthened steel hollow members

This paper reveals the effects of layer orientation on structural behaviour of three layers configured (LHL, HHL, LLH) CFRP strengthened circular hollow section (CHS) members subjected to bending. The beams were loaded to failure under four-point bending. The structural behaviour of the CFRP strengthened tubular steel beams with various layer orientations were presented in terms of failure load, stiffness, composite beam action and modes of failure. The LHL and LLH layers oriented strengthened beams perform slightly better than HHL layers oriented strengthened beams. The LHL and LLH layers oriented treated beams showed very similar structural behaviour.

Comparative durability study of CFRP strengthened tubular steel members under cold weather

In strengthening systems, the CFRP (Carbon Fibre Reinforced Polymer) materials typically have excellent resistance against environmental conditions; however, the performance of adhesives between CFRP and steel is generally affected by various environmental conditions such as marine environment, cold and hot weather. This paper presents the comparative durability study of CFRP strengthened tubular steel structures by using two different adhesives such as MBrace saturant and Araldite K630 under four-point bending. The program consisted of testing twelve CFRP strengthened specimens having treated with epoxy based adhesion promoter, untreated surface and one unstrengthened specimen and conditioned under cold weather for 3 and 6 months to determine the environmental durability. The beams were then loaded to failure in quasi-static manner under four-point bending. The structural responses of CFRP strengthened tubular steel beams were compared in terms of failure load, stiffness and modes of failure. The research findings show that the cold weather immersion had adversely affected the durability of CFRP strengthened steel members. Design factor is also proposed to address the short-terms durability performance under cold weather.

Characteristics and alteration origins of matrix minerals in volcaniclastic kimberlite of the Muskox pipe (Nunavut, Canada)

The matrix of volcaniclastic kimberlite (VK) from the Muskox pipe (Northern Slave Province, Nunavut, Canada) is interpreted to represent an overprint of an original clastic matrix. Muskox VK is subdivided into three different matrix mineral assemblages that reflect differences in the proportions of original primary matrix constituents, temperature of formation and nature of the altering fluids. Using whole rock X-ray fluorescence (XRF), whole rock X-ray diffraction (XRD), microprobe analyses, back-scatter electron (BSE) imaging, petrography and core logging, we find that most matrix minerals (serpentine, phlogopite, chlorite, saponite, monticellite, Fe-Ti oxides and calcite) lack either primary igneous or primary clastic textures. The mineralogy and textures are most consistent with formation through alteration overprinting of an original clastic matrix that form by retrograde reactions as the deposit cools, or, in the case of calcite, by precipitation from Ca-bearing fluids into a secondary porosity. The first mineral assemblage consists largely of serpentine, phlogopite, calcite, Fe-Ti oxides and monticellite and occurs in VK with relatively fresh framework clasts. Alteration reactions, driven by deuteric fluids derived from the juvenile constituents, promote the crystallisation of minerals that indicate relatively high temperatures of formation (> 400 °C). Lower-temperature minerals are not present because permeability was occluded before the deposit cooled to low temperatures, thus shielding the facies from further interaction with fluids. The other two matrix mineral assemblages consist largely of serpentine, phlogopite, calcite, +/- diopside, and +/- chlorite. They form in VK that contains more country rock, which may have caused the deposit to be cooler upon emplacement. Most framework components are completely altered, suggesting that larger volumes of fluids drove the alteration reactions. These fluids were likely of meteoric provenance and became heated by the volcaniclastic debris when they percolated into the VK infill. Most alteration reactions ceased at temperatures > 200 °C, as indicated by the absence or paucity of lower-temperature phases in most samples, such as saponite. Recognition that Muskox VK contains an original clastic matrix is a necessary first step for evaluating the textural configuration, which is important for reconstructing the physical processes responsible for the formation of the deposit.

