Preparation of Y2Si2O7/ ZrO2 composites and their composition - Mechanical properties - Tribology relationships

In this work, novel Y2Si2O7/ZrO 2 composites were developed for structural and coating applications by taking advantage of their unique properties, such as good damage tolerance, tunable mechanical properties, and superior wear resistance. The γ-Y 2Si2O7/ZrO2 composites showed improved mechanical properties compared to the γ-Y2Si 2O7 matrix material, that is, the Young's modulus was enhanced from 155 to 188 GPa (121%) and the flexural strength from 135 to 254 MPa (181%); when the amount of ZrO2 was increased from 0 to 50 vol%, the γ-Y2Si2O7/ZrO2 composites also presented relatively high facture toughness (>1.7 MPa·m 1/2), but this exhibited an inverse relationship with the ZrO 2 content. The composition-mechanical property-tribology relationships of the Y2Si2O7/ZrO2 composites were elucidated. The wear resistance of the composites is not only influenced by the applied load, hardness, strength, toughness, and rigidity but also effectively depends on micromechanical stability properties of the microstructures. The easy growth of subcritical microcracks in Y 2Si2O7 grains and at grain boundaries significantly contributes to the macroscopic fracture toughness, but promotes the pull-out of individual grains, thus resulting in a lack of correlation between the wear rate and the macroscopic fracture toughness of the composites.

Preparation of reticulated MAX-phase support with morphology-controllable nanostructured ceria coating for gas exhaust catalyst devices

Reticulated porous Ti3AlC2 ceramic, a member of the MAX-phase family (Mn+1AXn phases, where M is an early transition metal, A is an A-group element, and X is carbon and/or nitrogen), was prepared from the highly dispersed aqueous suspension by a replica template method. Through a cathodic electrogeneration method, nanocrystalline catalytic CeO2 coatings were deposited on the conductive porous Ti 3AlC2 supports. By adjusting the pH value and cathodic deposition current, coatings exhibiting nanocellar, nanosheets-like, or bubble-free morphologies can be obtained. This work expects to introduce a novel practically feasible material system and a catalytic coating preparation technique for gas exhaust catalyst devices.

Investigating the effect of Eye Movement Desensitization and Reprocessing (EMDR) on postoperative pain intensity in adolescents undergoing surgery: A randomized controlled trial

Aim To investigate the efficacy of Eye Movement Desensitization and Reprocessing for postoperative pain management in adolescents. Background Eye Movement Desensitization and Reprocessing is an inexpensive, non-pharmacological intervention that has successfully been used to treat chronic pain. It holds promise in the treatment of acute, postsurgical pain based on its purported effects on the brain and nervous system. Design A randomized controlled trial was used. Methods Fifty-six adolescent surgical patients aged between 12-18 years were allocated to gender-balanced Eye Movement Desensitization and Reprocessing (treatment) or non-Eye Movement Desensitization and Reprocessing (control) groups. Pain was measured using the Wong-Baker FACES® Pain Rating Scale (WBFS) before and after the intervention (or non-intervention for the control group). Findings A Wilcoxon signed-rank test demonstrated that the Eye Movement Desensitization and Reprocessing group experienced a significant reduction in pain intensity after treatment intervention, whereas the control group did not. Additionally, a Mann–Whitney U-test showed that, while there was no significant difference between the two groups at time 1, there was a significant difference in pain intensity between the two groups at time 2, with the Eye Movement Desensitization and Reprocessing group experiencing lower levels of pain. Conclusion These results suggest that Eye Movement Desensitization and Reprocessing may be an effective treatment modality for postoperative pain.