Influence of design parameters on the mechanical behavior and porosity of braided fibrous stents

In spite of all innovations in stent design, commonly used metallic stents present several problems such as corrosion, infection and restenosis, leading to health complications or even death of patients. In this context, the present paper reports a systematic investigation on designing and development of 100% fiber based stents, which can eliminate or minimize the problems with existing metallic stents. For this purpose, braided stents were produced by varying different materials, structural and process parameters such as mono-filament type and diameter, braiding angle and mandrel diameter. The influence of these design parameters on mechanical behavior as well as stent's porosity was thoroughly investigated, and suitable parameters were selected for developing a stentwith mechanical characteristics and porosity matching with the commercial stents. According to the experimental results, the best performance was achieved with a polyester stent designed with 0.27 mm monofilament diameter, braiding angle of 35° and mandrel diameter of 6 mm, providing similar properties to commercial Nitinol stents.

Antibacterial properties of fibrous stents coated with silver oxide nanocoatings

Stents are rigid and perforated tubular structures, which are inserted into blood vessels in order to prevent or inhibit the constriction of blood flow, restoring the normal blood flow, when blood vessels are clogged, being used in 70% of angioplasties. These medical devices assume great importance in the treatment of cardiovascular diseases (CVD) which are the leading cause of death worldwide. In the European Union CVD account for 40% of deaths and assume an estimated annual cost of 196 billion euros[1]. Stents must possess certain requirements, in order to, adequately, perform its function, such as biocompatibility (so that its use does not c ause damage on the health of its user), mechanical strength, radiopacity (so that it is easy to view), longitudinal flexibility, ease of handling, corrosion resistance and having high strength and high radial expansion ability to recover. Stents can be made of different materials, but metals, particularly stainless steel, are the most common. However, metallic stents present several dRawbacks such as corrosion and restenosis, leading to health complications for the patient, or even death. In order to minimize these disadvantages, new materials, like fibrous materials, have been used [2]. Monofilaments present high potential for stents development because, in addition to its biocompatibility, these materials allow the application of various surface treatments, such as antibacterial coatings. Furthermore, monofilament exhibit excellent mechanical properties, like greater stiffness and good results when subjected to compression, tensile and bending forces, since these forces will be directly supported by the monofilament [3]. To minimize the reaction of the human body and Limit the adhesion of microorganisms to the stent surface, some coatings have been developed, including the use of novel metals with antimicrobial properties, like silver. The main objective of this study was the development of fibrous stents, incorporation of silver oxide nanocoating. For the development of the stent, polyester monofilaments with 0.27mm of diameter were used in braiding technology, with a mandrel diameter of 6mm and a braiding angle of 35⁰. The mechanical behaviour of the stent were evaluated by mechanical testing under longitudinal and radial compression, bending. The results of compressive strength tests are according with value from literature: 1.13 to 2.9 N for radial compression and 0. 16-5.28N to longitudinal compression. From literature is also possible to verify that stents must present 75% of unchanged diameter during the bending test and must possess a porosity between 70% and 80% [4]. The produced polyester stent presents values of 1.29N for radial compression, 0.23N for longitudinal compression, 80% of porosity and 85.5% of unchanged diameter, during bending tests. For the antibacterial functionalization, silver oxide nanocoatings were prepared, through reactive magnetron g, with an Ag target in an Ar +O2 atmosphere. In order to evaluate the nanostructure and morphology of the coatings, d ifferent technique s like X-ray diffraction (XRD), scanning electron microscopy (SEM) and and X- ray photoelectron spectroscopy (XPS were used. From the analyses of XRD it is possible to verify that the peaks corresponds to planes of Ag2 O and MATERIAIS 2015 Porto, 21-23 June, 2015 characterize a cubic phase. The presence of Ag2 O is corroborated by XPS spectrum, where it is possible to observe silver, not only, in oxide state, but a lso in mettalic state, and it is possible to verify the presence of silver clusters, confirmed by SEM analysis. Films’ roughness and topography, parameters influencing the wettability of the surface and microorganism adhesion, were measured by Atomic Force Microscopy (AFM), and it was observed that the roughness is very low (under 10 nm). Coatings’ hydrophobicity and surface tension parameters were determined by contact angle measurement, and it was verified the hydrophobic behavior of the coatings. For antibacterial tests were used Staphylococcus epidermidis strain (IE186) and Staphylococcus aureus(ATCC 6538), and halo inhibition zone tests were realized. Ag+release rates were studied by means of inductively coupled plasma mass spectrometry (ICP -MS). The obtained results suggest that silver oxide coatings do not modify significantly surface properties of the substrate, like hydrophobicity and roughness, and present antimicrobial properties for both bacteria used.