Difficulties in distinguishing coherent from fragmental kimberlite: A case study of the Muskox pipe (Northern Slave Province, Nunavut, Canada)

Kimberlite drill core from the Muskox pipe (Northern Slave Province, Nunavut, Canada) highlights the difficulties in distinguishing coherent from fragmental kimberlite and assessing the volcanological implications of the apparent gradational contact between the two facies. Using field log data, petrography, and several methods to quantify crystal and xenolith sizes and abundances, the pipe is divided into two main facies, dark-coloured massive kimberlite (DMK) and light-coloured fragmental kimberlite (LFK). DMK is massive and homogeneous, containing country-rock lithic clasts (~ 10%) and olivine macrocrysts (~ 15%) set in a dark, typically well crystallised, interstitial medium containing abundant microphenocrysts of olivine (~ 15%), opaques and locally monticellite, all of which are enclosed by mostly serpentine. In general, LFK is also massive and structureless, containing ~ 20% country-rock lithic clasts and ~ 12% olivine macrocrysts. These framework components are supported in a matrix of serpentinized olivine microphenocrysts (10%), microlites of clinopyroxene, and phlogopite, all of which are enclosed by serpentine. The contact between DMK and LFK facies is rarely sharp, and more commonly is gradational (from 5 cm to ~ 10 m). The contact divides the pipe roughly in half and is sub-vertical with an irregular shape, locally placing DMK facies both above and below the fragmental rocks. Most features of DMK are consistent with a fragmental origin, particularly the crystal- and xenolith-rich nature (~ 55-65%), but there are some similarities with rocks described as coherent kimberlite in the literature. We discuss possible origins of gradational contacts and consider the significance for understanding the origin of the DMK facies, with an emphasis on the complications of alteration overprinting of primary textures.

Who owns Superman? The Man of Steel fights trademark law

Who is Superman’s greatest threat? Evil genius Lex Luthor? General Zod from the Phantom Zone? The doppelganger Bizarro? Super-villain Brainiac? Kryptonite? Or is it intellectual property law?

Design of steel roof and wall cladding systems for pull-out failures

When thin steel roof and wall cladding systems are subjected to wind uplift/suction forces, local pull-through or pull-out failures occur prematurely at their screwed connections. During high wind events such as stom1s and cyclones, these localized failures then lead to severe damage to buildings and their contents. In recent times, the use of thin steel battens, purlins and girts has increased considerably, which has made the pull-out failures more critical in the design of steel cladding systems. An experimental investigation was therefore carried out to study the pull-out failure using both static and cyclic tests for a range of commonly used screw fasteners and steel battens, purlins and girts. This paper presents the details ofthis experimental investigation and its results.

Full scale experiments of a steel portal frame building

While numerous full scale experimental programs have been conducted around the world over the past 50 years to investigate the behaviour of steel portal frame buildings, none have comprehensively investigated the behaviour of such buildings under wind uplift. Wind uplift loads often govern designs in the Australian environment and this became the subject of a recent research project at Queensland University of Technology (OUT). This paper describes the full scale experiments on a steel portal frame building subject to wind uplift, racking and gravity loads. The portal rafter and column members utilised hollow flange beam (HFB) sections [5-8] though the paper's findings on the theoretical and experimental building responses relate to conventional types of steel portal frame buildings.

Pull-through strength of high tensile steel cladding systems

The profiled steel roof and wall cladding systems in Australia are commonly made of very thin high tensile steels, and are crest-fixed with screw fasteners. A review of current literature and design standards indicated the need to improve the understanding of the behaviour of crest-fixed steel cladding systems under wind uplift/suction loading, in particular, the local failures. Therefore a detailed experimental study using a series of small scale tests and some two-span cladding tests was conducted to investigate the local pull-through and dimpling failures in the commonly used steel cladding systems. The applicability of the current design formulae for the pull-through strength of crest-fixed steel classing systems was investigated first. An improved design formula was then developed in terms of the thickness and ultimate tensile strenth of steel cladding material and diameter of screw head or washer. This paper presents the details of this investigation and its results. A review of current design and test methods is also included.

