Energy harvesting performance of BaTiO3/poly(vinylidene fluoride-trifluoroethylene) spin coated nanocomposites

The energy harvesting efficiency of poly(vinylidene fluoride-trifluoroethylene) spin coated films and its nanocomposites with piezoelectric BaTiO3 have been investigated as a function of ceramic filler size and content. It is found that the best energy harvesting performance of ~0.28 W is obtained for the nanocomposite samples with 20% filler content of 10 nm size particles and for 5% filler content for the 100 and 500 nm size fillers. For the larger filler average sizes, the power decreases for filler contents above 5% due to increase of the mechanical stiffness of the samples. Due to the similar dielectric characteristics of the samples, the performance is mainly governed by the mechanical response. The obtained power values, easy processing and the low cost and robustness of the polymer, allow the implementation of the material for micro and nanogenerator applications.

A review of squeaking in ceramic total hip prostheses

The occurrence of audible squeaking in some patients with ceramic-on-ceramic (CoC) hip prostheses is a cause for concern. Considering multifactor contributing to this phenomenon, many studies have been conducted over the last decade. Great efforts have been put on understanding the mechanics of the hip squeaking to gain a deep insight into factors resulting in sound emission from hip articulation. Disruption of fluid-film lubrication and friction were reported as main potential causes of hip squeaking, while patient and surgical factors as well as design and material of hip implants were identified as affecting factors. This review article therefore summarised the recent available literature on this subject to provide a platform for future developments. Moreover, high wear rates and ceramic liner fracture as viable consequences of hip squeaking were discussed.

Assessment of the properties to characterize the interface between clay brick substrate and strengthening mortar

The behaviour of masonry elements under in-plane and out-of-plane loads can be improved through the application of strengthening systems based on reinforcing overlays. After strengthening, the transition region between the original substrate and the strengthening layer is especially stressed, and premature failure of the strengthened masonry is reached if insufficient interfacial capacity is assured. Therefore, the assessment of the mechanical behaviour of the interface is critical to the development of the masonry strengthening system based on the application of strengthening overlays. In this research a method for the characterization of the interface behaviour between two different materials, a polypropylene fibre reinforced mortar (PFRM) and a ceramic brick used for masonry construction is presented. Direct shear tests were carried out in couplet specimens. Due to the orthotropic nature of the bricks surface, the shear load was applied along three different directions in order to perform an overall estimation of the interface behaviour. The peak and residual shear stresses, as well as the failure modes, were obtained at different levels of the normal stress. Based on these experimental results constitutive laws were assessed for the simulation of the interface mechanical behaviour based on the Mohr and Mohr-Coulomb failure criteria.

Electrochemical vs antibacterial characterization of ZrCN-Ag coatings

Nowadays, antibacterial properties are becoming a viable feature to be introduced in biomaterials due to the possibility of modifying the materials' surface used in medical devices in a micro/nano metric scale. As a result, it is mandatory to understand the mechanisms of the antimicrobial agents currently used and their possible failures. In this work, the antibacterial activity of ZrCNAg films is studied, taking into consideration the ability of silver nanoparticles to be dissolved when embedded into a ceramic matrix. The study focuses on the silver release evaluated by glow discharge optical emission spectroscopy and the effect of the fluid composition on this release. The results revealed a very low silver release of the films, leading to non-antibacterial activity of such materials. The silver release was found to be dependent on the electrolyte composition. NaCl (8.9 g L? 1) showed the lowest spontaneously silver ionization, while introducing the sulfates in Hanks' balanced salt solution (HBSS) such ionization is increased; finally, the proteins incorporated to the (HBSS) showed a reduction of the silver release, which also explains the low ionization in the culture medium (tryptic soy broth) that contains high quantities of proteins.

Spatio-temporal modelling of environmental data

Programa Doutoral em Matemática e Aplicações.