A continuous solvent- and oil-free method to prepare injectable PEGylated fibrinogen cell-laden microparticles

Injectable biomaterials with in situ cross-linking reactions have been suggested to minimize the invasiveness associated with most implantation procedures. However, problems related with the rapid liquid-to-gel transition reaction can arise because it is difficult to predict the reliability of the reaction and its end products, as well as to mitigate cytotoxicity to the surrounding tissues. An alternative minimally invasive approach to deliver solid implants in vivo is based on injectable microparticles, which can be processed in vitro with high fidelity and reliability, while showing low cytotoxicity. Their delivery to the defect can be performed by injection through a small diameter syringe needle. We present a new methodology for the continuous, solvent- and oil-free production of photopolymerizable microparticles containing encapsulated human dermal fibroblasts. A precursor solution of cells in photo-reactive PEG-fibrinogen (PF) polymer was transported through a transparent injector exposed to light-irradiation before being atomized in a jet-in-air nozzle. Shear rheometry data provided the cross-linking kinetics of each PF/cell solution, which was then used to determine the amount of irradiation required to partially polymerize the mixture prior to atomization. The partially polymerized drops fell into a gelation bath for further polymerization. The system was capable of producing cell-laden microparticles with high cellular viability, with an average diameter of between 88.1 µm to 347.1 µm and a dispersity of between 1.1 and 2.4, depending on the parameters chosen.

Pesquisa experimental para avaliação da eficiência da fibra de aço na resistência à punção de lajes lisas reforçadas simetricamente

O presente artigo é dedicado à avaliação experimental da eficiência do reforço com fibra de aço em termos da resistência à punção de lajes lisa carregadas simetricamente. Para este fim, oito lajes de 2550 x 2550 x 150 mm3 foram ensaiadas até a ruína, onde se investigou a influência do consumo de fibras (0, 60, 75 e 90 kg/m3) e da resistência do concreto (50 e 70 MPa). Duas lajes de referência, sem fibras, uma para cada classe de resistência do concreto, e uma laje para cada consumo de fibra e para cada classe de resistência do concreto compuseram o programa experimental. Todas as lajes foram armadas à flexão com barras de aço (armadura convencional) de forma a garantir a ruína por punção das lajes de referência. O único reforço transversal foi garantido pelas fibras de aço hooked ends com comprimento e diâmetro de 37 e 0,55 mm, respectivamente, e resistência à tração de aproximadamente 1100 MPa. Os resultados revelaram que as fibras de aço são muito eficientes em converter uma ruína frágil por cisalhamento em uma ruína dúctil por flexão, aprimorando ambos, carga de ruptura e deslocamento. Neste artigo o programa experimental é abordado em detalhe e os principais resultados são apresentados e discutidos.

Magnetoelectric CoFe2O4/polyvinylidene fluoride electrospun nanofibres

Magnetoelectric 0-1 composites comprising CoFe2O4 (CFO) nanoparticles in polyvinylidene fluoride (PVDF) polymerfibre matrix have been prepared by electrospinning. The average diameter of the electrospun composite fibres D is ~ 325 nm, independently of nanoparticle content, and the amount of crystalline polar β phase is strongly enhanced when compared to pure PVDF polymer fibres. The piezoelectric response of these electroactive nanofibres is modified by an applied magnetic field, thus evidencing the magnetoelectric character of the CFO/PVDF 0-1 composites.

A high order model for piezoelectric rods: an asymptotic approach

Preprint submitted to International Journal of Solids and Structures. ISSN 0020-7683

Silver nanoparticles to fight Candida coinfection in the oral cavity

[Exert] This chapter is focused on the activity of silver nanoparticles (SN) as an antifungal agent against Candida albicans and Candida glabrata biofilms, which are involved in oral candidosis. A discussion focusing on the influence of the stabilizing agent, diameter of SN on its antibiofilm activity, influence of chemical stability of SN on Candida biofilms, the effect of SN against adhered cells and biofilms, the effect on extracellular matrix composition and structure of Candida biofilms, the combination of SN with conventional antifungal drugs, and the incorporation of SN into denture acrylic resin is incorporated in the present chapter. Because of the resistance of Candida biofilms to conventional drugs and the positive effect of SN against them, these nanoparticles can be used as an alternative antifungal agent (...).