Structural identification of a laboratory-based steel through truss cantilevered bridge with suspended span using a layered genetic algorithm with patternsearch step (GAPS)

Structural identification (St-Id) can be considered as the process of updating a finite element (FE) model of a structural system to match the measured response of the structure. This paper presents the St-Id of a laboratory-based steel through-truss cantilevered bridge with suspended span. There are a total of 600 degrees of freedom (DOFs) in the superstructure plus additional DOFs in the substructure. The St-Id of the bridge model used the modal parameters from a preliminary modal test in the objective function of a global optimisation technique using a layered genetic algorithm with patternsearch step (GAPS). Each layer of the St-Id process involved grouping of the structural parameters into a number of updating parameters and running parallel optimisations. The number of updating parameters was increased at each layer of the process. In order to accelerate the optimisation and ensure improved diversity within the population, a patternsearch step was applied to the fittest individuals at the end of each generation of the GA. The GAPS process was able to replicate the mode shapes for the first two lateral sway modes and the first vertical bending mode to a high degree of accuracy and, to a lesser degree, the mode shape of the first lateral bending mode. The mode shape and frequency of the torsional mode did not match very well. The frequencies of the first lateral bending mode, the first longitudinal mode and the first vertical mode matched very well. The frequency of the first sway mode was lower and that of the second sway mode was higher than the true values, indicating a possible problem with the FE model. Improvements to the model and the St-Id process will be presented at the upcoming conference and compared to the results presented in this paper. These improvements will include the use of multiple FE models in a multi-layered, multi-solution, GAPS St-Id approach.

Effect of bond length on the behaviour of CFRP strengthened concrete-filled steel tubes under transverse impact

Concrete-filled steel tubular (CFST) columns have shown great potential as axial load carrying member and used widely in many mission critical infrastructures. However, attention is needed to strengthen these members where transverse impact force is expected to occur due to vehicle collisions. In this work, finite element (FE) model of carbon fibre reinforced polymer (CFRP) strengthened CFST columns are developed and the effect of CFRP bond length is investigated under transverse impact loading. Initially the numerical models have been validated by comparing impact test results from literature. The validated models are then used for detail parametric studies by varying the length of externally bonded CFRP composites. The parameters considered for this research are impact velocity, impact mass, CFRP modulus, adhesive type, and axial static loading. It has been observed that the effect of CFRP strengthening is consistent after an optimum effective bond length of CFRP wrapping. The effect of effective bond length has been studied for above parameters. The results show that, under combined axial static and transverse impact loads CFST columns can successfully prevent global buckling failure by strengthening only 34% of column length. Therefore, estimation of effective bond length is essential to utilise the CFRP composites cost effectively.

Influence of pipe length and flow rate on nano-particle deposition in laminar circular pipe flows

The Lagrangian particle tracking provides an effective method for simulating the deposition of nano- particles as well as micro-particles as it accounts for the particle inertia effect as well as the Brownian excitation. However, using the Lagrangian approach for simulating ultrafine particles has been limited due to computational cost and numerical difficulties. The aim of this paper is to study the deposition of nano-particles in cylindrical tubes under laminar condition using the Lagrangian particle tracking method. The commercial Fluent software is used to simulate the fluid flow in the pipes and to study the deposition and dispersion of nano-particles. Different particle diameters as well as different pipe lengths and flow rates are examined. The results show good agreement between the calculated deposition efficiency and different analytic correlations in the literature. Furthermore, for the nano-particles with higher diameters and when the effect of inertia has a higher importance, the calculated deposition efficiency by the Lagrangian method is less than the analytic correlations based on Eulerian method due to statistical error or the inertia effect.

Optimum position of steel outrigger system for high rise composite buildings subjected to wind loads

The responses of composite buildings under wind loads clearly become more critical as the building becomes taller, less stiff and more lightweight. When the composite building increases in height, the stiffness of the structure becomes more important factor and introduction to belt truss and outrigger system is often used to provide sufficient lateral stiffness to the structure. Most of the research works to date is limited to reinforced concrete building with outrigger system of concrete structure, simple building plan layout, single height of a building, one direction wind and single level of outrigger arrangement. There is a scarcity in research works about the effective position of outrigger level on composite buildings under lateral wind loadings when the building plan layout, height and outrigger arrangement are varied. The aim of this paper is to determine the optimum location of steel belt and outrigger systems by using different arrangement of single and double level outrigger for different size, shape and height of composite building. In this study a comprehensive finite element modelling of composite building prototypes is carried out, with three different layouts (Rectangular, Octagonal and L shaped) and for three different storey (28, 42 and 57-storey). Models are analysed for dynamic cyclonic wind loads with various combination of steel belt and outrigger bracings. It is concluded that the effectiveness of the single and double level steel belt and outrigger bracing are varied based on their positions for different size, shape and height of composite building.