Cost efficiency and resistance to chemical attack of a fly ash geopolymeric mortar versus epoxy resin and acrylic paint coatings

This article presents results of an experimental investigation on the resistance to chemical attack (with sulphuric, hydrochloric and nitric acid) of several materials: OPC concrete, high-performance concrete, epoxy resin, acrylic painting and a fly ash-based geopolymeric mortar). Three types of acids with three high concentrations (10, 20 and 30%) were used to simulate long-term degradation. A cost analysis was also performed. The results show that the epoxy resin has the best resistance to chemical attack independently of the acid type and the acid concentration. However, the cost analysis shows that the epoxy resin-based solution is the least cost-efficient solution being 70% above the cost efficiency of the fly ash-based geopolymeric mortar.

Monitoring the early stiffness development in epoxy adhesives for structural strengthening

The present work aimed to assess the early-age evolution of E-modulus of epoxy adhesives used for Fibre-Reinforced Polymer (FRP) strengthening applications. The study involved adapting an existing technique devised for continuous monitoring of concrete stiffness since casting, called EMM-ARM (Elasticity Modulus Measurement through Ambient Response Method) for evaluation of epoxy stiffness. Furthermore, monotonic tensile tests according to ISO standards and cyclic tensile tests were carried out at several ages. A comparison between the obtained results was performed in order to better understand the performance of the several techniques in the assessment of stiffness of epoxy resins. When compared to the other methodologies, the method for calculation of E-modulus recommended by ISO standard led to lower values, since in the considered strain interval, the adhesive had a non-linear stress–strain relationship. The EMM-ARM technique revealed its capability in clearly identifying the hardening kinetics of epoxy adhesives, measuring the material stiffness growth during the entire curing period. At very early ages the values of Young׳s modulus obtained with quasi-static tests were lower than the values collected by EMM-ARM, due to the fact that epoxy resin exhibited a significant visco-elastic behaviour.