Electrochromic devices incorporating biohybrid electrolytes doped with a lithium salt, an ionic liquid or a mixture of both

The sol-gel method was employed in the synthesis of di-urethane cross-linked poly( caprolactone) (PCL(530)/siloxane biohybrid ormolytes incorporating either a mixture of lithium triflate (LiCF3SO3) and the ionic liquid (IL) 1-ethyl-3-methyl imidazolium tetrafluoroborate ([Emim]BF4), or solely with [Emim]BF4 or LiCF3SO3. The ormolyte doped with [Emim]BF4 is thermally more stable and exhibits higher ionic conductivity (4 x 10-4 and 2 x 10-3 S cm-1 at 36 and 98 ºC, respectively) than those containing the LiCF3SO3/[Emim]BF4 mixture or just LiCF3SO3. The three ormolytes were employed in the production of glass/ITO/ormolyte/WO3/ITO/glass electrochromic devices (ECDs) designated as ECD@Y with Y = Li-[Emim]BF4, [Emim]BF4 and Li. The three ECDs displayed fast switching speed (ca. 30 s). ECD@Li-[Emim]BF4 exhibited an electrochromic contrast of 18.4 % and an optical density change of 0.11 in the visible region, the coloration efficiency attained at 555 nm was 159 and 80.2 cm-2 C-1 in the “on” and “off” states, respectively, and the open circuit memory was 48 hours. In the “on” state the CIE 1931 color space coordinates were x = 0.29 and y = 0.30, corresponding to blue color.

Polymer electrolyte based on DNA and N,N,N-trimethyl-N-(2-hydroxyethyl)ammonium bis(trifluoromethylsulfonyl)imide

Combining ionic liquids (ILs) with polymers offers the prospect of new applications, where they surpass the performance of conventional media, such as organic solvents, giving advantages in terms of improved safety and a higher operating temperature range. In this work we have investigated the morphology, thermal and electrochemical properties of polymer electrolytes prepared through the addition of con- trolled quantities of the cholinium based IL N,N,N-trimethyl-N-(2-hydroxyethyl)ammonium bis(trifluo- romethylsulfonyl)imide ([N1 1 1 2(OH)] [NTf2]) to a deoxyribonucleic acid (DNA) host network. These novel IL-based electrolytes have been analyzed aiming at applications in electrochemical devices. An optimized sample showed good thermal stability up to 155 °C and a wide electrochemical window of ~3.5 V. The highest conductivity was registered for the DNA[N1 1 1 2(OH)][NTf2] (1:1) (2.82 × 10-5 and 1.09 × 10-3 S cm-1 at 30 and 100 °C, respectively).