Durability indicators comparison for SCC and CC in tropical coastal environments

Self-compacting concrete (SCC) demands more studies of durability at higher temperatures when subjected to more aggressive environments in comparison to the conventional vibrated concrete (CC). This work aims at presenting results of durability indicators of SCC and CC, having the same water/binder relations and constituents. The applied methodologies were electrical resistivity, diffusion of chloride ions and accelerated carbonation experiments, among others, such as microstructure study, scanning electron microscope and microtomography experiments. The tests were performed in a research laboratory and at a construction site of the Pernambuco Arena. The obtained results shows that the SCC presents an average electrical resistivity 11.4% higher than CC; the average chloride ions diffusion was 63.3% of the CC; the average accelerated carbonation penetration was 45.8% of the CC; and the average open porosity was 55.6% of the CC. As the results demonstrated, the SCC can be more durable than CC, which contributes to elucidate the aspects related to its durability and consequent prolonged life cycle.

Dynamic wet etching of silicon through isopropanol alcohol evaporation

In this paper, Isopropanol (IPA) availability during the anisotropic etching of silicon in Potassium Hydroxide (KOH) solutions was investigated. Squares of 8 to 40 m were patterned to (100) oriented silicon wafers through DWL (Direct Writing Laser) photolithography. The wet etching process was performed inside an open HDPE (High Density Polyethylene) flask with ultrasonic agitation. IPA volume and evaporation was studied in a dynamic etching process, and subsequent influence on the silicon etching was inspected. For the tested conditions, evaporation rates for water vapor and IPA were determined as approximately 0.0417 mL/min and 0.175 mL/min, respectively. Results demonstrate that IPA availability, and not concentration, plays an important role in the definition of the final structure. Transversal SEM (Scanning Electron Microscopy) analysis demonstrates a correlation between microloading effects (as a consequence of structure spacing) and the angle formed towards the (100) plane.