Carbonation front progress in mortars containing fly ash considering the presence of chloride ions

The incorporation of fly ash (FA) in cementitious matrices have been frequently used in order to make the matrix more resistant to the action of chlorides. On the other hand, it is known that Ca (OH)2 existing in the matrix is partially consumed by the pozzolanic reactions, which facilitates the advancement of carbonation. Given that the combined action between carbonation and chloride penetration is a fact little known, we speculate about the behaviour of the matrix in this context. This study investigates the influence of the presence of chlorides on the carbonation in mortars with FA. Samples with 0% and 40% replacement of cement CEM I 42.5 R for FA were molded with water/binder 0.56 and 0.52 respectively. After 90 days of curing the specimens were subjected to cycles of immersion/drying for 56 days. Half of the samples was subjected to the following cycle: two days in a solution containing NaCl (concentration equal to 3.5 %); 12 days in the carbonation chamber (4% of CO2). The other half was: two days in water; 12 days in the carbonation chamber. Then, the development of carbonation was evaluated. The results indicate that the presence of chlorides influences the carbonation. The specimens submitted to the exclusive action of CO2 showed a greater depth of carbonation compared to that presented by the specimens subjected to combined action. This may be related to changes in properties of the matrix which may lead to further refinement of the pores and related to the presence of the salt that can lead to partial filling of the pores and the increase in moisture content.

Pulse wave velocity distribution in a cohort study: from arterial stiffness to early vascular aging

BACKGROUND: By contrast with other southern European people, north Portuguese population registers an especially high prevalence of hypertension and stroke incidence. We designed a cohort study to identify individuals presenting accelerated and premature arterial aging in the Portuguese population. METHOD: Pulse wave velocity (PWV) was measured in randomly sampled population dwellers aged 18-96 years from northern Portugal, and used as a marker of early vascular aging (EVA). Of the 3038 individuals enrolled, 2542 completed the evaluation. RESULTS: Mean PWV value for the entire population was 8.4?m/s (men: 8.6?m/s; women: 8.2?m/s; P??10?m/s). Logistic regression models indicated gender differences concerning the risk of developing large artery damage, with women having the same odds of PWV above 10?m/s 10 years later than men. CONCLUSION: The population PWV values were higher than expected in a low cardiovascular risk area (Portugal). High prevalence rates of EVA and noteworthy large artery damage in young ages were found.