Acellular Gellan-gum based bilayered structures for the regeneration of osteochondral defects: a preclinical study

 In orthopaedics, the management and treatment of osteochondral (OC) defects remains an ongoing clinical challenge. Autologous osteochondral mosaicplasty has been used as a valid option for OC treatments although donor site morbidity remains a source of concern [1]. Engineering a whole structure capable of mimicking different tissues (cartilage and subchondral bone) in an integrated manner could be a possible approach to regenerate OC defects. In our group we have been proposing the use of bilayered structures to regenerate osteochondral defects [2,3]. The present study aims to investigate the pre-clinical performance of bilayered hydrogels and spongy-like hydrogels in in vivo  models (mice and rabbit, respectively), in both subcutaneous and orthotopic models. The bilayered structures were produced from Low Acyl Gellan Gum (LAGG) from Sigma-Aldrich, USA. Cartilage-like layers were obtained from a 2wt% LAGG solution. The bone-like layers were made of 2wt% LAGG with incorporation of hydroxyapatite at 20% and 30% (w/v). Hydrogels and spongy-like were subcutaneouly implanted in mice to evaluate the inflammatory response. Then, OC defects were induced in rabbit knee to create a critical size defect (4 mm diameter and 5 mm depth), and then hydrogels and sponges implanted. Both structures followed different processing methods. The hydrogels were injected allowing in situ  crosslinking. Unlike, the spongy-like were pre-formed by freeze-drying. The studies concerning subcutaneous implantation and critical size OC defect were performed for 2 and 4 weeks time, respectively. Cellular behavior and inflammatory responses were assessed by means of histology staining and biochemical function and matrix deposition by immunohistochemistry. Additionally, both OC structures stability and new cartilage and bone formation were evaluated by using vivo- computed tomography (Scanco 80). The results showed no acute inflammatory response for both approaches. New tissue formation and integration in the adjacent tissues were also observed, which present different characteristic behaviors when comparing hydrogels and sponges response. As future insights, a novel strategy for regeneration of OC defects can be designed encompassing both, hydrogels and spongy-like structures and cellular approaches. References: 1. Espregueira-Mendes J. et al. Osteochondral transplantation using autografts from the upper tibio-fibular joint for the treatment of knee cartilage lesions. Knee Surgery, Sports Traumatology, Arthroscopy 20,1136, 2012. 2. Oliveira JM. et al, Novel hydroxyapatite/chitosan bilayered scaffold for osteochondral tissue-engineering applications: Scaffold design and its performance when seeded with goat bone marrow stromal cells. Biomaterials 27, 6123, 2006. 3. Pereira D R. et al. Gellan Gum-Based Hydrogel Bilayered Scaffolds for Osteochondral Tissue Engineering. Key Engineering Materials 587, 255, 2013.

Microencapsulation of ellagic acid from pomegranate husk and karaya gum by spray drying

Objective: The aim of this study was to obtain and characterize microcapsules with Ellagic Acid (EA) from pomegranate as core material and Karaya Gum (KG) as wall material. Methods: EA was obtained from dry pomegranate peel powder via methanolysis and quantified by HPLC. Microcapsules were obtained preparing a dispersion containing KG and EA in phosphate buffer pH 8. The dispersion was processed in a spray dryer under specific conditions (inlet temperature at 150 °C, feed flow at 30% and aspirator at 100 %) for obtaining of microcapsules. Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) were used for characterization. Results: Obtained material contains 98.03±2.82 mg EA/g of pomegranate peel. FTIR showed that there were changes in the molecular structure of microcapsules referred to raw materials. SEM confirmed that particles obtained had micron-size (1-5 µm). DSC analysis showed that raw materials had glass transition temperatures of 79.58 and 83.41 °C and for microcapsules the value was67.25 °C. Conclusion: Methanolysis is a viable technique for the obtaining of EA from the peel of pomegranate. KG shows good potential for be used as wall material for EA microencapsulation.

Gellan gum-Ionic liquid membranes for electrochromic device application

Biopolymer-based materials have been of particular interest and they are alternatives to synthetic polymers based on the decreasing oil resources. The polymer electrolytes were doped with choline-based IL N,N,Ntrimethyl- N-(2-hydroxyethyl)ammonium bis(trifluoromethylsulfonyl)imide ([N1 1 1 2(OH)][NTf2]), or Er (CF3SO3)3 or both. The polymer electrolytes were employed in the production of glass/ITO/WO3/electrolyte/ CeO2–TiO2/ITO/glass electrochromic devices (ECDs). The lowest onset temperature for the degradation of all the SPEs is at ~130 °C for the Gellan Er (CF3SO3)3 (10:1) this temperature range of stability is wide enough for a material to be applied as an electrolyte/separator component in electrochemical devices. The three ECDs displayed fast switching speed (ca. 15 s). Gellan [N1 1 1 2(OH)][NTf2] Er (CF3SO3)3 (5:1:10) exhibited an electrochromic contrast of 4.2% in the visible region, the coloration efficiency attained at 555 nm was 3.5 and 0.90 cm-2 C-1 in the “colored” and “bleached” states, respectively, and the open circuit memorywas 48 h. Preliminary tests performed with a prototype electrochromic device (ECD) incorporating WO3 as cathodic electrochromic layer, are extremely encouraging.

Gellan gum-coated gold nanorods: an intracellular nanosystem for bone tissue engineering

Gold nanorods (AuNRs) have emerged as an exceptional nanotool for a myriad of applications ranging from cancer therapy to tissue engineering. However, their surface modification with biocompatible and stabilizing biomaterials is crucial to allow their use in a biological environment. Herein, low-acyl gellan gum (GG) was used to coat AuNRs surface, taking advantage of its stabilizing, biocompatible and gelling features. The layer-by-layer based strategy implied the successive deposition of poly(acrylic acid), poly(allylamine hydrochloride) and GG, which allowed the formation of a GG hydrogel-like shell with 7 nm thickness around individual AuNRs. Stability studies in a wide range of pH and salt concentrations showed that the polysaccharide coating can prevent AuNRs aggregation. Moreover, a reversible pH-responsive feature of the nanoparticles was observed. Cytocompatibility and osteogenic ability of GG-coated AuNRs was also addressed. After 14 days of culturing within SaOS-2, an osteoblast-like cell line, in vitro studies revealed that AuNRs-GG exhibit no cytotoxicity, were internalized by the cells and localized inside lysosomes. AuNRs-GG combined with osteogenic media enhanced the mineralization capacity two-fold, as compared to cells exposed to osteogenic media alone. The proposed system has shown interesting features for osteogenesis, and further insights might be relevant for drug delivery, tissue engineering and regenerative medicine.

Gellan gum-hyaluronate spongy-like hydrogels promote angiogenesis in hindlimb ischemia

"Tissue engineering: part A", vol. 21, suppl. 1 (2015)