Dielectric relaxation and ferromagnetic resonance in magnetoelectric (Polyvinylidene-fluoride)/ferrite composites

In this work the dielectric properties and ferromagnetic resonance of Polyvinylidene- uoride embedded with 10 wt. % of NiFe2O4 or Ni0.5Zn0.5Fe2O4 nanoparticles are presented. The mechanisms of the dielectric relaxation in these two composites do not differ from each other. For more precise characterization of the dielectric relaxation, a two dimensional distribution of relaxation times was calculated from the temperature dependencies of the complex dielectric permittivity. The results obtained from the 2D distribution and the mean relaxation time are found to be consistent. The dynamics of the dielectric permittivity is described by the Arrhenius law. The energy and attempt time of the dielectric relaxators lie in a narrow energy and time region thus proving that the single type chains of polymer are responsible for a dispersion. The magnetic properties of the composites were investigated using the fer- romagnetic resonance. A single resonance line was observed for both samples. From the temperature dependence (100 K - 310 K) of the resonance eld and linewidth, the origin of the observed line was attributed to the NiFe2O4 and Ni0.5Zn0.5Fe2O4 superparamagnetic nanoparticles. By measuring lms at dif- ferent orientations with respect to the external magnetic eld, the angular dependence of the resonance was observed, indicating the magnetic dipolar in-plane interactions.

Induced magnetoelectric effect driven by magnetization in BaFe12O19 -/P(VDF-TrFE) composites

Films of BaFe12O19/P(VDF-TrFE) composites with 5, 10 and 20 %wt Barium ferrite content have been fabricated. BaFe12O19 microparticles have the shape of thin hexagonal platelets, the easy direction of magnetization remaining along the c axis, which is perpendicular to the plates. This fact allows for ferrite particles orientation in-plane and out-of-plane within the composite films, as confirmed by measured hysteresis loops. While the in-plane induced magnetoelectric effect (ME) is practically zero, these composite films show a good out-of-plane magnetoelectric effect. with maximum ME coupling coefficient changes of 3, 17 and 2 mV/cm.Oe for the 5, 10 and 20%wt Barium ferrite content films, respectively. We infer that this ME behavior appears as driven by the magnetization process arising when we applied the external magnetic field. We have also measured linear and reversible magnetoelectric effect for low applied bias field, when magnetization process is still reversible.